Fluorinated semi-interpenetrating polymer networks for enhancing the mechanical performance and storage stability of polymer-bonded explosives by controlling curing and phase separation rates

Herein, the effect of fluoropolymer binders on the properties of polymer-bonded explosives(PBXs) was comprehensively investigated. To this end, fluorinated semi-interpenetrating polymer networks(semiIPNs) were prepared using different catalyst amounts(denoted as F23-CLF-30-D). The involved curing and phase separation processes were monitored using Fourier-transform infrared spectroscopy, differential scanning calorimetry, a haze meter and a rheometer. Curing rate constant and activation energy were calculated using a theoretical model and numerical method, respectively. Results revealed that owing to its co-continuous micro-phase separation structure, the F23-CLF-30-D3 semi-IPN exhibited considerably higher tensile strength and elongation at break than pure fluororubber F2314 and the F23-CLF-30-D0 semi-IPN because the phase separation and curing rates matched in the initial stage of curing.An arc Brazilian test revealed that F23-CLF-30-D-based composites used as mock materials for PBXs exhibited excellent mechanical performance and storage stability. Thus, the matched curing and phase separation rates play a crucial role during the fabrication of high-performance semi-IPNs;these factors can be feasibly controlled using an appropriate catalyst amount.

Semi-Interpenetrating Novolac-Epoxy Thermoset Polymer Networks Derived from Plant Biomass

Bio-based phenol-formaldehyde polymer (BioNovolac) was developed by reacting molar excess of bio-oil/phenolwith formaldehyde in acidic medium. Glycidyl 3,5-diglycidoxybenzoate (GDGB), was prepared by directglycidylation of α-resorcylic acid (RA), a naturally occurring phenolic monomer. GDGB was crosslinked in thepresence of BioNovolac by anionic polymerization. Fourier transform infrared spectroscopy (FTIR) confirmedthe formation of semi-interpenetrating polymer networks. The glass transition temperature and moduli of biobasedcrosslinked systems were observed to increase with increasing GDGB content. Active chain density andmass retention measured by dynamic mechanical analysis (DMA) and Soxhlet extraction, respectively, indicated ahigh crosslink density of the cured networks. Scanning electron microscopy (SEM) images depicted thehomogeneity of the bulk phase. The preparation of bio-based epoxy-novolac thermoset network resulted inreduced consumption of petroleum-based chemicals.

Semi-interpenetrating network anion exchange membranes based on quaternized polyvinyl alcohol/poly(diallyldimethylammonium chloride)

The semi-interpenetrating network anion exchange membranes(AEMs)based on quaternized polyvinyl alcohol(QPVA)and poly(-diallyldimethylammonium chloride)(PDDA)are synthesized.The chemical cross-linking structure is formed between hydroxyl groups of QPVA and aldehyde groups of glutaraldehyde(GA),which makes PDDA more stable embed in the QPVA matrix and also improves the mechanical properties and dimensional stability of AEMs.Due to the phase separation phenomenon of AEMs swelling in water,a microporous structure may be formed in the membrane,which reduces the transmission resistance of hydroxide ions and provides a larger space for the transfer of hydroxide ions,thus improving the conductivity.The ring structure of PDDA is introduced as a cationic group to transfer hydroxide ions,and shields the nucleophilic attack of the hydroxide ions through the steric hindrance effect,which improves alkaline stability.The hydroxide conductivity of semi-interpenetrating network membrane(QPVA/PDDA0.5-GA)is 36.5 mS cm^(-1) at 60℃.And the membrane of QPVA/PDDA0.5-GA exhibits excellent mechanical property with maximum tensile strength of 19.6 MPa.After immersing into hot 3 mol L^(-1) NaOH solutions at 60℃ for 300 h,the OHconductivity remains 78%of its initial value.The semi-interpenetrating network AEMs with microporous structure exhibit good ionic conductivity,mechanical strength and alkaline durability.

