This work focuses on the development of carpets from sand, fabrics of cotton fiber and mosquito nets and rubber latex. Following a study on the choice of the best formulations, the quantity of rubber latex used for sh...This work focuses on the development of carpets from sand, fabrics of cotton fiber and mosquito nets and rubber latex. Following a study on the choice of the best formulations, the quantity of rubber latex used for shaping varies between 14% and 18% (latex/sand + latex ratio) for the carpet with the fabric of mosquito nets and between 16% and 18% for the one made with the fabric of cotton fiber. Thus, with a mixture of sand, fiber fabrics (cotton and mosquito nets) and rubber latex, carpets were developed. In addition, the wear test carried out on these samples indicates that it is possible to produce carpets with the new material made of rubber sand and latex: SABLATEX At room temperature. Following the characterization test, it resorts to only 16% latex with cotton fiber fabric, allowing to have carpets with good mechanical characteristics.展开更多
The radial-orientation-die has special structure to make short fibers get radial orientation in rubber matrix during extrusion process,which means the physical and mechanical properties of short fiber and rubber compo...The radial-orientation-die has special structure to make short fibers get radial orientation in rubber matrix during extrusion process,which means the physical and mechanical properties of short fiber and rubber composite material will be influenced by the die different structures. The effects of radial-orientation-die structure parameters on properties of short fiber and rubber composite were studied experimentally by different structure parameters, including expansion ratio, expansion angle, dam clearance, molding channel length, convergence angle, and transition channel length. The experimental results indicated that short fiber and rubber composite could get good properties with optimized radial-orientation-die structure parameter. And the optimized structure parameters are that expansion ratio is about 5with an expansion angle of 150°,dam clearance is about 4 mm,molding channel length is about 50 mm,convergence angle is about120°,and transition channel length is about 30 mm. Accordingly,the physical and mechanical properties of the composite can be remarkably improved,which give an obvious anisotropy.展开更多
A mixture of NaOH and Na2SO3 was used in modification of banana stem fibers (BSF). Unidirectional BSF reinforced natural rubber (NR) lamina composites were made using compression moulding method. The results of the te...A mixture of NaOH and Na2SO3 was used in modification of banana stem fibers (BSF). Unidirectional BSF reinforced natural rubber (NR) lamina composites were made using compression moulding method. The results of the tensile loading in 0°, 45° and 90° to the fiber directions of the composite with fiber mass fraction of 30% were studied. Surface modification of the BSF with a mixture of 4% NaOH and 2% Na2SO3 increased the tensile strength and elastic modulus of the composite to 4.03 MPa and 147.34 MPa respectively from 3.12 MPa and 84.30 MPa of the untreated. Variation in properties due to fiber orintations was observed indicating a higher value of properties in the 0° fiber orientation than in 45° and 90° directions. The result of scanning electron microscope (SEM) micrographs of the surfaces of the fibers indicted an improvement in bonding of the fiber bundles prior to lamination with natural rubber as a result of surface treatment which resulted in its higher tensile strength.展开更多
This article contributes to the development of the new class of fully biodegradable “green” composites by combining fibers (natural/bio) with biodegradable resin. The vegetable fibers (Triumfetta cordifolia and suga...This article contributes to the development of the new class of fully biodegradable “green” composites by combining fibers (natural/bio) with biodegradable resin. The vegetable fibers (Triumfetta cordifolia and sugarcane bagasse) treated with NaOH and bleached were incorporated into a natural rubber matrix. The influence of the fiber ratio on the physical properties, tensile strength and surface hardness of the hybrid composites was analyzed. The results show that the addition of fibers in the natural rubber matrix increases the water absorption capacity but gradually reduces it with increasing fiber ratio. The hybrid composites of the NRT50-50B proportions show the best tensile strengths at 20 phr and a shore A hardness of 43.7 at 30 phr. The combination of two fibers has improved the physical and mechanical properties of the hybrid composites which can be used in engineering applications.展开更多
In this work,Epoxidized natural rubber/sawdust short fiber(ENR-50/SD)composites at different fiber content(5,10,15 and 20 phr)and size(fine size at 60–100μm and coarse size at 10–20 mm)were prepared using two-roll ...In this work,Epoxidized natural rubber/sawdust short fiber(ENR-50/SD)composites at different fiber content(5,10,15 and 20 phr)and size(fine size at 60–100μm and coarse size at 10–20 mm)were prepared using two-roll mill and electrical-hydraulic hot press machine respectively.Curing characteristics,water uptake,tensile,morphological,physical,and thermal properties of the composites were investigated.Results indicated that the scorch time and cure time became shorter whereas torque improved as SD content increase.Though the decline of tensile strength and elongation at break values,modulus,hardness and crosslinking density have shown enhancements with the increasing of SD content.The water uptake percentage of all samples has shown an increasing as SD content increase.However,the low SD content,particularly fine size have presented lower water uptake.The temperature of weight%loss(5 and 50 wt%loss)of 5 phr SD(low content)have recorded higher temperature compared to 20 phr SD(high content)in the rubber composites,which indicated higher thermal stability.The fine size of SD has recorded better overall properties than SD coarse size at same loading in the rubber composites.展开更多
文摘This work focuses on the development of carpets from sand, fabrics of cotton fiber and mosquito nets and rubber latex. Following a study on the choice of the best formulations, the quantity of rubber latex used for shaping varies between 14% and 18% (latex/sand + latex ratio) for the carpet with the fabric of mosquito nets and between 16% and 18% for the one made with the fabric of cotton fiber. Thus, with a mixture of sand, fiber fabrics (cotton and mosquito nets) and rubber latex, carpets were developed. In addition, the wear test carried out on these samples indicates that it is possible to produce carpets with the new material made of rubber sand and latex: SABLATEX At room temperature. Following the characterization test, it resorts to only 16% latex with cotton fiber fabric, allowing to have carpets with good mechanical characteristics.
