1.3μm InGaAs/InAs/GaAs Self-Assembled Quantum Dot Laser Diode Grown by Molecular Beam Epitaxy

The growth of multi-layer InGaAs/InAs/GaAs self-assembled quantum dots （QDs） by molecular beam epitaxy （MBE） is investigated,and a QD laser diode lasing at 1.33μm in continuous operation mode at room temperature is reported. The full width at half maximum of the band edge emitting peaks of the photoluminescence （PL） spectra at room temperature is less than 35meV for most of the multi-layer QD samples,revealing good,reproducible MBE growth conditions. Moreover,atomic force microscopy images show that the QD surface density can be controlled in the range from 1×10^10 to 7 ×10^10 cm^-2 . The best PL properties are obtained at a QD surface density of about 4×10^10cm^-2. Edge emitting lasers containing 3 and 5 stacked QD layers as the active layer lasing at room temperature in continuous wave operation mode are reported.

Kinetic Monte Carlo simulations of three-dimensional self-assembled quantum dot islands

By three-dimensional kinetic Monte Carlo simulations, the effects of the temperature, the flux rate, the total coverage and the interruption time on the distribution and the number of self-assembled InAs/GaAs （001） quantum dot （QD） islands are studied, which shows that a higher temperature, a lower flux rate and a longer growth time correspond to a better island distribution. The relations between the number of islands and the temperature and the flux rate are also successfully simulated. It is observed that for the total coverage lower than 0.5 ML, the number of islands decreases with the temperature increasing and other growth parameters fixed and the number of islands increases with the flux rate increasing when the deposition is lower than 0.6 ML and the other parameters are fixed.

Spatial weak-light ring soliton in self-assembled quantum dots

By using semiclassical theory combined with multiple-scale method, we analytically study the linear absorption and the nonlinear dynamical properties in a lifetime broadened Λ-type three-level self-assembled quantum dots. It is found that this system can exhibit the transparency, and the width of the transparency window becomes wider with the increase of control light field. Interestingly, a weak probe light beam can form spatial weak-light dark solitons. When it propagates along the axial direction, the soliton will transform into a steady spatial weak-light ring dark soltion. In addition, the stability of two-dimensional spatial optical solitons is testified numerically.

Quantum light source devices of In(Ga)As semiconductor self-assembled quantum dots

A brief introduction of semiconductor self-assembled quantum dots (QDs) applied in single-photon sources is given. Single QDs in confined quantum optical microcavity systems are reviewed along with their optical properties and coupling characteristics. Subsequently, the recent progresses in In(Ga)As QDs systems are summarized including the preparation of quantum light sources, multiple methods for embedding single QDs into different microcavities and the scalability of single-photon emitting wavelength. Particularly, several In(Ga)As QD single-photon devices are surveyed including In(Ga)As QDs coupling with nanowires, InAs QDs coupling with distributed Bragg reflection microcavity and the In(Ga)As QDs coupling with micropillar microcavities. Furthermore, applications in the field of single QDs technology are illustrated, such as the entangled photon emission by spontaneous parametric down conversion, the single-photon quantum storage, the chip preparation of single-photon sources as well as the single-photon resonance-fluorescence measurements.

SELF-ASSEMBLED QUANTUM DOTS ON AU AND THE INTERFACE FLUORESCENCE

In this paper,amino capped CdSe/ZnS quantum dots(QDs)were immobilized on the 11-mercaptoundecanoic acid(MUA)self-assembled Au surface(SAM/Au)by 1-ethyl-3-(3-dimethylaminopropyl)carbodiimide hydrochloride(EDC).Atomic force microscopy(AFM),fluorescence imaging and electrochemistry were employed to characterize the surface.The results showed that CdSe/ZnS QDs were immobilized on the surface of SAM/Au successfully.Based on this method,the fluorescence of the QDs on the SAM/Au was monitored on-line.

Distribution of Ge Self-Assembled Quantum Dots on Six Ge1 - x Buffer Layers

The effect of buried misfit dislocation on the distribution of Ge self-assembled quantum dots (SAQDs) grown on a relaxed SiGe buffer layer was investigated. The strain field of arrays of buried dislocations in a relaxed SiGe buffer layer provided preferential nucleation sites for quantum dots. Burgers vector analysis using plan-view transmission electron microscopy (TEM) verified that the preferential nucleation sites of Ge SAQDs depended on the Burgers vector direction of corresponding dislocations. The measurement of the lateral distance between SAQDs and dislocations together with crosssection TEM observation clarified that the location of SAQDs was at the intersection of the dislocation slip plane and the top surface. The misfit strain should be an additional factor governing the uniformity in size, shape and distribution of Ge SAQDs.

