Study of the Characteristics of Large-Diameter Iron Bars Obtained by Rolling at the ODHAV Foundry in the Republic of Guinea

This work consists of evaluating the quality of the mechanical parameters of large-diameter steels, i.e. 20, 25, 28 and 32, through a process of recycling scrap metal that fills garages, rubbish dumps, gutters and other abandoned sites, as well as imported concrete reinforcing steel sold in the Republic of Guinea. To carry out this important work, a number of mechanical tensile and bending tests and a microscopic analysis combining two devices, an electron microscope and a photographic camera, were carried out. The samples were taken from sampling areas in the major communes of Conakry, namely: Casse Sonfonia, Matoto and Kagbélen. The tensile strength values of the large dimensions 20, 25, 28 and 32 are given in the tables.

Three-Dimensional Thermo-mechanical Coupled FEM Simulation for Hot Continuous Rolling of Large-Diameter Mandrel Bar

Based on the important boundary conditions of rolling simulation including friction, heat conduction and interactionsof the workpiece and rolls, the hot continuous rolling processes of large-diameter mandrel round bar (200 mm indiameter) in 6VH-stand hot tandem mill are successfully simulated by three-dimensional coupled thermomechanicalelastoplastic finite element method (FEM). The distributions of stress, strain, temperature and the rolling force andtorque for the two-pass and four-pass continuous rolling are calculated respectively. Thus, the two and four-passroll schedules are verified, respectively. The simulation results show that it is safe to produce 200 mm round barby the two-pass (oval pass and round pass) continuous rolling on the existing equipment compared to the four-passcontinuous rolling. There are concave surfaces and increased widths occurring at the end of rolled billet due touneven deformations between the outside and inside of the workpiece as well as the free spreading close to the rollgap of the final pass.

A NOVEL APPROACH FOR THE PREDICTION OF SURFACE PROFILE OF OUTGOING WORKPIECE AND THE CALCULATION OF MEAN ROLL RADIUS IN ALLOY BAR ROLLING

In alloy bar rolling process, the component of alloyed steel influenced the spread coefficient greatly, therefore, the component influence coefficient m of different alloyed steel has been determined firstly to calculate the maximum spread. Then the curvature radius of stress free surface and the ＂critical point on the contact boundary＂ have been solved, the surface profile of outgoing workpiece has been obtained. Furthermore, the formula of the equivalent contact section area has been proposed and the mean roll radius has been calculated. The bar rolling experiment and the rigid-plastic FEM （finite element method） simulation have been carried out to verify the novel approach. Compared with experimental data and simulation results, the novel approach can be used in setting processing parameter and design of finishing groove.

An analytical model for the prediction of cross-section profile and mean roll radius in alloy bar rolling

In a round-oval-round pass rolling sequence, the cross-section profile of an outgoing workpiece was predicted first after getting the maximum spread. The concept ＂critical point on the contact boundary＂ was proposed and the coordinates of the critical point were solved. The equivalent contact section area was represented and the mean roll radius was determined. The validity of this model was examined by alloy bar rolling experiment and rigid-plastic FEM simulation. Compared with the existing models, the mean roll radius obtained by this model is similar to experiment data.

Improvement to anti-rust property of hot rolled rebar by compact oxide scale

A method was proposed to improve the anti-rust property of hot rolled rebar, which uses oil–water emulsion cooling instead of water cooling after hot rolling. The experiments were carried out by two cooling methods, one cooled by water, the other cooled by oil–water emulsion. The results of wet/dry cyclic accelerated corrosion test showed that the anti-rust property of rebar cooled by oil–water emulsion was better than that by water obviously. The results of OM, SEM and EPMA analysis indicated that these two scales contained three layers: an outer Fe_3O_4 layer, an intermediate Fe O layer with island-shaped pro-eutectoid Fe_3O_4, an inner eutectoid Fe_3O_4 layer. For the water cooled rebar, all three layers of oxide scale were relatively thin. Moreover, the scale had plenty of defects such as porosity, and crack. However, for the oil–water emulsion cooled rebar, all three layers of oxide scale were relatively thick and compact, which played an important role in protecting the rebar from atmospheric rust.