Imidazolium group prompted alkaline anion-exchange membrane with high performance for efficient electrochemical CO_(2) conversion

Development of high-performance hydroxide-conductive membranes is a focus research subject owing to promising applications in electrochemical reduction of CO_(2)(eCO_(2)RR).However,few satisfactory membranes have been developed to maximize the performance of CO_(2) electrolyzers,despite its role as the core in regulating ion transport and preventing product crossover or fuel loss.Herein,we report the synthesis of alkaline anion-exchange membranes fabricated by poly(vinyl-alcohol)(PVA)and poly[(3-methyl-1-vinylimidazoliummethylsulfate)-co-(1-vinylpyrrolidone)](PQ44)for use in CO_(2) electrolysis.Owing to the unique imidazolium ring structure coupled with a three-dimensional semiinterpenetrating porous internal architecture,the PVA/PQ44-OH-membranes provide a high hydroxide conductivity(21.47 mS cm^(-1)),preferable mechanical property and thermal stability.In particular,the eCO_(2)RR used PVA/PQ44-OH^(-) as electrolyte membrane realized a charming Faradaic efficiency(88%)and partial current density(29 mA cm^(-2))at0.96 VRHE and,delivered the excellent durability over 20 h electrolysis in 0.5 mol L^(-1) KHCO_(3) electrolyte.Notably,it can even enable an ultrahigh current density beyond 100 mA cm^(-2) at^(-1).11 VRHE when the electrolyte was KOH instead,and produced the FEHCOOof 85%at a low potential of0.81 VRHE,superior to both commercial alkaline A201 and acidic Nafion117 membrane.

Tough Semi-interpenetrating Polyvinylpyrrolidone/Polyacrylamide Hydrogels Enabled by Bioinspired Hydrogen-bonding Induced Phase Separation

Semi-interpenetrating(semi-IPN)hydrogels formed by the continuous interpenetration of cross-linked polymer network and linear non-crosslinked polymer with multifunctionality are widely used in biomedical and other fields.However,the negative impact of linear polymer on the homogeneity of the cross-linked network often leads to a decrease in the mechanical properties of semi-IPN hydrogels and severely limits their applications.Herein,a bioinspired hydrogen-bonding induced phase separation strategy is presented to construct the tough semi-IPN polyvinylpyrrolidone/polyacrylamide hydrogels(named PVP/PAM hydrogels),including the linear polymer polyvinylpyrrolidone(PVP)and cross-linked polyacrylamide(PAM)network.The resultant PVPx/PAM hydrogels exhibit unique phase separation induced by the hydrogen bonding between PVP and PAM and affected by the amount of substance of PVP.Meanwhile,the phase separation of PVPx/PAM hydrogels results in excellent mechanical properties with a strain of 2590%,tensile strength of 0.28 MPa and toughness of 2.17 MJ/m^(3).More importantly,the hydrogen bonding between PVP and PAM firstly disrupts to dissipate energy under external forces,so the PVPx/PAM hydrogels exhibit good self-recovery properties and outperform chemically cross-linked PAM hydrogels in impact resistance and damping applications.It is believed that the PVPx/PAM hydrogels with hydrogen-bonding induced phase separation possess more potential application prospects.

Anion exchange membranes with a semi-interpenetrating polymer network using 1,6-dibromohexane as bifunctional crosslinker

An anion exchange membrane(AEM)is generally expected to possess high ion exchange capacity(IEC),low water uptake(WU),and high mechanical strength when applied to electrodialysis desalination.Among different types of AEMs,semi-interpenetrating polymer networks(SIPNs)have been suggested for their structural superiorities,i.e.,the tunable local density of ion exchange groups for IEC and the restrained leaching of hygroscopic groups by insolubility for WU.Unfortunately,the conventional SIPN AEMs still struggle to balances IEC,WU,and mechanical strength simultaneously,due to the lack of the compact crosslinking region.In this work,we proposed a novel SIPN structure of polyvinylidene difluoride/polyvinylimidazole/1,6-dibromohexane(PVDF/PVIm/DBH).On the one hand,DBH with two cationic groups of imidazole groups are introduced to enhance the ion conductivity,which is different from the conventional monofunctional modifier with only one cationic group.On the other hand,DBH has the ability to bridge with PVIm,where the mechanical strength of the resulting AEM is increased by the increase of crosslinking degree.Results show that a low WU of 38.1%to 62.6%,high IEC of 2.12—2.22 mmol·g^(-1),and excellent tensile strength of 3.54—12.35 MPa for PVDF/PVIm/DBH membrane are achieved.This work opens a new avenue for achieving the high-quality AEMs.

Cell Growth and Desorption on the Surface of Temperature-sensitive Semi-IPNs Hydrogels Based on Silk Sericin

Semi-interpenetrating （semi-IPNs） hydrogels containing biocompatible silk sericin （SS） and poly（N-isopropylacrylamide）（PNIPAM） were prepared as novel cellular matrices. Their maximum swelling degree and basic characteristics for biomedical applications such as mouse ？broblasts （L929） cell proliferation and desorption were investigated. The results showed that the incorporation of high hydrophilic SS into PNIPAM hydrogel increased the maximum swelling degree of the semi-IPNs hydrogels, and the adhesion and growth of the L929 on semi-IPNs hydrogels were at least comparable to, or even better than, that on conventional PNIPAM hydrogel. In addition, L929 cells were found to detach from the hydrogels surface naturally by controlling environmental temperature. These results suggest great potential of semi-IPNs hydrogels in tissue engineering.