Molecular Dynamics Study on Mechanical Properties in the Structure of Self-Assembled Quantum Dot

Stress and strain in the structure of self-assembled quantum dots constructed in the Ge/Si(001) system is calculated by using molecular dynamics simulation. Pyramidal hut cluster composed of Ge crystal with {105} facets surfaces observed in the early growth stage are computationally modeled. We calculate atomic stress and strain in relaxed pyramidal structure. Atomic stress for triplet of atoms is approximately defined as an average value of pairwise (virial) quantity inside triplet, which is the product of vectors between each two atoms. Atomic strain by means of atomic strain measure (ASM) which is formulated on the Green’s definition of continuum strain. We find the stress (strain) relaxation in pyramidal structure and stress (strain) concentration in the edge of pyramidal structure. We discuss size dependency of stress and strain distribution in pyramidal structure. The relationship between hydrostatic stress and atomic volumetric strain is basically linear for all models, but for the surface of pyramidal structure and Ge-Si interface. This means that there is a reasonable correlation between atomic stress proposed in the present study and atomic strain measure, ASM.

Local Structure of Ge/Si(100) Self-Assembled Quantum Dots

Local structure of uncapped and Si capped Ge quantum dots grown on Si(100) has been probed by X ray absorption fine structure spectroscopy. It is found that the uncapped Ge dots are partially oxidized and partially alloyed with Si. The amount of Ge present in the Ge phase is found to be about 20 30%. In the Si capped sample, Ge is found to be dissolved in silicon, the fraction of Ge atoms existing as pure Ge phase being not more than 10%.

N-doped graphene quantum dot-decorated N-TiO2/P-doped porous hollow g-C_(3)N_(4) nanotube composite photocatalysts for antibiotic photodegradation and H2 production

Exclusive responsiveness to ultraviolet light (~3.2 eV) and high photogenerated charge recombination rate are the two primary drawbacks of pure TiO_(2). We combined N-doped graphene quantum dots (N-GQDs), morphology regulation, and heterojunction construction strategies to synthesize N-GQD/N-doped TiO_(2)/P-doped porous hollow g-C_(3)N_(4) nanotube (PCN) composite photocatalysts (denoted as G-TPCN). The optimal sample (G-TPCN doped with 0.1wt% N-GQD, denoted as 0.1% G-TPCN) exhibits significantly enhanced photoabsorption, which is attributed to the change in bandgap caused by elemental doping (P and N), the improved light-harvesting resulting from the tube structure, and the upconversion effect of N-GQDs. In addition, the internal charge separation and transfer capability of0.1% G-TPCN are dramatically boosted, and its carrier concentration is 3.7, 2.3, and 1.9 times that of N-TiO_(2), PCN, and N-TiO_(2)/PCN(TPCN-1), respectively. This phenomenon is attributed to the formation of Z-scheme heterojunction between N-TiO_(2) and PCNs, the excellent electron conduction ability of N-GQDs, and the short transfer distance caused by the porous nanotube structure. Compared with those of N-TiO_(2), PCNs, and TPCN-1, the H2 production activity of 0.1%G-TPCN under visible light is enhanced by 12.4, 2.3, and 1.4times, respectively, and its ciprofloxacin (CIP) degradation rate is increased by 7.9, 5.7, and 2.9 times, respectively. The optimized performance benefits from excellent photoresponsiveness and improved carrier separation and migration efficiencies. Finally, the photocatalytic mechanism of 0.1% G-TPCN and five possible degradation pathways of CIP are proposed. This study clarifies the mechanism of multiple modification strategies to synergistically improve the photocatalytic performance of 0.1% G-TPCN and provides a potential strategy for rationally designing novel photocatalysts for environmental remediation and solar energy conversion.