Pulsed current-assisted twelve-roll precision rolling deformation of SUS304 ultra-thin strips with exceptional mechanical properties

Innovative pulsed current-assisted multi-pass rolling tests were conducted on a 12-roll mill during the rolling deformation processing of SUS304 ultra-thin strips.The results show that in the first rolling pass,the rolling reduction rate of a conventionally rolled sample(at room temperature)is 33.8%,which can be increased to 41.5%by pulsed current-assisted rolling,enabling the formation of an ultra-thin strip with a size of 67.3μm in only one rolling pass.After three passes of pulsed current-assisted rolling,the thickness of the ultra-thin strip can be further reduced to 51.7μm.To clearly compare the effects of a pulsed current on the microstructure and mechanical response of the ultra-thin strip,ultra-thin strips with nearly the same thickness reduction were analyzed.It was found that pulsed current can reduce the degree of work-hardening of the rolled samples by promoting dislocation detachment,reducing the density of stacking faults,inhibiting martensitic phase transformation,and shortening the total length of grain boundaries.As a result,the ductility of ultra-thin strips can be effectively restored to approximately 16.3%while maintaining a high tensile strength of 1118 MPa.Therefore,pulsed current-assisted rolling deformation shows great potential for the formation of ultra-thin strips with a combination of high strength and ductility.

Microstructure evolution and strengthening mechanism of high -performance powder metallurgy TA15 titanium alloy by hot rolling

Hot deformation of sintered billets by powder metallurgy(PM)is an effective preparation technique for titanium alloys,which is more significant for high-alloying alloys.In this study,Ti–6.5Al–2Zr–Mo–V(TA15)titanium alloy plates were prepared by cold press-ing sintering combined with high-temperature hot rolling.The microstructure and mechanical properties under different process paramet-ers were investigated.Optical microscope,electron backscatter diffraction,and others were applied to characterize the microstructure evolution and mechanical properties strengthening mechanism.The results showed that the chemical compositions were uniformly dif-fused without segregation during sintering,and the closing of the matrix craters was accelerated by increasing the sintering temperature.The block was hot rolled at 1200℃ with an 80%reduction under only two passes without annealing.The strength and elongation of the plate at 20–25℃ after solution and aging were 1247 MPa and 14.0%,respectively,which were increased by 24.5%and 40.0%,respect-ively,compared with the as-sintered alloy at 1300℃.The microstructure was significantly refined by continuous dynamic recrystalliza-tion,which was completed by the rotation and dislocation absorption of the substructure surrounded by low-angle grain boundaries.After hot rolling combined with heat treatment,the strength and plasticity of PM-TA15 were significantly improved,which resulted from the dense,uniform,and fine recrystallization structure and the synergistic effect of multiple slip systems.

FINITE ELEMENT ANALYSIS OF AXIAL FEED BAR ROLLING

A flexible technique of hot working of bars by axial feed rolling was introduced. The process deformation, strain field, stress field, and temperature fie M of the parts are analyzed by finite element method （ FEM）-simulation software DEFORM-3D. The material flow rule and tool load have been investigated.

Fluid Resonance Between Twin Floating Barges with Roll Motion Under Wave Action

The wave-induced fluid resonance between twin side-by-side rectangular barges coupled with the roll motion of the twin barges is investigated by both numerical simulation and physical model test.A 2D numerical wave flume,based on an open source computational fluid dynamics(CFD)package OpenFOAM,is applied for the numerical simulation.After numerical validations and convergent verifications,the characteristics of the fluid resonance in the gap between the twin rolling side-by-side barges are examined.The resonant frequency of the oscillating fluid in the gap between the twin rolling barges decreases compared with that between the twin fixed barges.Generally,the twin barges roll in the opposite directions,and their equilibrium positions lean oppositely with respect to the initial vertical direction.A physical model test is carried out for a further investigation,in which the twin barges are set oppositely leaning and fixed.From the present experimental results,a linear decrease of the resonant frequency with the increasing leaning angle is found.Combined with the numerical results,the deflection of the equilibrium positions of the twin barges is a relevant factor for the resonant frequency.Besides,the effects of the gap width and incident wave height on the fluid resonance coupled with roll motion are examined.

