Separation of arsenic and antimony from dust with high content of arsenic by a selective sulfidation roasting process using sulfur

The separation of arsenic and antimony from dust with high content of arsenic was conducted via a selective sulfidation roasting process.The factors such as roasting temperature,roasting time,sulfur content and nitrogen flow rate were investigated using XRD,EPMA and SEM-EDS.In a certain range,the sulfur addition has an active effect on the arsenic volatilization because the solid solution phase（（Sb,As）2O3）in the dust can be destroyed after the Sb component in it being vulcanized to Sb2S3 and this generated As2O3 continues to volatile.In addition,an amorphization reaction between As2O（3 ）and Sb2O（3 ）is hindered through the sulfidation of Sb2O3,which is also beneficial to increasing arsenic volatilization rate.The results show that volatilization rates of arsenic and antimony reach 95.36%and only 9.07%,respectively,under the optimum condition of roasting temperature of 350℃,roasting time of 90 min,sulfur content of 22%and N2 flow rate of 70 m L/min.In addition,the antimony in the residues can be reclaimed through a reverberatory process.

Ultrasonic-enhanced selective sulfide precipitation of copper ions from copper smelting dust using monoclinic pyrrhotite

The sulfide passivation film produced on the surface seriously prevents further reaction in the process of using monoclinic pyrrhotite(MPr)to treat heavy metal ions in wastewater.Ultrasonic technology was introduced to assist MPr to recover the copper ions.XPS result proves that CuS products exist on the surface of MPr.XRD and SEM results show that the CuS on the particles’surface is stripped under ultrasonic condition.The kinetics results indicate that the reaction under both conventional and ultrasonic conditions conform to the Avrami model.The reaction process changes from diffusion control to chemical reaction control under the ultrasonic condition as the solid layer is stripped off.The presence of ultrasonic significantly reduces the acidity and temperature required for the reaction and enhances the utilization efficiency of MPr;by controlling the amount of MPr,the removal rates of copper and arsenic in copper smelting dust leachate exceed 99%and 95%,respectively.

Separation and recovery of copper in Cu-As-bearing copper electrorefining black slime by oxidation acid leaching and sulfide precipitation

A new hydrometallurgical route for separation and recovery of Cu from Cu-As-bearing copper electrorefining black slime was developed. The proposed process comprised oxidation acid leaching of Cu-As-bearing slime and selective sulfide precipitation of Cu from the leachate. The effects of various process parameters on the leaching and precipitation of Cu and As were investigated. At the first stage, Cu extraction of 95.2% and As extraction of 97.6% were obtained at 80 ℃ after 4 h with initial H2 SO4 concentration of 1.0 mol/L and liquid-to-solid ratio of 10 mL/g. In addition, the leaching kinetics of Cu and As was successfully reproduced by the Avrami model, and the apparent activation energies were found to be 33.6 and 35.1 kJ/mol for the Cu and As leaching reaction, respectively, suggesting a combination of chemical reaction and diffusion control. During the selective sulfide precipitation, about 99.4% Cu was recovered as CuS, while only 0.1% As was precipitated under the optimal conditions using sulfide-to-copper ratio of 2.4:1, time of 1.5 h and temperature of 25 ℃.

Improving gold recovery of Pb–Zn sulfide ore by selective activation with organic acid

Free gold and gold wrapped in sulfides are considered as the object of gold floatation. However,floatation of free gold exhibits more variables in practice.In this study, improving gold recovery of a Pb-Zn sulfide ore from Yunnan Province, China, was investigated. The results show that free gold and auriferous sulfides account for 94.99 % of total gold. Without adding organic acid in floatation, only 82 % recovery of gold could be obtained.Gold recovery in Au/Pb concentrates increases by 9.29 %with oxalate added and by 7.35 % with citric acid added,respectively, while performances of lead and arsenic nearly keep a constant. A possible reason is that free gold is of wonderful selectivity against pyrite with organic activators.A new method to enhance gold recovery is proposed.

CATALYTIC PROPERTIES OF NANOFIBROUS CARBON IN SELECTIVE OXIDATION OF HYDROGEN SULPHIDE

Nanofibrous carbonaceous materials （NFC） as a new class of materials having many applications, can catalyze the selective oxidation of H2S to sulfur. The correlation between NFC structure and its activity and selectivity in H2S oxidation was determined. It is demonstrated that selectivity can be improved if NFC with more ordered structure be synthesized and the portion of the original catalyst in carbon be reduced by increasing the carbon accumulated in the catalyst.