Preheating-assisted solid-state friction stir repair of Al-Mg-Si alloy plate at different rotational speeds

Additive friction stir deposition(AFSD)is a novel structural repair and manufacturing technology has become a research hotspot at home and abroad in the past five years.In this work,the microstructural evolution and mechanical performance of the Al-Mg-Si alloy plate repaired by the preheating-assisted AFSD process were investigated.To evaluate the tool rotation speed and substrate preheating for repair quality,the AFSD technique was used to additively repair 5 mm depth blind holes on 6061 aluminum alloy substrates.The results showed that preheat-assisted AFSD repair significantly improved joint bonding and joint strength compared to the control non-preheat substrate condition.Moreover,increasing rotation speed was also beneficial to improve the metallurgical bonding of the interface and avoid volume defects.Under preheating conditions,the UTS and elongation were positively correlated with rotation speed.Under the process parameters of preheated substrate and tool rotation speed of 1000 r/min,defect-free specimens could be obtained accompanied by tensile fracture occurring in the substrate rather than the repaired zone.The UTS and elongation reached the maximum values of 164.2MPa and 13.4%,which are equivalent to 99.4%and 140%of the heated substrate,respectively.

Research on Cavitation Characteristics and Influencing Factors of Herringbone Gear Pump

Cavitation is a common issue in pumps,causing a decrease in pump head,a fall in volumetric efficiency,and an intensification of outlet flow pulsation.It is one of the main hazards that affect the regular operation of the pump.Research on pump cavitation mainly focuses on mixed flow pumps,jet pumps,external spur gear pumps,etc.However,there are few cavitation studies on external herringbone gear pumps.In addition,pumps with different working principles significantly differ in the flow and complexity of the internal flow field.Therefore,it is urgent to study the cavitation characteristics of external herringbone gear pumps.Compared with experimentalmethods,visual research and cavitation area identification are achieved through computation fluid dynamic(CFD),and changing the boundary conditions and shape of the gear rotor is easier.The simulation yields a head error of only 0.003%under different grid numbers,and the deviation between experimental and simulation results is less than 5%.The study revealed that cavitation causes flow pulsation at the outlet,and the cavitation serious area is mainly distributed in the meshing gap and meshing area.Cavitation can be inhibited by reducing the speed,increasing the inlet pressure,and changing the helix angle can be achieved.For example,when the inlet pressure is 5 bar,the maximumgas volume fraction in themeshing area is less than 50%.These results provide a reference for optimizing the design and finding the optimal design parameters to reduce or eliminate cavitation.

Earth: Review Article

Every year on 22 April, we have celebrated Earth Day and the beautiful planet we call home. Earth Day, established in 1970, has been used to highlight our planet’s environmental challenges and raise awareness of the importance of protecting our world for future generations [1]. To provide the protection of our planet, we should explain Earth’s environmental challenges to the best of our knowledge in frames of contemporary Geophysics. This paper gives a short overview of the developed Hypersphere World-Universe Model (WUM) and pay particular attention to the principal role of Dark Matter (DM) in the Earth’s life. In this manuscript, we discuss different aspects of the Earth: a condition of Young Earth before the Beginning of life on It;Internal Structure;“The 660-km Boundary” that we named Geomagma;Random Variations of Earth’s Rotational Speed on a daily basis;Origin of Moon;Expanding Earth;Internal Heating;Faint Young Sun paradox;Geocorona and Planetary Coronas;High-Energy Atmospheric Physics. WUM proposed principally different ways to solve the problems of Internal Heating, Origin of the Moon, and Faint Young Sun paradox based on DM core of the Earth. The Model revealed the fact that the Sun Activity causes the Geomagma Activity and, as a consequence, Random Variations of Earth’s Rotational Speed by the varying Sun’s magnetic field.

Effect of driver roll rotational speed on hot ring rolling of AZ31 magnesium alloy

Based on the ABAQUS/Explicit code,A 3D elastic-plastic and coupled thermo-mechanical FE model of radial ring rolling of AZ31 Magnesium alloy has been proposed to analyze the influence of rotational speed of driver roll to study the inhomogeneity distribution of strain and temperature,fishtail coefficient,rolling force parameters.The results show that:(1)when the rotational speed of driver roll n increases,the strain distribution of the rolled ring becomes less homogeneous,and the temperature distribution more homogeneous yet,and leading to an optimal n value;(2)the fishtail coefficient firstly decreases,then increases with the increase of n;(3)the rolling force,contact area and rolling moment gradually descend with the increase of n.

