The present study aims at developing the high speed steel (HSS) as rollmaterials to replace the traditional roll materials such as the alloy cast iron and powdermetallurgical (PM) hard alloy. The HSS roll billet was f...The present study aims at developing the high speed steel (HSS) as rollmaterials to replace the traditional roll materials such as the alloy cast iron and powdermetallurgical (PM) hard alloy. The HSS roll billet was formed by centrifugal casting, and the billetwas rough machined alter soften annealing heat treatment, then it was quenched and tempered to getsuitable hardness and toughness. After that the HSS roll was finish machined to the final dimensionof phi 285 mm in the outer diameter, phi 160 mm in the inner diameter and 120 mm in width and itssurface hardness was tested. Finally the HSS roll was used in high speed wire rod mill. The testresults show that a high and homogeneous hardness can obtain on the work surface of HSS rolls, thesurface hardness is 63-65HRC and its variation is smaller than 2HRC. The impact toughness of thiskind of HSS is about 16 J/cm^2. The results of on-line service investigation in high speed wire rodmill indicate that the HSS rolls have excellent wear resistance, the steel rolling quantity per mmof HSS rolls is 3120 t, the service life-span of HSS rolls is 4 times longer than that of highchromium cast iron rolls and it is close to that of the PM hard alloy rolls. The manufacturingburden of HSS rolls is obviously lower than that of the PM hard alloy rolls, it is only 25 percentof that of the PM hard alloy rolls.展开更多
High speed steel (HSS) rolls can replace traditional rolls such as alloyed cast iron rolls and powder metallurgical (PM) hard alloy rolls. The main reasons for the replacement are that the wear resistance of low-cost ...High speed steel (HSS) rolls can replace traditional rolls such as alloyed cast iron rolls and powder metallurgical (PM) hard alloy rolls. The main reasons for the replacement are that the wear resistance of low-cost alloyed cast iron rolls is poor and the cost of high-quality PM hard alloy rolls is very high. By means of centrifugal casting, HSS rolls having excellent wear resistance have been manufactured. The hardness of the HSS roll is 6.5~67 HRC, the range of variation is smaller than 2 HRC and its impact toughness is 15 J/cm^2. The wear rate of HSS rolls used in the pre-finishing stands of high-speed hot wire-rod rolling mill reaches 2.5×10^(-4)mm per ton steel. Furthermore, the manufacturing cost of HSS rolls is significantly lower than that of PM hard alloy rolls; it is only 30 percent of that of PM hard alloy rolls.展开更多
The centrifugal casting of compound HSS/nodular cast iron roll collar was studied,and the factors affecting transition zone quality were analyzed.The pouring temperature and interval in pouring are the main factors af...The centrifugal casting of compound HSS/nodular cast iron roll collar was studied,and the factors affecting transition zone quality were analyzed.The pouring temperature and interval in pouring are the main factors affecting transition zone quality.By controlling process parameter and flux adding during casting,high quality roll collar was obtained.The cause,why in the casting of HSS part,segregation appears easily,was analyzed and the countermeasure eliminating segregation was put forward,the measure eliminating heat treatment crackling was also put forward.展开更多
The present study aims at developing high speed steel (HSS) as roll materialsto replace traditional roll materials such as the alloy cast iron and powder metallurgical (PM)hard alloy, because low-cost alloy cast iron ...The present study aims at developing high speed steel (HSS) as roll materialsto replace traditional roll materials such as the alloy cast iron and powder metallurgical (PM)hard alloy, because low-cost alloy cast iron rolls have poor wear resistance and the cost ofhigh-quality PM hard alloy rolls is too high to be accepted by some users. By means of a centrifugalcasting method, HSS rolls with excellent wear resistance have been developed. Its hardness is 65-67 HRC, and its variation is smaller than 2HRC; its impact toughness excels 15J/cm^2. Usingpre-finishing stands of a high-speed hot wire-rod rolling mill, the wear rate of HSS rolls per onethousand ton of steel is 0. 25mm. However, the manufacturing burden of HSS rolls is obviously lowerthan that of PM hard alloy rolls; it is only 30% of that of PM hard alloy rolls.展开更多
Due to its high hardness,good red hardness and excellent wear resistance at high temperature,high speed steel(HSS)is fit for the roll manufacture.In order to overcome the segregation of centrifugal casting of HSS roll...Due to its high hardness,good red hardness and excellent wear resistance at high temperature,high speed steel(HSS)is fit for the roll manufacture.In order to overcome the segregation of centrifugal casting of HSS roll,die-cast processes were developed and its effects on the properties of the HSS roll were investigated.It was found that pressure,pressing time and speed are three important factors affecting shrinkage cavity.For pouring temperature of 1 400-1 450 ℃,pressure of 150-160 MPa,pressing time of 120-150 sand pressing speed of 14-16mm/s,a compact HSS roll was obtained,which has no segregation and small working allowance.In the high speed wire rod rolling mill,service life of the HSS roll is 5to 8times longer than that of high nickel chromium infinite chilled cast iron roll.展开更多