Effect of Barkhausen Detection Distance in Cold and Temper Rolled Low Carbon Steels: A Novel Approach

In this paper, a novel arrangement for magnetic Barkhausen noise detection is introduced. Measurements have been performed using two low carbon steel plates of 1 mm thickness. The measurements were conducted along the rolling and the transverse directions. The new arrangement includes a displacement of the detection coil in predetermined steps in while the magnetizing yoke is kept stationary introducing a cyclic magnetization in the rolling direction and transverse to it. In general, the intensity of the Barkhausen signals decreased as a function of coil displacement in both plates. In the temper rolled plate, Barkhausen noise profile shape changed from a single peak to a double peak one when coil has been displaced by 5 mm away in both magnetizing directions. Peaks are more apparent while magnetizing in the transverse direction. The appearance of two peaks profile in the temper rolled plate may be attributed to two stages of magnetization taking place at different times as a function of the applied field. Magnetization in the transverse direction results in a partition of the internal magnetizations into two main components perpendicular to each other. The internal components of magnetization involve the magnetic easy axes in the rolling direction and the forced magnetization in the transverse direction due to the applied field. Another assumption to interpret the findings may be due to the internal demagnetization field in the soft material below surface. The findings support this assumption in such a way that the demagnetizing field is strong enough in the transverse direction than in the rolling direction. This assumption is supported by the experiment on cold rolled plate. In the cold rolled plate, the resultant MBN profiles are composed of one peak throughout the test due to high dislocation density and hence a very weak demagnetizing field.

Tailoring the texture and mechanical properties of 3%Y_(2)O_(3)p/ZGK200 composites fabricated by unidirectional and cross rolling followed by annealing

3%Y_(2)O_(3)p/ZGK200 composites were subjected to unidirectional rolling(UR)and cross rolling(CR)at 400℃and 350℃followed by annealing at 300℃for 1 h.The microstructure,texture and mechanical properties of rolled and annealed composites were systematically studied.The rolled composites exhibited a heterogeneous microstructure,consisting of deformed grains elongated along rolling direction(RD)and Y_(2)O_(3)particles bands distributed along RD.After annealing,static recrystallization(SRX)occurred and most deformed grains transformed into equiaxed grains.A non-basal texture with two strong T-texture components was obtained after UR while a non-basal elliptical/circle texture with circle multi-peaks was obtained after CR,indicating that rolling path had great influences on texture of the composites.After annealing process,R-texture component disappeared or weakened,as results,a non-basal texture with double peaks tilting from normal direction(ND)to transverse direction(TD)and a more random non-basal texture with circle multi-peaks were obtained for UR and CR composites,respectively.The yield strength of rolled composites after UR showed obvious anisotropy along RD and TD while a low anisotropic yield strength was obtained after CR.Some Y_(2)O_(3)particles broke during rolling.The fracture of the composites was attributed to the existence of Y_(2)O_(3)clusters and interfacial debonding between particles and matrix during tension,as a result,the ductility was not as superior as matrix alloy.

Effect of annealing temperature on microstructure and mechanical properties of Mg-Zn-Zr-Nd alloy with large final rolling deformation

In this study,the Mg-3Zn-0.5Zr-χNd(χ=0,0.6)alloys were subjected to final rolling treatment with large deformation of 50%.The impact of annealing temperatures on the microstructure and mechanical properties was investigated.The rolled Mg-3Zn-0.5Zr-0.6Nd alloy exhibited an ultimate tensile strength of 386 MPa,a yield strength of 361 MPa,and an elongation of 7.1%.Annealing at different temperatures resulted in reduced strength and obviously increased elongation for both alloys.Optimal mechanical properties for the Mg-3Zn-0.5Zr-0.6Nd alloy were achieved after annealing at 200℃,with an ultimate tensile strength of 287 MPa,a yield strength of 235 MPa,and an elongation of 26.1%.The numerous deformed microstructures,twins,and precipitated phases in the rolled alloy could impede the deformation at room temperature and increase the work hardening rate.After annealing,a decrease in the work hardening effect and an increase in the dynamic recovery effect were obtained due to the formation of fine equiaxed grains,and the increased volume fraction of precipitated phases,which significantly improved the elongation of the alloy.Additionally,the addition of Nd element could enhance the annealing recrystallization rate,reduce the Schmid factor difference between basal and prismatic slip systems,facilitate multi-system slip initiation and improve the alloy plasticity.