On the Effect of the Rotating Chamber Reverse Speed on the Mixing of SiC Ceramic Particles in a Dry Granulation Process

In order to control the accumulation of SiC ceramic particles on the wall of the rotating chamber in the frame of a dry granulation process,the effect of the wall reverse speed on the mixing process is investigated.In particular,an Euler-Euler two-phase flow model is used to analyze the dynamics of both SiC particles and air.The numerical results show that by setting a certain reverse rotating speed of the rotating chamber,the accumulation of SiC particles on the wall can be improved,i.e.,their direction of motion in proximity to the wall can be changed and particles can be forced to re-join the granulation process.Experimental tests conducted to verify the reliability of the numerical findings,demonstrate that when the reverse rotating speed of the rotating chamber is 4 r/min,the sphericity of SiC particles in the rotating chamber is the highest and the fluidity is the best possible one.

Research on dynamic stabilityrotational speed range of rolling projectiles with different characteristics

Traditional dynamic stability analyses of the rolling projectiles are mainly based on solving the systems＇ transfer functions or angular motion＇ s homogeneous equations to obtain their charac- teristic roots. The solving processes of these methods are complex and lacking further analysis of the results. To solve this problem, Routh stability criterion is introduced to determine the stability of rolling missiles based on the transfer function model, and an important advantage of this method is that it is unnecessary to solve the system＇ s characteristic equation. Rotational speed ranges satisfy- ing the dynamic stability of rolling projectiles with four different characteristics are acquired, and the correctness of analysis results is verified by computing the system＇ s root locus. The analysis results show that the relation between stability and rotational speed for static stable missiles is opposite to that for spin-stabilized projectiles, and the relative size of gyroscopic effect and Magnus effect has an extremely important influence on the trend of the stability of the system with increasing rotational speed.

Effect of Rotating Speed Fluctuation on External Hydraculic Performance of a Vane Pump

The rotating speed fluctuation for turbomachinery is a common problem, which will cause severe destruction for equipments and basis when the fluctuation is very strong. In this paper,in order to study the transient response characteristics of a radial vane pump subjected to slight( 5%) and strong( 20%)fluctuating rotational speeds, the variation characteristics of the external hydraulic performances are numerically predicted by means of computational fluid dynamics( CFD) technology. The results manifest that the responses of head and flow rate are different relative to the fluctuating characteristics of rotational speed. The response of the former is very satisfied in synchronism,while that of the latter is hysteretic. Meanwhile,it is found that the variation tendencies of the static pressures at the inlet and outlet of the pump are completely opposite, while the response characteristics of the dynamic pressures at the inlet and outlet are nearly identical.Subsequently,in order to further reveal the transient behavior during the instantaneous operating periods,two non-dimensional parameters are employed to deeply analyze it. The result shows that the variation tendencies of these two parameters are also approximately opposite.Moreover,the quasi-steady assumption is not able to be used to accurately assess the transient flow during transient operating periods. The comparison results show that the transient behavior does not show obvious distinctions between slight and strong fluctuating rotating speeds.

Analysis of flow response to fluctuation of rotational speed in a radial impeller

By discretizing the convection terms with AUSM+-up scheme in the rotating coordinate system,a finite volume analysis code based on multi-block structured grids was developed independently so as to realize the numerical solving of internal flow fields of turbomachineries.Taking an unshrouded radial impeller with the working fluid of water vapour as the research object,the flow response to the fluctuation of rotational speed was calculated.By comparing the surface pressure profiles and velocity contours calculated by the code and commercial software respectively,the accuracy of flow solver was verified.The analysis of flow response data indicates that,as the working condition shifts closer towards the surge boundary,the response of flow parameters such as mass flow and aerodynamic torque will be more nonsynchronous with the fluctuation of rotational speed,and also the influence of density variation on mass flow variation will be smaller.Moreover,the transient variation region of working condition performance will deviate farther away from the steady performance curve as the working condition approaches the surge boundary.Compared to the working conditions with small mass flows,the distribution characteristics of pressure difference load on the blade surface vary little under large mass flow conditions.The reduction of fluctuation amplitude of rotational speed exerts no influence on abating the hysteresis of flow response.

