Digital patternless freeze-casting technology is a new approach for obtaining frozen sand moulds using digital milling technology. The change law of tensile strength and air permeability of frozen sand moulds (100-mes...Digital patternless freeze-casting technology is a new approach for obtaining frozen sand moulds using digital milling technology. The change law of tensile strength and air permeability of frozen sand moulds (100-mesh and 200-mesh silica sand, and zircon sand moulds) under different freezing temperatures and water contents was studied. Results show that with the decrease of freezing temperature and the increase of water contents, the tensile strength and air permeability of the sand moulds are gradually improved. Meanwhile, computed tomography technology was used to characterize the shape and size of the water film between the sand particles mixed with 4wt.% water. The results show that in silica sand moulds, the form of water film is lumpy, and 200-mesh silica sand moulds have more water films and higher proportion of small-sized water films than 100-mesh silica sand moulds, while in zircon sand moulds, the form of water film is membranous. At the same freezing temperature and water content, the tensile strength of zircon sand mould is the highest, and 100-mesh silica sand mould is the lowest. A comparative solidification experiment of A356 aluminum alloy was carried out in frozen sand mould and resin sand mould. The results show that the primary α-Al phase appears in the form of equiaxed and eutectic silicon phase is needle-like in freezing sand mould casting, but the primary α-Al phase grows in the form of dendrites, and the eutectic silicon phase is coarse needle-like in the resin sand mould casting. The difference of microstructure is caused by the different cooling rate. The cooling rate of A356 aluminum alloy in frozen sand mould is higher than that in resin sand mould.展开更多
In the present work,an attempt is made to partially replace high cost silica sand with sustainable eco-friendly cow-dung.The practical utility of cow dung as an additive material that facilitates binding in sand mould...In the present work,an attempt is made to partially replace high cost silica sand with sustainable eco-friendly cow-dung.The practical utility of cow dung as an additive material that facilitates binding in sand moulds has been tested.The Taguchi method is used to plan and conduct nine experiments with three replicates each.Pareto analysis of variance study is performed to understand the practical significance of moulding sand variables,that is,percentage of cow dung,clay,water,and degree of ramming on sand mould properties.The conflicting multiple objective functions(maximize mould hardness,and minimize collapsibility and gas evolution)are optimized by utilizing the Data Envelopment Analysis Ranking(DEAR)method.The optimal parameters i.e.6%of clay,4%of water,5%of cow-dung and 4 numbers of ramming strokes are obtained by applying a hybrid Taguchi-DEAR method.These parameters show the best moulding properties are:mould hardness 55,gas evolution 5.9 ml·g-1,and collapsibility 470 g·cm-2.Thereafter,a Lovejoy coupling made of aluminium is cast in the sand mould prepared with cow dung and without cow dung,with the optimum set of parameters.The mechanical properties,surface finish,and microstructure of the casting cast with cow-dung are better than that without cowdung.展开更多
This paper presents a technique for controlling the pressure of a molten metal when using a new type of iron casting method called sand mold press casting to realize high productivity and obtain high-quality products....This paper presents a technique for controlling the pressure of a molten metal when using a new type of iron casting method called sand mold press casting to realize high productivity and obtain high-quality products.The past test results using this method showed a casting yield of 90% to 95%,while conventional methods only show a casting yield of 60% to 70%.Although the press casting method does not require a sprue cup or runner channel casting defects such as metal penetration are often caused by the high pressure in the high-velocity pressing part of this casting process.Therefore,we proposed a pressure control method with a mathematical model of molten metal pressure,and with it we achieved experimental confirmation of the successful production of brake drums at different pressing temperatures.Results show that the proposed pressing control method can realize sound,penetration-free casting production.However,the theoretical analysis and design of this pressing process had not previously been studied sufficiently,and therefore this paper presents the theoretical design algorithm for the process as well as its experimental confirmation.展开更多
基金This work was financially supported by the National Science Found for Distinguished Young Scholars(No.51525503).
文摘Digital patternless freeze-casting technology is a new approach for obtaining frozen sand moulds using digital milling technology. The change law of tensile strength and air permeability of frozen sand moulds (100-mesh and 200-mesh silica sand, and zircon sand moulds) under different freezing temperatures and water contents was studied. Results show that with the decrease of freezing temperature and the increase of water contents, the tensile strength and air permeability of the sand moulds are gradually improved. Meanwhile, computed tomography technology was used to characterize the shape and size of the water film between the sand particles mixed with 4wt.% water. The results show that in silica sand moulds, the form of water film is lumpy, and 200-mesh silica sand moulds have more water films and higher proportion of small-sized water films than 100-mesh silica sand moulds, while in zircon sand moulds, the form of water film is membranous. At the same freezing temperature and water content, the tensile strength of zircon sand mould is the highest, and 100-mesh silica sand mould is the lowest. A comparative solidification experiment of A356 aluminum alloy was carried out in frozen sand mould and resin sand mould. The results show that the primary α-Al phase appears in the form of equiaxed and eutectic silicon phase is needle-like in freezing sand mould casting, but the primary α-Al phase grows in the form of dendrites, and the eutectic silicon phase is coarse needle-like in the resin sand mould casting. The difference of microstructure is caused by the different cooling rate. The cooling rate of A356 aluminum alloy in frozen sand mould is higher than that in resin sand mould.
文摘In the present work,an attempt is made to partially replace high cost silica sand with sustainable eco-friendly cow-dung.The practical utility of cow dung as an additive material that facilitates binding in sand moulds has been tested.The Taguchi method is used to plan and conduct nine experiments with three replicates each.Pareto analysis of variance study is performed to understand the practical significance of moulding sand variables,that is,percentage of cow dung,clay,water,and degree of ramming on sand mould properties.The conflicting multiple objective functions(maximize mould hardness,and minimize collapsibility and gas evolution)are optimized by utilizing the Data Envelopment Analysis Ranking(DEAR)method.The optimal parameters i.e.6%of clay,4%of water,5%of cow-dung and 4 numbers of ramming strokes are obtained by applying a hybrid Taguchi-DEAR method.These parameters show the best moulding properties are:mould hardness 55,gas evolution 5.9 ml·g-1,and collapsibility 470 g·cm-2.Thereafter,a Lovejoy coupling made of aluminium is cast in the sand mould prepared with cow dung and without cow dung,with the optimum set of parameters.The mechanical properties,surface finish,and microstructure of the casting cast with cow-dung are better than that without cowdung.
文摘This paper presents a technique for controlling the pressure of a molten metal when using a new type of iron casting method called sand mold press casting to realize high productivity and obtain high-quality products.The past test results using this method showed a casting yield of 90% to 95%,while conventional methods only show a casting yield of 60% to 70%.Although the press casting method does not require a sprue cup or runner channel casting defects such as metal penetration are often caused by the high pressure in the high-velocity pressing part of this casting process.Therefore,we proposed a pressure control method with a mathematical model of molten metal pressure,and with it we achieved experimental confirmation of the successful production of brake drums at different pressing temperatures.Results show that the proposed pressing control method can realize sound,penetration-free casting production.However,the theoretical analysis and design of this pressing process had not previously been studied sufficiently,and therefore this paper presents the theoretical design algorithm for the process as well as its experimental confirmation.