Reshaping force for deformed casing repairing with hydraulic rolling reshaper and its influencing factors

Hydraulic rolling reshaper is an advanced reshaping tool to solve the problem of casing deformation,which has been widely used in recent years.When it is used for well repair operation,the reshaping force provided by ground devices is generally determined by experience.However,too large reshaping force may destroy the deformed casing,and too small reshaping force may also prolong the construction period and affect the repairing effect.In this paper,based on Hertz contact theory and elastic-plastic theory,combined with the process parameters of shaping,and considering the structural characteristics of the deformed casing and reshaper,we propose a mathematical model for calculating the reshaping force required for repairing deformed casing by hydraulic rolling reshaper.Meanwhile,the finite element model and numerical method of hydraulic rolling reshaper repairing deformed casing are established by using the finite element method,and the reliability of the mathematical model is verified by several examples.On this basis,the control variable method is used to investigate the influence of each parameter on the reshaping force,and the influence degree of each parameter is explored by orthogonal simulation test and Pearson correlation analysis.The research results not only provide an important theoretical basis for the prediction of reshaping force in on-site construction,but also provide a reference for the subsequent improvement of the shaping process.

Unveiling the rolling texture variations ofα-Mg phases in a dual-phase Mg-Li alloy

LZ91 Mg-Li alloy plates with three types of initial texture were rolled by 70%reduction at both room temperature and 200℃to explore the rolling texture formation ofα-Mg phase.The results showed that the rolling texture is largely affected by the initial texture.All the samples exhibited two main texture components as RD-split double peaks texture and TD-split double peaks texture after large strain rolling.The intensity of the two texture components was strongly influenced by the initial orientation and rolling temperature.Extension twinning altered the large-split non-basal orientation to a near basal one at low rolling strain.The basal orientation induced by twinning is unstable,which finally transmitted to the RD-split texture.The strong TD-split texture formed due to slip-induced orientation transition from its initial orientation.The competition between prismatic and basal slip determined the intensity and tilt angle of the TD-split texture.By increasing the rolling temperature,the TD-split texture component was enhanced in all three samples.Limitation of extension twinning behavior and the promotion of prismatic slip at elevated temperature are the main reasons for the difference in hot and cold rolling texture.

Design,preparation,microstructure and mechanical property of the lightweight radiation-shielding Mg-Ta-Al composites basing differential temperature hot rolling

A novel lightweight,radiation-shielding Mg-Ta-Al layered metal-matrix composite(LMC)was successful designed by doping the extremely refractory metal(Ta)into Mg sheets.These Mg-based LMCs sheets shows excellent radiation-dose shield effect,about 145 krad·a^(−1),which is about 17 times of traditional Mg alloy,while its surface density is only about 0.9 g·cm^(−2),reducing by 60%than that of pure Ta.The quantitate relationship between radiation-dose and the materials’thickness was also confirmed to the logistic function when the surface density is in the range of 0.6-1.5 g·cm^(−2).Meantime,the rolling parameters,interface microstructure and mechanical properties in both as-rolled and annealing treated samples were evaluated.The sheets possess a special dissimilar atoms diffusion transitional zone containing an obvious inter-diffusion Mg-Al interface and the unique micro-corrugated Ta-Al interface,as well as a thin Al film with a thickness of about 10μm.The special zone could reduce the stress concentration and enhance the strength of Mg-Ta-Al LMCs.The interface bonding strength reaches up to 54-76 MPa.The ultimate tensile strength(UTS)and yield strength(TYS)of the Mg-Ta-Al sheet were high to 413 MPa and 263 MPa,respectively,along with an elongation of 5.8%.The molecular dynamics(MD)analysis results show that the two interfaces exhibit different formation mechanism,the Mg-Al interface primarily depended on Mg/Al atoms diffusion basing point defects movement,while the Ta-Al interface with a micro-interlock pining shape formed by close-packed planes slipping during high temperature strain-induced deformation process.