基金National Natural Science Foundation of China(No.511576)Doctoral Research Foundation of Education Ministry,China(No.20103719110003)Science&Technology Development Planning of Shandong Province,China(No.2013TD16006)
文摘The radial-orientation-die has special structure to make short fibers get radial orientation in rubber matrix during extrusion process,which means the physical and mechanical properties of short fiber and rubber composite material will be influenced by the die different structures. The effects of radial-orientation-die structure parameters on properties of short fiber and rubber composite were studied experimentally by different structure parameters, including expansion ratio, expansion angle, dam clearance, molding channel length, convergence angle, and transition channel length. The experimental results indicated that short fiber and rubber composite could get good properties with optimized radial-orientation-die structure parameter. And the optimized structure parameters are that expansion ratio is about 5with an expansion angle of 150°,dam clearance is about 4 mm,molding channel length is about 50 mm,convergence angle is about120°,and transition channel length is about 30 mm. Accordingly,the physical and mechanical properties of the composite can be remarkably improved,which give an obvious anisotropy.
文摘A mixture of NaOH and Na2SO3 was used in modification of banana stem fibers (BSF). Unidirectional BSF reinforced natural rubber (NR) lamina composites were made using compression moulding method. The results of the tensile loading in 0°, 45° and 90° to the fiber directions of the composite with fiber mass fraction of 30% were studied. Surface modification of the BSF with a mixture of 4% NaOH and 2% Na2SO3 increased the tensile strength and elastic modulus of the composite to 4.03 MPa and 147.34 MPa respectively from 3.12 MPa and 84.30 MPa of the untreated. Variation in properties due to fiber orintations was observed indicating a higher value of properties in the 0° fiber orientation than in 45° and 90° directions. The result of scanning electron microscope (SEM) micrographs of the surfaces of the fibers indicted an improvement in bonding of the fiber bundles prior to lamination with natural rubber as a result of surface treatment which resulted in its higher tensile strength.
文摘This article contributes to the development of the new class of fully biodegradable “green” composites by combining fibers (natural/bio) with biodegradable resin. The vegetable fibers (Triumfetta cordifolia and sugarcane bagasse) treated with NaOH and bleached were incorporated into a natural rubber matrix. The influence of the fiber ratio on the physical properties, tensile strength and surface hardness of the hybrid composites was analyzed. The results show that the addition of fibers in the natural rubber matrix increases the water absorption capacity but gradually reduces it with increasing fiber ratio. The hybrid composites of the NRT50-50B proportions show the best tensile strengths at 20 phr and a shore A hardness of 43.7 at 30 phr. The combination of two fibers has improved the physical and mechanical properties of the hybrid composites which can be used in engineering applications.
文摘In this work,Epoxidized natural rubber/sawdust short fiber(ENR-50/SD)composites at different fiber content(5,10,15 and 20 phr)and size(fine size at 60–100μm and coarse size at 10–20 mm)were prepared using two-roll mill and electrical-hydraulic hot press machine respectively.Curing characteristics,water uptake,tensile,morphological,physical,and thermal properties of the composites were investigated.Results indicated that the scorch time and cure time became shorter whereas torque improved as SD content increase.Though the decline of tensile strength and elongation at break values,modulus,hardness and crosslinking density have shown enhancements with the increasing of SD content.The water uptake percentage of all samples has shown an increasing as SD content increase.However,the low SD content,particularly fine size have presented lower water uptake.The temperature of weight%loss(5 and 50 wt%loss)of 5 phr SD(low content)have recorded higher temperature compared to 20 phr SD(high content)in the rubber composites,which indicated higher thermal stability.The fine size of SD has recorded better overall properties than SD coarse size at same loading in the rubber composites.