A high speed steel composite roll billet was fabricated, which is regular in shape, smooth in surface, slight in trace, compact in internal structure, free of slag inclusion, shrinkage cavity, cracks and other flaws, ...A high speed steel composite roll billet was fabricated, which is regular in shape, smooth in surface, slight in trace, compact in internal structure, free of slag inclusion, shrinkage cavity, cracks and other flaws, and good in macro quality of junction surface using a vertical continuous casting machine. The interface zone microstructure of bimetallic in billet of high speed steel composite roll was analyzed by metallurgical microscope(OM), X-ray diffractmeter(XRD), scanning electron microscopy(SEM) and energy-dispersive X-ray analysis(EDS). The results indicate that the microstructure of roll billet is composed of chilled solidified layer, dendrite zone, interfacial zone of bimetal and core material zone. The microstructure of outer shell material is composed of martensite + bainite + residual austenite + some small labyrinth-shape, small-short lath-shape, or dollop-shape eutectic carbides. The microstructure of core material is slice-shape pearlite and a little ferrite along boundary of cells. The interface region microstructure of bimetallic composite roll consists of diffusion region, chilled solidified layer and columnar grain region.展开更多
The M2 high-speed steel strip was produced by using the laboratory scale twin roll strip caster. The microstructure and eutectic carbide morphology of thus produced products were observed and analyzed, and the compari...The M2 high-speed steel strip was produced by using the laboratory scale twin roll strip caster. The microstructure and eutectic carbide morphology of thus produced products were observed and analyzed, and the comparison of those with conventional products was carried out. The effects of the processing parameters such as the melting temperature, the pouring temperature, rolling speed and separating force on the microstructure and eutectic carbide morphology and their distribution were analyzed. The spheroidizing process of the strips in the annealing process was investigated. The relations between the growth and spheroidizing of the eutectic carbide and the annealing technology were obtained, and the mechanism of the twin roll strip casting process improving the eutectic carbide spheroidizing was discussed. The theoretical instruction for determining the subsequent treatment process was provided.展开更多
The centrifugal casting of compound HSS/nodular cast iron roll collar was studied, and the factors affecting transition zone quality were analyzed. The pouring temperature and interval in pouring are the main factors ...The centrifugal casting of compound HSS/nodular cast iron roll collar was studied, and the factors affecting transition zone quality were analyzed. The pouring temperature and interval in pouring are the main factors affecting transition zone quality. By controlling process parameter and flux adding during casting, high quality roll collar was obtained. The cause, why in the casting of HSS part, segregation appears easily, was analyzed and the countermeasure eliminating segregation was put forward, the measure eliminating heat treatment crackling was also put forward.展开更多
文摘The present study aims at developing the high speed steel (HSS) as rollmaterials to replace the traditional roll materials such as the alloy cast iron and powdermetallurgical (PM) hard alloy. The HSS roll billet was formed by centrifugal casting, and the billetwas rough machined alter soften annealing heat treatment, then it was quenched and tempered to getsuitable hardness and toughness. After that the HSS roll was finish machined to the final dimensionof phi 285 mm in the outer diameter, phi 160 mm in the inner diameter and 120 mm in width and itssurface hardness was tested. Finally the HSS roll was used in high speed wire rod mill. The testresults show that a high and homogeneous hardness can obtain on the work surface of HSS rolls, thesurface hardness is 63-65HRC and its variation is smaller than 2HRC. The impact toughness of thiskind of HSS is about 16 J/cm^2. The results of on-line service investigation in high speed wire rodmill indicate that the HSS rolls have excellent wear resistance, the steel rolling quantity per mmof HSS rolls is 3120 t, the service life-span of HSS rolls is 4 times longer than that of highchromium cast iron rolls and it is close to that of the PM hard alloy rolls. The manufacturingburden of HSS rolls is obviously lower than that of the PM hard alloy rolls, it is only 25 percentof that of the PM hard alloy rolls.
文摘High speed steel (HSS) rolls can replace traditional rolls such as alloyed cast iron rolls and powder metallurgical (PM) hard alloy rolls. The main reasons for the replacement are that the wear resistance of low-cost alloyed cast iron rolls is poor and the cost of high-quality PM hard alloy rolls is very high. By means of centrifugal casting, HSS rolls having excellent wear resistance have been manufactured. The hardness of the HSS roll is 6.5~67 HRC, the range of variation is smaller than 2 HRC and its impact toughness is 15 J/cm^2. The wear rate of HSS rolls used in the pre-finishing stands of high-speed hot wire-rod rolling mill reaches 2.5×10^(-4)mm per ton steel. Furthermore, the manufacturing cost of HSS rolls is significantly lower than that of PM hard alloy rolls; it is only 30 percent of that of PM hard alloy rolls.
