The paper has studied the mechanical properties and heat treatment effects on multi-element low alloy wear-resistant steel (MLAWS) used as a material for the liner of rolling mill torii. The results show that when que...The paper has studied the mechanical properties and heat treatment effects on multi-element low alloy wear-resistant steel (MLAWS) used as a material for the liner of rolling mill torii. The results show that when quenched at 900-920℃ and tempered at 350-370℃, the MLAWS has achieved hardness above 60 HRC, tensile strength greater than 1 600 MPa, impact toughness higher than 18J/cm2 and fracture toughness greater than 37 MPa·m1/2. When the quenching temperature is lower than 900℃, the hardness of the MLAWS increases with the temperature. When the quenching temperature is higher than 900℃, the hardness decreases with the increase of temperature. At a quenching temperature below 920℃, the effect of quenching temperature on the impact toughness is not obvious. In quenching at above 920℃, impact toughness decreases as the temperature increases. When the tempering temperature is exceeding 450℃, the hardness begins to decrease significantly. Tempering at 350℃ has produced the best wear resistance on the MLAWS.展开更多
The effects of heat treatment on the properties of multi element wear-resistant low-alloy steel (MLAWS) which is used to make the liner of rolling mill torus were researched. The results show that when quenching tem...The effects of heat treatment on the properties of multi element wear-resistant low-alloy steel (MLAWS) which is used to make the liner of rolling mill torus were researched. The results show that when quenching temperature is lower than 900℃, the hardness increases with the increase of temperature, and when quenching temperature is higher than 900℃, the hardness decreases with the increase of temperature. As quenching temperature is lower than 920℃, the effect of quenching temperature on the impact toughness is not obvious. When quenching temperature is higher than 920℃ , impact toughness decreases with the increase of temperature. When tempering temperature is higher than 450 ℃ , the hardness begins to decrease obviously. After tempering at 350℃, the best wear resistance was obtained. According to the service condition of rolling mill torus liner, the MLAWS is quenched from 900-920 ℃ and tempered at 350-370℃.展开更多
文摘The paper has studied the mechanical properties and heat treatment effects on multi-element low alloy wear-resistant steel (MLAWS) used as a material for the liner of rolling mill torii. The results show that when quenched at 900-920℃ and tempered at 350-370℃, the MLAWS has achieved hardness above 60 HRC, tensile strength greater than 1 600 MPa, impact toughness higher than 18J/cm2 and fracture toughness greater than 37 MPa·m1/2. When the quenching temperature is lower than 900℃, the hardness of the MLAWS increases with the temperature. When the quenching temperature is higher than 900℃, the hardness decreases with the increase of temperature. At a quenching temperature below 920℃, the effect of quenching temperature on the impact toughness is not obvious. In quenching at above 920℃, impact toughness decreases as the temperature increases. When the tempering temperature is exceeding 450℃, the hardness begins to decrease significantly. Tempering at 350℃ has produced the best wear resistance on the MLAWS.
基金ItemSponsored by Tackle-Key-Programof Science and Technology Committee of Henan Province (042426002 ,0535010700)Henan Innovation Project for University Prominent Research Talents (2006KYCX022)
文摘The effects of heat treatment on the properties of multi element wear-resistant low-alloy steel (MLAWS) which is used to make the liner of rolling mill torus were researched. The results show that when quenching temperature is lower than 900℃, the hardness increases with the increase of temperature, and when quenching temperature is higher than 900℃, the hardness decreases with the increase of temperature. As quenching temperature is lower than 920℃, the effect of quenching temperature on the impact toughness is not obvious. When quenching temperature is higher than 920℃ , impact toughness decreases with the increase of temperature. When tempering temperature is higher than 450 ℃ , the hardness begins to decrease obviously. After tempering at 350℃, the best wear resistance was obtained. According to the service condition of rolling mill torus liner, the MLAWS is quenched from 900-920 ℃ and tempered at 350-370℃.