Recent research progresses in Multi-Beam Klystron (MBK) in IECAS are briefly introduced in the letter. The S-band MBKs of IECAS have peak power of 120-250 kW, average power of 4-9 kW, efficiency of 35-45%, gain of 41-...Recent research progresses in Multi-Beam Klystron (MBK) in IECAS are briefly introduced in the letter. The S-band MBKs of IECAS have peak power of 120-250 kW, average power of 4-9 kW, efficiency of 35-45%, gain of 41-46 dB, beam voltage of 15-19 kV, and weight of 40-45 kg. Some key technical problems of MBK are also described and discussed. Among them,improving the design of MBK to obtain the required bandwidth, raising beam transmission to increase average power, eliminating oscillation and spray spectrum, overcoming window breakdown caused by magic mode, reducing breakdown times of electrongun, are most important things for the practical MBK. Besides, further research work in MBK in IECAS is commented.展开更多
Cr/SmCo/Cr films with different SmCo thickness were deposited on glass substrates by magnetron sputtering,followed by an annealing process at 550 °C for 20 min.Experimental results showed that the SmCo film of 30...Cr/SmCo/Cr films with different SmCo thickness were deposited on glass substrates by magnetron sputtering,followed by an annealing process at 550 °C for 20 min.Experimental results showed that the SmCo film of 30 nm exhibited two-phase behavior in the demagnetization process,the obvious kink was observed near zero.For the SmCo film of 50 nm,the kink was invisible,and a single phase like behavior was obtained in the demagnetization process.The reversal behavior became consistent in the thicker films.Moreover,the coercivity reduced and the saturated magnetization increased obviously with the increasing thickness.X-ray diffraction results indicated that the average grain size of SmCo 5 in the thicker films were almost 30 nm,but the quantity of SmCo 5 grains increased with the increasing thickness,which enhanced the intergrain exchange coupling（IEC） of the SmCo 5 hard phases.The increase of IEC improved the magnetic properties of SmCo films with increasing thickness.展开更多
文摘Recent research progresses in Multi-Beam Klystron (MBK) in IECAS are briefly introduced in the letter. The S-band MBKs of IECAS have peak power of 120-250 kW, average power of 4-9 kW, efficiency of 35-45%, gain of 41-46 dB, beam voltage of 15-19 kV, and weight of 40-45 kg. Some key technical problems of MBK are also described and discussed. Among them,improving the design of MBK to obtain the required bandwidth, raising beam transmission to increase average power, eliminating oscillation and spray spectrum, overcoming window breakdown caused by magic mode, reducing breakdown times of electrongun, are most important things for the practical MBK. Besides, further research work in MBK in IECAS is commented.
基金Project supported by National Natural Science Foundation of China (50871014)New Teacher Foundation of Ministry of Education(200800081030)+1 种基金Funding Project for Academic Human Resources Development in Institutions of Higher Learning Under the Jurisdiction of Beijing Municipality (PHR201007122)Beijing Natural Science Foundation (2102014)
文摘Cr/SmCo/Cr films with different SmCo thickness were deposited on glass substrates by magnetron sputtering,followed by an annealing process at 550 °C for 20 min.Experimental results showed that the SmCo film of 30 nm exhibited two-phase behavior in the demagnetization process,the obvious kink was observed near zero.For the SmCo film of 50 nm,the kink was invisible,and a single phase like behavior was obtained in the demagnetization process.The reversal behavior became consistent in the thicker films.Moreover,the coercivity reduced and the saturated magnetization increased obviously with the increasing thickness.X-ray diffraction results indicated that the average grain size of SmCo 5 in the thicker films were almost 30 nm,but the quantity of SmCo 5 grains increased with the increasing thickness,which enhanced the intergrain exchange coupling（IEC） of the SmCo 5 hard phases.The increase of IEC improved the magnetic properties of SmCo films with increasing thickness.