Effect of pin rotating speed on lap shear strength of stationary shoulder friction stir lap welded 6005A-T6 aluminum alloy

Stationary shoulder friction stir lap welding （SSFSLW） was successfully used to weld 6005A-T6 aluminum alloy in this paper. Effect of pin rotating speed on cross section morphologies and lap shear strength of the SSFSLW joints were mainly discussed. Results show that joints without flash and shoulder marks can be obtained by the stationary shoulder. Cross section of the SSFSLW joint presents a basin-like morphology and little material loss. By increasing the rotating speed from 1 000 rpm to 1 600 rpm, both effective sheet thickness and lap width increase, while lap shear failure load firstly decreases and then increases. The maximum failure load of 14. 05 kN /s attained when 1 000 rpm is used. All SSFSLW joints present shear fracture mode.

Controllable and high-throughput preparation of microdroplet using an ultra-high speed rotating packed bed

Microdroplets and their dispersion,with a large specific surface area and a short diffusion distance,have been applied in various unit operations and reaction processes.However,it is still a challenge to control the size and size distribution of microdroplets,especially for high-throughput generation.In this work,a novel ultra-high speed rotating packed bed(UHS-RPB)was invented,in which rotating foam packing with a speed of 4000-12000 r·min^(-1) provides microfluidic channels to disperse liquid into microdroplets with high throughput.Then generated microdroplets can be directly dispersed into a continuous falling film for obtaining a mixture of microdroplet dispersion.In this UHS-RPB,the effects of rotational speed,liquid initial velocity,liquid viscosity,liquid surface tension and packing pore size on the average size(d_(32))and size distribution of microdroplets were systematically investigated.Results showed that the UHS-RPB could produce microdroplets with a d_(32) of 25-63μm at a liquid flow rate of 1025 L·h^(-1),and the size distribution of the microdroplets accords well with Rosin-Rammler distribution model.In addi-tion,a correlation was established for the prediction of d_(32),and the predicted d_(32) was in good agreement with the experimental data with a deviation within±15%.These results demonstrated that UHS-RPB could be a promising candidate for controllable preparation of uniform microdroplets.

Microstructures in Centrifugal Casting of SiC_p/AlSi9Mg Composites with Different Mould Rotation Speeds

Two ingots were produced by centrifugal casting at mould rotational speeds of 600 rpm and 800 rpm using 20 vol%SiC p /AlSi9Mg composite melt,respectively.The microstructure along the radial direction of cross-sectional sample of ingots was presented.SiC particles migrated towards the external circumference of the tube,and the distribution of SiC particles became uniform under centrifugal force.Voids in 20 vol%SiC p /AlSi9Mg composite melt migrated towards the inner circumference of the tube.The quantitative analysis results indicated that not only SiC particles but also primaryαphases segregated greatly in centrifugal casting resulting from the transportation behavior of constitutions with different densities in the SiC p /AlSi9Mg composite melt.In addition,the eutectic Si was broken owing to the motion of SiC p /AlSi9Mg composite melt during centrifugal casting.

Distribution of oxide inclusions in H13 castings under super-gravity field with multi-stage rotation speeds

The 42 kg industrial H13 castings were prepared by different super-gravity fields with multi-rotation speeds,and the distribution of oxide inclusions in the castings was studied.In addition,the inward movement Reynolds number and inward movement time of oxide inclusions as well as the solidification time of molten steel at different positions in the castings were calculated to clarify the removal mechanism of oxide inclusions in super-gravity field.The results show that the large size(i.e.,greater than 10μm)oxide inclusions are mainly concentrated in the inner and outer parts of the super-gravity castings with constant rotation speed(500 r min^(-1))and five-stage rotation speeds(500,600,750,850,and 950 r min^(-1)),respectively,while there are no large oxide inclusions in the super-gravity castings with three-stage rotation speeds(500,600,and 750 r min^(-1)).Although an increase in the particle size of inclusion and the rotation speed in super-gravity field is conducive to the increase in the inward movement Reynolds number of oxide inclusions and reduction in the inward movement time of oxide inclusions,it will reduce the local solidification time of molten steel.In the range of the rotation speed studied,the super-gravity field with three-stage rotation speeds has the best effect on the removal of inclusions in H13 molten steel.