Effects of cold rolling path on recrystallization behavior and mechanical properties of pure copper during annealing

The recrystallization behavior,grain boundary characteristic distribution,and mechanical properties of pure Cu sheets that were subjected to different cold rolling paths,and then annealed at 400°C for 10,30,60,and 420 min,were investigated.Different rolling paths changed the grain boundary orientations of cold-rolled copper,causing recrystallized grains to nucleate and grow in an oriented manner.However,the evolution of the texture indicated that cold-rolled copper with different rolling paths did not show an obvious preferred orientation after annealing.The RD-60 specimen exhibited the smallest grain size(6.6μm).The results indicated that the grain size and low-ΣCSL grain boundaries worked together to provide RD-60 samples with appropriate mechanical properties and high plasticity.The yield strength,ultimate tensile strength,and elongation of RD-60 sample were 81 MPa,230 MPa,and 49%,respectively.These results could provide guidance for tuning the microstructures and properties of pure Cu foils,as well as designing fabrication routes for pure Cu foils through processes such as rolling and drawing.

Multi-dimension and multi-modal rolling mill vibration prediction model based on multi-level network fusion

Mill vibration is a common problem in rolling production,which directly affects the thickness accuracy of the strip and may even lead to strip fracture accidents in serious cases.The existing vibration prediction models do not consider the features contained in the data,resulting in limited improvement of model accuracy.To address these challenges,this paper proposes a multi-dimensional multi-modal cold rolling vibration time series prediction model(MDMMVPM)based on the deep fusion of multi-level networks.In the model,the long-term and short-term modal features of multi-dimensional data are considered,and the appropriate prediction algorithms are selected for different data features.Based on the established prediction model,the effects of tension and rolling force on mill vibration are analyzed.Taking the 5th stand of a cold mill in a steel mill as the research object,the innovative model is applied to predict the mill vibration for the first time.The experimental results show that the correlation coefficient(R^(2))of the model proposed in this paper is 92.5%,and the root-mean-square error(RMSE)is 0.0011,which significantly improves the modeling accuracy compared with the existing models.The proposed model is also suitable for the hot rolling process,which provides a new method for the prediction of strip rolling vibration.

Carbon Fiber Breakage Mechanism in Aluminum(Al)/Carbon Fibers(CFs) Composite Sheet during Accumulative Roll Bonding(ARB) Process

We put forward a method of fabricating Aluminum(Al)/carbon fibers(CFs) composite sheets by the accumulative roll bonding(ARB) method. The finished Al/CFs composite sheet has CFs and pure Al sheets as sandwich and surface layers. After cross-section observation of the Al/CFs composite sheet, we found that the CFs discretely distributed within the sandwich layer. Besides, the tensile test showed that the contribution of the sandwich CFs layer to tensile strength was less than 11% compared with annealed pure Al sheet. With ex-situ observation of the CFs breakage evolution with-16%,-32%, and-45% rolling reduction during the ARB process, the plastic instability of the Al layer was found to bring shear damages to the CFs. At last, the bridging strengthening mechanism introduced by CFs was sacrificed. We provide new insight into and instruction on Al/CFs composite sheet preparation method and processing parameters.

Online task planning method of anti-ship missile based on rolling optimization

Based on the wave attack task planning method in static complex environment and the rolling optimization framework, an online task planning method in dynamic complex environment based on rolling optimization is proposed. In the process of online task planning in dynamic complex environment,online task planning is based on event triggering including target information update event, new target addition event, target failure event, weapon failure event, etc., and the methods include defense area reanalysis, parameter space update, and mission re-planning. Simulation is conducted for different events and the result shows that the index value of the attack scenario after re-planning is better than that before re-planning and according to the probability distribution of statistical simulation method, the index value distribution after re-planning is obviously in the region of high index value, and the index value gap before and after re-planning is related to the degree of posture change.

Bonding enhancement of cold rolling TA1 P-Ti/AA6061 composite plates via surface oxidation treatment

TA1 P-Ti/AA6061 composite plate was produced by oxidizing the surface of the titanium plate and adopting a cold roll bonding process.The results revealed that the oxide film(Ti6O)prepared on the surface of TA1 pure titanium was easy to crack during the cold roll bonding,thereby promoting the formation of an effective mechanical interlock at the interface,which can effectively reduce the minimum reduction rate of the composite plates produced by cold rolling of titanium and aluminium plates.Moreover,the composite plate subjected to oxidation treatment exhibited high shear strength,particularly at a 43%reduction rate,achieving a commendable value of 117 MPa.Based on oxidation treatment and different reduction rates,the annealed composite plates at temperatures of 400,450,and 500°C displayed favorable resistance to interface delamination,highlighting their remarkable strength-plasticity compatibility as evidenced by a maximum elongation of 31.845%.