New Technology of Multidirectional Loading Rotary Extrusion

To satisfy the requirements for the precise formation of large-scale high-performance lightweight components with inner ring reinforcement, a new multidirectional loading rotary extrusion forming technology is developed to match the linear motion with the rotary motion and actively increases the strong shear force. Its principle is that the radial force and rotating torque increase when the blank is axially extruded and loaded. Through the synergistic action of axial, radial, and rotating motions, the orderly fow of metal is controlled, and the cumulative severe plastic deformation (SPD) of an“uplift-trowel” micro-area is generated. Consequently, materials are uniformly strengthened and toughened. Simultaneously, through the continuous deformation of a punch “ellipse-circle,” a high reinforcement component is grown on the cylinder wall to achieve the high-quality formation of cylindrical parts or the inner-ring-reinforcement components. Additionally, the efective strain increases with rotation speed, and the maximum intensity on the basal plane decreases as the number of revolutions increase. The punch structure also afects the axial extrusion loading and equivalent plastic strain. Thus, the proposed technology enriches the plastic forming theory and widens the application feld of plastic forming. Furthermore, the formed large-scale high-performance inner-ring-stifened magnesium components have been successfully verifed in aerospace equipment, thereby solving the problems of integral forming and severe deformation strengthening and toughening. The developed technology has good prospects for mass production and application.

Radially loading rotary extrusion for manufacturing large-size conical cylinders with inner transverse high ribs

The Large-size Conical Cylinders with Inner Transverse High Ribs(LCCWITHR) can reduce the weight of the parts while maintaining high rigidity and strength. Radially Loading Rotary Extrusion(RLRE) forming technology can achieve integral forming of LCCWITHR through the synergy of radial and rotary movements of dies. The flow law of the material during the forming process is the key to forming large-size inner ribs. At present, there is no unified understanding of the metal flow law of RLRE forming technology. An analytical expression was derived to predict the Radial Direction(RD) deformation loads. The FE simulation and process experiment were carried out to investigate the effects of the inclination angle, thickness factor and transition arc radius of the split top dies on the spacing of the metal diversion plane, the metal flow velocity of the rib area and the final radius of the inner rib. The influence of the split top dies loading distance and the bottom die rotation angle of each pass on the inner radius of the inner rib was verified. And the optimal combination of dies shape parameters and loading paths which can make the metal flow orderly was obtained: the inclination angle is 140°, the thickness factor is 3.64, the transition arc radius is 16 mm;the top dies loading distance is 15 mm, the bottom die rotation angle is 45°.The FE simulation results have been found to be in close agreement with physics experiment.The research results reveal the metal flow law of rib growth in the RLRE of LCCWITHR, which lays a theoretical foundation for subsequent thorough research and process optimization.

Effect of circumferential strain rate on dynamic recrystallization and texture of Mg-13Gd-4Y-2Zn-0.5Zr alloy during rotary backward extrusion

Gleeble-3500 thermal simulator was applied to realize the rotary backward extrusion forming of Mg-13Gd-4Y-2Zn-0.5Zr(wt%)alloy at different circumferential strain rate from 0.009 s^(-1)to 0.027 s^(-1)at 400℃and the dynamic recrystallization mechanism and texture evolution were studied.The results show that the grain size of the alloy was obviously refined after rotary backward extrusion.As the circumferenlial strain rate increased,the dynamic recrystallization fraction gradually increased causing the grain size decreased and the distribution of microstructure became more uniform.At the same time,the texture of{0001},{10-10},{11-20}was weakened and the grain orientation distribution became more random.With the increase of circumferential strain rate,the discontinuous dynamic recrystallization mechanism became dominant,which promoted the weakening of texture and grain refinement of the alloy.