Complementary-Label Adversarial Domain Adaptation Fault Diagnosis Network under Time-Varying Rotational Speed and Weakly-Supervised Conditions

Recent research in cross-domain intelligence fault diagnosis of machinery still has some problems,such as relatively ideal speed conditions and sample conditions.In engineering practice,the rotational speed of the machine is often transient and time-varying,which makes the sample annotation increasingly expensive.Meanwhile,the number of samples collected from different health states is often unbalanced.To deal with the above challenges,a complementary-label(CL)adversarial domain adaptation fault diagnosis network(CLADAN)is proposed under time-varying rotational speed and weakly-supervised conditions.In the weakly supervised learning condition,machine prior information is used for sample annotation via cost-friendly complementary label learning.A diagnosticmodel learning strategywith discretized category probabilities is designed to avoidmulti-peak distribution of prediction results.In adversarial training process,we developed virtual adversarial regularization(VAR)strategy,which further enhances the robustness of the model by adding adversarial perturbations in the target domain.Comparative experiments on two case studies validated the superior performance of the proposed method.

SIMULATION STUDY OF GENERALIZED MINIMUM VARIANCE CONTROL FOR AN EXTRACTION TURBINE

In an extraction turbine, pressure of the extracted steam and rotate speed of the rotor are two important controlled quantities. The traditional linear state feedback control method is not perfect enough to control the two quantities accurately because of existence of nonlinearity and coupling. A generalized minimum variance control method is studied for an extraction turbine. Firstly, a nonlinear mathematical model of the control system about the two quantities is transformed into a linear system with two white noises. Secondly, a generalized minimum variance control law is applied to the system. A comparative simulation is done. The simulation results indicate that precision and dynamic quality of the regulating system under the new control law are both better than those under the state feedback control law.

Pitting Corrosion Behavior of Stainless Steel 304 in Carbon Dioxide Environments

With a rotating cylinder electrode apparatus, the polarization behaviors of the mild steel and the stainless steel 0Cr18Ni9 in NaHCO 3 (0.5 M)+Na 2CO 3 (0.5 M) solution with and without erodent particles were investigated and compared. The results show that the rotation speed of cylinder hardly affects the polarization behavior of sample in solution without particles but exerts a great influence on that with particles. Increasing rotation speed, the free corrosion potential shifts to positive direction and the oxygen limiting current density increases. Both the mild steel and stainless steel 0Cr18Ni9 experience a significant increase of the mass loss by increasing erosion, and erosive wear was dominated by severe micro-plowing. The insufficient mechanical strength of both materials leads to a low resistance to particle removal. Increasing peripheral velocities of the rotating cylinder enhances the corrosion rate of the mild steel. The stainless steel 0Cr18Ni9, due to a high erosive wear, also suffers from similar erosion-corrosion damage, despite that its corrosion resistance is much higher than that of the mild steel.

Experimental Study of Cavitation Phenomenon in a Centrifugal Blood Pump Induced by the Failure of Inlet Cannula