文摘The centrifugal casting of compound HSS/nodular cast iron roll collar was studied,and the factors affecting transition zone quality were analyzed.The pouring temperature and interval in pouring are the main factors affecting transition zone quality.By controlling process parameter and flux adding during casting,high quality roll collar was obtained.The cause,why in the casting of HSS part,segregation appears easily,was analyzed and the countermeasure eliminating segregation was put forward,the measure eliminating heat treatment crackling was also put forward.
文摘The present study aims at developing high speed steel (HSS) as roll materialsto replace traditional roll materials such as the alloy cast iron and powder metallurgical (PM)hard alloy, because low-cost alloy cast iron rolls have poor wear resistance and the cost ofhigh-quality PM hard alloy rolls is too high to be accepted by some users. By means of a centrifugalcasting method, HSS rolls with excellent wear resistance have been developed. Its hardness is 65-67 HRC, and its variation is smaller than 2HRC; its impact toughness excels 15J/cm^2. Usingpre-finishing stands of a high-speed hot wire-rod rolling mill, the wear rate of HSS rolls per onethousand ton of steel is 0. 25mm. However, the manufacturing burden of HSS rolls is obviously lowerthan that of PM hard alloy rolls; it is only 30% of that of PM hard alloy rolls.
基金Item Sponsored by Provincial Natural Science Foundation of Henan of China(2003460001)University Young Backbone Teacher Fund of Henan ProvinceTackle-Key-Program of Science and Technology Committee of Henan Province(0424260002)
文摘Due to its high hardness,good red hardness and excellent wear resistance at high temperature,high speed steel(HSS)is fit for the roll manufacture.In order to overcome the segregation of centrifugal casting of HSS roll,die-cast processes were developed and its effects on the properties of the HSS roll were investigated.It was found that pressure,pressing time and speed are three important factors affecting shrinkage cavity.For pouring temperature of 1 400-1 450 ℃,pressure of 150-160 MPa,pressing time of 120-150 sand pressing speed of 14-16mm/s,a compact HSS roll was obtained,which has no segregation and small working allowance.In the high speed wire rod rolling mill,service life of the HSS roll is 5to 8times longer than that of high nickel chromium infinite chilled cast iron roll.
基金Project(200809123) supported by the National Natural Science Foundation of China
文摘A high speed steel composite roll billet was fabricated, which is regular in shape, smooth in surface, slight in trace, compact in internal structure, free of slag inclusion, shrinkage cavity, cracks and other flaws, and good in macro quality of junction surface using a vertical continuous casting machine. The interface zone microstructure of bimetallic in billet of high speed steel composite roll was analyzed by metallurgical microscope(OM), X-ray diffractmeter(XRD), scanning electron microscopy(SEM) and energy-dispersive X-ray analysis(EDS). The results indicate that the microstructure of roll billet is composed of chilled solidified layer, dendrite zone, interfacial zone of bimetal and core material zone. The microstructure of outer shell material is composed of martensite + bainite + residual austenite + some small labyrinth-shape, small-short lath-shape, or dollop-shape eutectic carbides. The microstructure of core material is slice-shape pearlite and a little ferrite along boundary of cells. The interface region microstructure of bimetallic composite roll consists of diffusion region, chilled solidified layer and columnar grain region.
基金supported by both the National Natural Science Foundation of China under the contract No.59995440the Natural Science Foundation of Liaoning Province under the contract No.2001101021
文摘The M2 high-speed steel strip was produced by using the laboratory scale twin roll strip caster. The microstructure and eutectic carbide morphology of thus produced products were observed and analyzed, and the comparison of those with conventional products was carried out. The effects of the processing parameters such as the melting temperature, the pouring temperature, rolling speed and separating force on the microstructure and eutectic carbide morphology and their distribution were analyzed. The spheroidizing process of the strips in the annealing process was investigated. The relations between the growth and spheroidizing of the eutectic carbide and the annealing technology were obtained, and the mechanism of the twin roll strip casting process improving the eutectic carbide spheroidizing was discussed. The theoretical instruction for determining the subsequent treatment process was provided.
基金Sponsored by National Natural Science Foundation(59874024)
文摘The centrifugal casting of compound HSS/nodular cast iron roll collar was studied, and the factors affecting transition zone quality were analyzed. The pouring temperature and interval in pouring are the main factors affecting transition zone quality. By controlling process parameter and flux adding during casting, high quality roll collar was obtained. The cause, why in the casting of HSS part, segregation appears easily, was analyzed and the countermeasure eliminating segregation was put forward, the measure eliminating heat treatment crackling was also put forward.