Novel Semi-IPN Gel Electrolyte for Polymer Lithium-ion Battery

A new type of semi-IPN gel electrolyte was prepared by thermal polymerization in this article.The cross-linked PEG200 (MXPEG) was prepared by condensation reaction in the presence of methacryloxypropyltrimethoxysilane (MAPTMS),the condensation product was then blent with PMMA and polymerized to form polymer blends with semi-IPN fabric.Differential scanning calorimetry and X-ray diffraction spectroscopy were used to investigate the thermal transition behavior of the polymer blends prepared.Ion-conducting behaviors and the electrochemical stability window for semi-IPN gel electrolyte were investigated by means ofimpedance spectroscopy and linear sweep voltammetry.The Arrhenius-type relationship was observed in the temperature dependence ofionic conductivity.All the properties shows that the prepared semi-IPN gel electrolyte possesses certain levels of electrolye salt and plasticizer were expected to have applications of gel polymer electrolyte for lithium polymer secondary batteries.

Swelling Behaviors of Polyaniline-Poly(Acrylic Acid) Hydrogels

Using poly（acrylic acid） （PAA） aqueous solution, NaOH aqueous solution, aniline （An） and ammonium persulfate （APS）, PAn-PAA hydrogels with a semi-interpenetrating structure connected by physical interlocks, chemical ion bonds and hydrogen bonds were prepared. The swelling properties of the hydrogels in solutions of different pH values （adjusted by adding NaOH or HCI） were studied. All the hydrogels prepared have similar swelling curves （the curves of equilibrium swelling ratio vs. pH value） and reach their maximum swelling at pH of 8 - 10. The maximum swelling ratio of the hydrogels is dependent on composition, including molecular weight of PAA, polymer content of the hydrogel, and molar ratios of AA to An, APS to An, and NaOH to AA, And the compositional dependence of the swelling capacity of PAn-PAA hydrogels was also studied.

A self-standing,UV-cured semi-interpenetrating polymer network reinforced composite gel electrolytes for dendrite-suppressing lithium ion batteries

A self-standing,flexible and lithium dendrite growth-suppressing composite gel polymer electrolyte membrane was designed for the use of room-temperature lithium ion batteries.The multi-functional composite semi-interpenetrating polymer network(referred to as“Cs-IPN”)electrolyte membrane was fabricated by combining a UV-cured ethoxylated trimethylolpropane triacrylate(ETPTA)macromer with alumina nanoparticles in the presence of liquid electrolyte and thermoplastic linear poly(ethylene oxide)(PEO).The polymer electrolyte membrane exhibits a semi-interpenetrating polymer network structure and a higher room temperature ionic conductivity,which impart the electrolyte with a significant cycling(120 mAh g^(-1)after 200 cycles)and a remarkable rate(137 mAh g^(-1)at 0.1℃,130 mAh g^(-1)at 0.5℃,119 mAh g^(-1)at 1℃ and 100 mAh g^(-1)at 2℃)performance in Li/LiFePO4 battery.More importantly,the polymer electrolyte possesses superior ability to inhibit the growth of lithium dendrites,which makes it promising for next generation lithium ion batteries.

Semi-interpenetrating polymer networks toward sulfonated poly(ether ether ketone) membranes for high concentration direct methanol fuel cell

Low methanol permeability of proton exchange membranes (PEMs) is greatly important for direct methanol fuel cells (DMFCs). Here, sulfonated poly (ether ether ketone) (SPEEK) based semiinterpenetrating polymer networks (semi-IPNs) are successfully prepared by interpenetrating SPEEK into the in-situ synthesized crosslinking networks. The polymeric networks are formed by the covalent bonds between bromobenzyl groups of bro mo methylated poly (phenylene oxide) and amine groups of diamine linkers as well as the ionic bonds between amine species and sulfonated groups. Two linkers without and with sulfonated groups are applied to fabricate the semi-IPNs. The core properties of the membranes, like phase separation, water uptake, proton conductivity and methanol permeability, are systematically studied and compared. The DMFCs assembled by using the semi-IPN membranes display better performance than Nafion 117 in high concentration methanol solutions. The present work provides a facile way to prepare PEMs with enhanced DMFC performance.