Threshold-independent method for single-shot readout of spin qubits in semiconductor quantum dots

The single-shot readout data process is essential for the realization of high-fidelity qubits and fault-tolerant quantum algorithms in semiconductor quantum dots. However, the fidelity and visibility of the readout process are sensitive to the choice of the thresholds and limited by the experimental hardware. By demonstrating the linear dependence between the measured spin state probabilities and readout visibilities along with dark counts, we describe an alternative threshold-independent method for the single-shot readout of spin qubits in semiconductor quantum dots. We can obtain the extrapolated spin state probabilities of the prepared probabilities of the excited spin state through the threshold-independent method. We then analyze the corresponding errors of the method, finding that errors of the extrapolated probabilities cannot be neglected with no constraints on the readout time and threshold voltage. Therefore, by limiting the readout time and threshold voltage, we ensure the accuracy of the extrapolated probability. We then prove that the efficiency and robustness of this method are 60 times larger than those of the most commonly used method. Moreover, we discuss the influence of the electron temperature on the effective area with a fixed external magnetic field and provide a preliminary demonstration for a single-shot readout of up to 0.7K/1.5T in the future.

Advantageous properties of halide perovskite quantum dots towards energy-efficient sustainable applications

As lead halide perovskite(LHP)semiconductors have shown tremendous promise in many application fields,and particularly made strong impact in the solar photovoltaic area,low dimensional quantum dot forms of these perovskites are showing the potential to make distinct marks in the fields of electronics,optoelectronics and photonics.The so-called perovskite quantum dots(PQDs)not only possess the most important features of LHP materials,i.e.,the unusual high defect tolerance,but also demonstrate clear quantum size effects,along with exhibiting desirable optoelectronic properties such as near perfect photoluminescent quantum yield,multiple exciton generation and slow hot-carrier cooling.Here,we review the advantageous properties of these nanoscale perovskites and survey the prospects for diverse applications which include lightemitting devices,solar cells,photocatalysts,lasers,detectors and memristors,emphasizing the distinct superiorities as well as the challenges.

Experimental and computational study of annealed nickel sulfide quantum dots for catalytic and antibacterial activity

This research investigates the hydrothermal synthesis and annealing duration effects on nickel sulfide(NiS_(2) quantum dots(QDs)for catalytic decolorization of methylene blue(MB)dye and antimicrobial efficacy.QD size increased with longer annealing,reducing catalytic activity.UV–vis,XRD,TEM,and FTIR analyses probed optical structural,morphological,and vibrational features.XRD confirmed NiS2's anorthic structure,with crystallite size growing from 6.53 to 7.81 nm during extended annealing.UV–Vis exhibited a bathochromic shift,reflecting reduced band gap energy(Eg)in NiS_(2).TEM revealed NiS_(2)QD formation,with agglomerated QD average size increasing from 7.13 to 9.65 nm with prolonged annealing.Pure NiS_(2) showed significant MB decolorization(89.85%)in acidic conditions.Annealed NiS_(2) QDs demonstrated notable antibacterial activity,yielding a 6.15mm inhibition zone against Escherichia coli(E.coli)compared to Ciprofloxacin.First-principles computation supported a robust interaction between MB and NiS_(2),evidenced by obtained adsorption energies.This study highlights the nuanced relationship between annealing duration,structural changes,and functional properties in NiS_(2)QDs,emphasizing their potential applications in catalysis and antibacterial interventions.

Coupling and characterization of a Si/SiGe triple quantum dot array with a microwave resonator

Scaling up spin qubits in silicon-based quantum dots is one of the pivotal challenges in achieving large-scale semiconductor quantum computation.To satisfy the connectivity requirements and reduce the lithographic complexity,utilizing the qubit array structure and the circuit quantum electrodynamics(cQED)architecture together is expected to be a feasible scaling scheme.A triple-quantum dot(TQD)coupled with a superconducting resonator is regarded as a basic cell to demonstrate this extension scheme.In this article,we investigate a system consisting of a silicon TQD and a high-impedance TiN coplanar waveguide(CPW)resonator.The TQD can couple to the resonator via the right double-quantum dot(RDQD),which reaches the strong coupling regime with a charge–photon coupling strength of g0/(2p)=175 MHz.Moreover,we illustrate the high tunability of the TQD through the characterization of stability diagrams,quadruple points(QPs),and the quantum cellular automata(QCA)process.Our results contribute to fostering the exploration of silicon-based qubit integration.