Cavitation of centrifugal blood pump is a serious problem accompany with the blocking failure of short inlet cannula. However, hardly any work has been seen in published literature on this complex cavitation phenomenon caused by the coupling effect of inlet cannula blocking and pumps suction. Even for cavitation studies on ordinary centrifugal pumps, similar researches on this issue are rare. In this paper, the roles of throttling, rotation speed and fluid viscosity on bubble inception and intensity in a centrifugal blood pump are studied, on the basis of experimental observations. An adjustable throttle valve installed just upstream blood pump inlet is used to simulate the throttling effect of the narrowed inlet cannula. The rotation speed is adjusted from 2 600 r/rain to 3 200 r/min. Glycerin water solutions are used to investigate the influences of kinetic viscosity. Bubbles are recorded with a high-speed video camera. Direct observation shows that different from cavitation in industrial centrifugal pumps, gas nuclei appears at the nearby of vane leading edges while throttling is light, then moves upstream to the joint position of inlet pipe and pump with the closing of the valve. It＇s found that the critical inlet pressure, obtained when bubbles are first observed, decreases linearly with viscosity and the slope is independent with rotation speeds; the critical inlet pressure and the inlet extreme pressure which is obtained when the throttle valve is nearly closed, fall linearly with rotation speed respectively and the relative pressure between them is independent with rotation speed and fluid viscosity. This paper studies experimentally on cavitation in centrifugal blood pump that caused by the failure of assembled short inlet cannula, which mav beneficial the desima of centrifugal blood Dumo with inlet cannula.

Effect of Process Parameters on Tensile Strength of Friction Stir Welded Cast LM6 Aluminium Alloy Joints

This paper reports the effect of friction stir welding （FSW） process parameters on tensile strength of cast LM6 aluminium alloy. Joints were made by using different combinations of tool rotation speed, welding speed and axial force each at four levels. The quality of weld zone was investigated using macrostructure and microstructure analysis. Tensile strength of the joints were evaluated and correlated with the weld zone hardness and microstructure. The joint fabricated using a rotational speed of 900 r/min, a welding speed of 75 mm/min and an axial force of 3 kN showed superior tensile strength compared with other joints. The tensile strength and microhardness of the welded joints for the optimum conditions were 166 MPa and 64.8 Hv respectively.

FOUR WHEELS DRIVEN INDEPENDENTLY BY ONE PUMP DRIVING FOUR HYDRAULIC MOTORS

An improved Narendra model reference adaptive control (MRAC) scheme isproposed to research one variable displacement pump driving four hydraulic variable displacementmotors. This approach not only ensures the underdamped and unstable system be global uniformasymptotic stability, but also has good robustness in these aspects of modeling uncertainty,pressure fluctuation of constant pressure network, and disturbance from external load, which alsoupgrades the rapidity of system response so as to make controlled system with nicer dynamic quality.The scheme of one pump driving four motors can meet the demand on off-road mobility of engineeringvehicles and armored cars. A proof of stability about improved Narendra MRAC scheme is also given.

Effect of centrifugal counter-gravity casting on solidification microstructure and mechanical properties of A357 aluminum alloy

To investigate the influence of Centrifugal Counter-gravity Casting(C3) process on the solidification microstructure and mechanical properties of the casting, A357 aluminum alloy samples were produced by different process conditions under C3. The results show that C3 has better feeding capacity compared with the vacuum suction casting; and that the mechanical vibration and the convection of melts formed at the centrifugal rotation stage suppress the growth of dendrites, subsequently resulting in the refinement of grains and the improvement of mechanical properties, density and hardness. A finer grain and higher strength can be obtained in the A357 alloy by increasing centrifugal radius and rotational speed. However, casting defects will appear near the rotational axis and the mechanical properties will decrease once the rotational speed exceeds 150 r·min-1.

Analysis Method and Principle of Dual-mode Electro-mechanical Variable Transmission Program

Automotive industry,as an important pillar of the national economy,has been rapidly developing in recent years.But proplems such as energy comsumption and environmental pollution are posed at the same time.Electro-mechanical variable transmission system is considered one of avilable workarounds.It is brought forward a kind of design methods of dual-mode electro-mechanical variable transmission system rotational speed characteristics and dual-mode drive diagrams.With the motor operating behavior of running in four quadrants and the speed characteristics of the simple internal and external meshing single planetary gear train,four kinds of dual-mode electro-mechanical transmission system scheme are designed.And the velocity,torque and power characteristics of one of the programs are analyzed.The magnitude of the electric split-flow power is an important factor which influences the system performance,so in the parameters matching design,it needs to reduce the power needs under the first mode of the motor.The motor,output rotational speed range and the position of the mode switching point have relationships with the characteristics design of the planetary gear set.The analysis method is to provide a reference for hybrid vehicles＇ design.As the involved rotational speed and torque relationships are the natural contact of every part of transmission system,a theory basis of system program and performance analysis is provided.