Secondary cooling technology for high-efficiency continuous billet-casting

The mathematical model of high-efficiency continuous billet casting was developed, incorporating the effective spraying water coefficient and the effective specific spraying water flowrate of secondary cooling. To realize uniform cooling in secondary cooling zones, the spraying cooling structure and the arrangement of nozzles were redesigned and optimized, and an additional spraying cooling zone was used. A new secondary cooling model of spraying water was built. It was found that the required spraying water flowrate of a cooling zone was related with the casting speed, the casting temperature, the compositions of liquid steel and the cooling water temperature of secondary cooling. The operation of the reformed caster proved that the spraying cooling structure and the new secondary cooling model were suitable, and the casting speed was greatly enhanced. The highest casting speed was （3.8 to 4.0） m/min for billet with a section of 150× 150 mm^2. The quality And the outout of the billet were imoroved, andthe economical benefit was heightened.

Numerical simulation on solidification behavior and structure of 38CrMoAl large round bloom using CAFE model

A coupled cellular automaton-finite element model was developed to simulate the solidification behavior and structure of 38CrMoAl large round bloom,in which mold electromagnetic stirring+final electromagnetic stirring was taken into consideration,under different superheat,casting speeds,and secondary cooling water flow.Industrial trials for infrared temperature measurement and macro etch experiments of the post-test round bloom samples were used to verify the simulated solidification structure and temperature field.The simulation results show that superheat and secondary cooling water flow have little influence on the surface temperature,center temperature,and center solid fraction while casting speed has a more obvious influence on solidification behavior.With the increase in the casting speed of 0.02 m min^(-1),the solidification position is prolonged by about 1.64 m.With the increasing specific water ratio by 0.02 L kg^(-1) each,the surface temperature of the secondary cooling zones decreases by about 18℃,and the solidification position shortens by about 0.11 m.As the superheat increases from 10 to 40℃,the ratio of the equiaxed crystal zone decreases from 35.98% to 23.98%.The casting speed and secondary cooling water flow increase the equiaxed crystal ratios of the large round bloom,but neither is significant,both being about 2%.