Coupling of BiOCl Ultrathin Nanosheets with Carbon Quantum Dots for Enhanced Photocatalytic Performance

Over the past few decades,photocatalysis technology has received extensive attention because of its potential to mitigate or solve energy and environmental pollution problems.Designing novel materials with outstanding photocatalytic activities has become a research hotspot in this field.In this study,we prepared a series of photocatalysts in which BiOCl nanosheets were modified with carbon quantum dots(CQDs)to form CQDs/BiOCl composites by using a simple solvothermal method.The photocatalytic performance of the resulting CQDs/BiOCl composite photocatalysts was assessed by rhodamine B and tetracycline degradation under visible-light irradiation.Compared with bare BiOCl,the photocatalytic activity of the CQDs/BiOCl composites was significantly enhanced,and the 5 wt%CQDs/BiOCl composite exhibited the highest photocatalytic activity with a degradation efficiency of 94.5%after 30 min of irradiation.Moreover,photocatalytic N_(2)reduction performance was significantly improved after introducing CQDs.The 5 wt%CQDs/BiOCl composite displayed the highest photocatalytic N_(2)reduction performance to yield NH_3(346.25μmol/(g h)),which is significantly higher than those of 3 wt%CQDs/BiOCl(256.04μmol/(g h)),7 wt%CQDs/BiOCl(254.07μmol/(g h)),and bare BiOCl(240.19μmol/(g h)).Our systematic characterizations revealed that the key role of CQDs in improving photocatalytic performance is due to their increased light harvesting capacity,remarkable electron transfer ability,and higher photocatalytic activity sites.

Effective Activation of Melamine for Synchronous Synthesis of Catalytically Active Nanosheets and Fluorescence-Responsive Quantum Dots

Because of the low reactivity of cyclic nitrides,liquid-phase synthesis of carbon nitride introduces challenges despite its favorable potential for energy-efficient preparation and superior applications.In this study,we demonstrate a strong interaction between citric acid and melamine through experimental observation and theoretical simulation,which eff ectively activates melamine-condensation activity and produces carbon-rich carbon nitride nanosheets(CCN NSs)during hydrothermal reaction.Under a large specific surface area and increased light absorption,these CCN NSs demonstrate significantly enhanced photocatalytic activity in CO_(2) reduction,increasing the CO production rate by approximately tenfold compared with hexagonal melamine(h-Me).Moreover,the product selectivity of CCN NSs reaches up to 93.5%to generate CO from CO_(2).Furthermore,the annealed CCN NSs exhibit a CO conversion rate of up to 95.30μmol/(g h),which indicates an 18-fold increase compared with traditional carbon nitride.During the CCN NS synthesis,nitrogen-doped carbon quantum dots(NDC QDs)are simultaneously produced and remain suspended in the supernatant after centrifugation.These QDs disperse well in water and exhibit excellent luminescent properties(QY=67.2%),allowing their application in the design of selective and sensitive sensors to detect pollutants such as pesticide 2,4-dichlorophenol with a detection limit of as low as 0.04μmol/L.Notably,the simultaneous synthesis of CCN NSs and NDC QDs provides a cost-eff ective and highly efficient process,yielding products with superior capabilities for catalytic conversion of CO_(2) and pollutant detection,respectively.

Paving continuous heat dissipation pathways for quantum dots in polymer with orangeinspired radially aligned UHMWPE fibers

Thermal management of nanoscale quantum dots(QDs)in light-emitting devices is a long-lasting challenge.The existing heat transfer reinforcement solutions for QDs-polymer composite mainly rely on thermal-conductive fillers.However,this strategy failed to deliver the QDs’heat generation across a long distance,and the accumulated heat still causes considerable temperature rise of QDs-polymer composite,which eventually menaces the performance and reliability of lightemitting devices.Inspired by the radially aligned fruit fibers in oranges,we proposed to eliminate this heat dissipation challenge by establishing long-range ordered heat transfer pathways within the QDs-polymer composite.Ultrahigh molecular weight polyethylene fibers(UPEF)were radially aligned throughout the polymer matrix,thus facilitating massive efficient heat dissipation of the QDs.Under a UPEF filling fraction of 24.46 vol%,the in-plane thermal conductivity of QDs-radially aligned UPEF composite(QDs-RAPE)could reach 10.45 W m^(−1) K^(−1),which is the highest value of QDs-polymer composite reported so far.As a proof of concept,the QDs’working temperature can be reduced by 342.5℃ when illuminated by a highly concentrated laser diode(LD)under driving current of 1000 mA,thus improving their optical performance.This work may pave a new way for next generation high-power QDs lighting applications.

