Zeolite （Na） modified by self-synthesized nano-Fe particles was used as infiltration media to adsorb phosphate in rainwater runoff. The adsorption capacities increased up to 75 times that of natural zeolite at a sat...Zeolite （Na） modified by self-synthesized nano-Fe particles was used as infiltration media to adsorb phosphate in rainwater runoff. The adsorption capacities increased up to 75 times that of natural zeolite at a saturated equilibrium phosphate concentration of 0.42 mg/L. The correlation of capacity and material-specific surface area indicated that specific surface area was not the key factor contributing to the capacity improvement. SEM and XRD analysis showed that chemical reaction between Fe and P to form new products like cacoxenite is the main reason for the increased capacity, and that the method of adding metal ions or particles to improve the adsorption capacity for phosphate is feasible.展开更多
Self-made cation exchange resin supported nanoscale zero-valent iron （R-nZVI） was used to remove phosphorus in rainwater runoff. 80% of phosphorus in rainwater runoff from grassland was removed with an initial conce...Self-made cation exchange resin supported nanoscale zero-valent iron （R-nZVI） was used to remove phosphorus in rainwater runoff. 80% of phosphorus in rainwater runoff from grassland was removed with an initial concentration of 0.72 mg. L-1 phosphorus when the dosage of R-nZVl is 8 g per liter rainwater, while only 26% of phosphorus was removed when using cation exchange resin without supported nanoscale zero-valent iron under the same condition. The adsorption capacity of R-nZVI increased up to 185 times of that of the cation exchange resin at a saturated equilibrium phosphorous concentration of 0.42 mg. L-1. Various techniques were implemented to characterize the R-nZVI and explore the mechanism of its removal of phosphate. Scanning electron microscopy （SEM） indicated that new crystal had been formed on the surface of R-nZVI. The result from inductive coupled plasma （ICP） indicated that 2.1% of nZVI was loaded on the support material. The specific surface area was increased after the load of nanoscale zero-valent iron （nZVI）, according to the measurement of BET-N2 method. The result of specific surface area analysis also proved that phosphorus was removed mainly through chemical adsorption process. X-ray photoelectron spectroscopy （XPS） analysis showed that the new product obtained from chemical reaction between phosphate and iron was ferrous phosphate.展开更多
基金supported by the Chinese National Special Science & Technology Project on Treatment and Control of Water Pollution (No.2008ZX07313-004)
文摘Zeolite （Na） modified by self-synthesized nano-Fe particles was used as infiltration media to adsorb phosphate in rainwater runoff. The adsorption capacities increased up to 75 times that of natural zeolite at a saturated equilibrium phosphate concentration of 0.42 mg/L. The correlation of capacity and material-specific surface area indicated that specific surface area was not the key factor contributing to the capacity improvement. SEM and XRD analysis showed that chemical reaction between Fe and P to form new products like cacoxenite is the main reason for the increased capacity, and that the method of adding metal ions or particles to improve the adsorption capacity for phosphate is feasible.
文摘Self-made cation exchange resin supported nanoscale zero-valent iron （R-nZVI） was used to remove phosphorus in rainwater runoff. 80% of phosphorus in rainwater runoff from grassland was removed with an initial concentration of 0.72 mg. L-1 phosphorus when the dosage of R-nZVl is 8 g per liter rainwater, while only 26% of phosphorus was removed when using cation exchange resin without supported nanoscale zero-valent iron under the same condition. The adsorption capacity of R-nZVI increased up to 185 times of that of the cation exchange resin at a saturated equilibrium phosphorous concentration of 0.42 mg. L-1. Various techniques were implemented to characterize the R-nZVI and explore the mechanism of its removal of phosphate. Scanning electron microscopy （SEM） indicated that new crystal had been formed on the surface of R-nZVI. The result from inductive coupled plasma （ICP） indicated that 2.1% of nZVI was loaded on the support material. The specific surface area was increased after the load of nanoscale zero-valent iron （nZVI）, according to the measurement of BET-N2 method. The result of specific surface area analysis also proved that phosphorus was removed mainly through chemical adsorption process. X-ray photoelectron spectroscopy （XPS） analysis showed that the new product obtained from chemical reaction between phosphate and iron was ferrous phosphate.