We investigated the simulation of the cracking and ablation behavior of ferro-siliceous and siliceous nuclear sacrificial concretes. To this end, four type of sacrificial concretes were fabricated, i e, the ferro-sili...We investigated the simulation of the cracking and ablation behavior of ferro-siliceous and siliceous nuclear sacrificial concretes. To this end, four type of sacrificial concretes were fabricated, i e, the ferro-siliceous（F） and siliceous（S） plain concretes, and the polypropylene fiber reinforced concretes of the above two（FF, SF）. The cracking and ablation behaviors of the sacrificial concretes were investigated by simulation tests, and the simulated elevated temperature was obtained by means of thermite powder. The number and the width of the cracks were compared and the pore size distribution of sacrificial concretes was measured. In addition, the interface and chemical composition of melt at different positions were analyzed, and the ablation depth of the sacrificial concrete crucibles was also measured. It was found that the siliceous concrete shows to be more prone to cracking than the ferro-siliceous concrete due to the higher content of fly ash and lower water to binder ratio; though the ablation depth of siliceous concrete is found to be slightly larger, no clear difference can be detected for the basemat ablation rate.展开更多
基金Funded by National Natural Science Foundation of China(Nos.51378114 and 5161113020)National Basic Research Program of China(973 Program)(No.2015CB655105)
文摘We investigated the simulation of the cracking and ablation behavior of ferro-siliceous and siliceous nuclear sacrificial concretes. To this end, four type of sacrificial concretes were fabricated, i e, the ferro-siliceous（F） and siliceous（S） plain concretes, and the polypropylene fiber reinforced concretes of the above two（FF, SF）. The cracking and ablation behaviors of the sacrificial concretes were investigated by simulation tests, and the simulated elevated temperature was obtained by means of thermite powder. The number and the width of the cracks were compared and the pore size distribution of sacrificial concretes was measured. In addition, the interface and chemical composition of melt at different positions were analyzed, and the ablation depth of the sacrificial concrete crucibles was also measured. It was found that the siliceous concrete shows to be more prone to cracking than the ferro-siliceous concrete due to the higher content of fly ash and lower water to binder ratio; though the ablation depth of siliceous concrete is found to be slightly larger, no clear difference can be detected for the basemat ablation rate.