Temperature-controlled DCP Fluorescent Probe Based on Hydrogel-immobilized Quantum Dots Composite

A composite was created by incorporating the quantum dot-enhanced SiO_(2)nanoparticles within this hydrogel.Based on this composite,a temperature-controlled fluorescent probe for DCP was developed.A meticulous examination of this probe revealed its attributes and factors affecting its performance.By using temperature modulation,the probe was adept at detecting DCP concentrations ranging between 1.0×10^(-6)and 9.0×10^(-6)mol/L.Such a probe offers remarkable selectivity,repeatability,and robust stability,so that the detection of DCP can be carried out at different temperatures,and a fast,reliable,sensitive and low-cost intelligent detection method is realized.

Majorana tunneling in a one-dimensional wire with non-Hermitian double quantum dots

The combination of non-Hermitian physics and Majorana fermions can give rise to new effects in quantum transport systems. In this work, we investigate the interplay of PT-symmetric complex potentials, Majorana tunneling and interdot tunneling in a non-Hermitian double quantum dots system. It is found that in the weak-coupling regime the Majorana tunneling has pronounced effects on the transport properties of such a system, manifested as splitting of the single peak into three and a reduced 1/4 peak in the transmission function. In the presence of the PT-symmetric complex potentials and interdot tunneling, the 1/4 central peak is robust against them, while the two side peaks are tuned by them. The interdot tunneling only induces asymmetry, instead of moving the conductance peak, due to the robustness of the Majorana modes. There is an exceptional point induced by the union of Majorana tunneling and interdot tunneling. With increased PT-symmetric complex potentials, the two side peaks will move towards each other. When the exceptional point is passed through, these two side peaks will disappear. In the strong-coupling regime, the Majorana fermion induces a 1/4 conductance dip instead of the three-peak structure. PT-symmetric complex potentials induce two conductance dips pinned at the exceptional point. These effects should be accessible in experiments.

NbN quantum dots anchored hollow carbon nanorods as efficient polysulfide immobilizer and lithium stabilizer for Li-S full batteries

The shuttle effect of lithium polysulfides(LiPSs)and uncontrollable lithium dendrite growth seriously hinder the practical application of lithium-sulfur(Li-S)batteries.To simultaneously address such issues,monodispersed Nb N quantum dots anchored on nitrogen-doped hollow carbon nanorods(NbN@NHCR)are elaborately developed as efficient Li PSs immobilizer and Li stabilizer for high-performance Li-S full batteries.Density functional theory(DFT)calculations and experimental characterizations demonstrate that the sulfiphilic and lithiophilic NbN@NHCR hybrid can not only efficiently immobilize the soluble Li PSs and facilitate diffusion-conversion kinetics for alleviating the shuttling effect,but also homogenize the distribution of Li+ions and regulate uniform Li deposition for suppressing Li-dendrite growth.As a result,the assembled Li-S full batteries(NbN@NHCR-S||Nb N@NHCR-Li)deliver excellent long-term cycling stability with a low decay rate of 0.031%per cycle over 1000 cycles at high rate of 2 C.Even at a high S loading of 5.8 mg cm^(-2)and a low electrolyte/sulfur ratio of 5.2μL mg^(-1),a large areal capacity of 6.2 mA h cm^(-2)can be achieved in Li-S pouch cell at 0.1 C.This study provides a new perspective via designing a dual-functional sulfiphilic and lithiophilic hybrid to address serious issues of the shuttle effect of S cathode and dendrite growth of Li anode.

Manipulation of internal blockage in triangular triple quantum dot

We utilize the calculation of hierarchical equations of motion to demonstrate that the spin-dependent properties between adjacent quantum dots(QDs)can be changed by breaking the internal symmetry configuration,corresponding to the inversion of dominant chiral states.In the linear triple quantum dots(LTQDs)connected to two electron reservoirs,we can observe that the blockage appears at the triangle triple quantum dots(TTQDs)by gradually increasing the coupling strength between next-nearest double QDs.When the initial coupling between LTQDs has altered,the internal chiral circulation also undergoes the corresponding transform,thus achieving qualitative regulation and detection of the blocking region.We also investigate the response of the chiral circulation to the dot–lead coupling strength,indicating the overall robust chiral circulation of the TTQDs frustration.