Microstructural characteristics of near-liquidus cast AZ91D alloy during semi-solid die casting

Near-liquidus cast ingot was reheated to semi-solid firstly, and then a bracket of motor was prepared by die casting the semi-solid ingot into mould. The microstructural characteristics of AZ91D alloy in these processes were investigated. In the process of near-liquidus casting, primary α-Mg grains tend to be rosette-like because of the increase of plentiful quasi-solid atom clusters in molten alloy with the decrease of pouring temperature. These rosette-like α-Mg grains in ingots fabricated by near-liquidus casting are fused off and refined into near-globular structure owing to the solute diffusion mechanism and the minimum surface energy mechanism during reheating. After semi-solid die-casting, α-Mg grains, located in biscuit, impact and connect with each other; α-Mg grains, located in inner gate, congregate together; while α-Mg grains, located in component, distribute uniformly and become into globularity or strip. Because the inner gate limits the flowing of semi-solid slurry, and the pressure acted on the semi-solid slurry decreases gradually along the filling direction of semi-solid slurry in cavity, microstructural segregation of unmelted α-Mg grains appears along this direction. Shrinkage holes in casting are caused by two different reasons. For biscuit, the shrinkage holes are caused by the blocked access of feeding liquid to the shrinkage zone for the agglomerated unmelted α-Mg grains. For component, the shrinkage holes are caused by the lack of feeding of liquid alloy.

Feasibility of semi-solid die casting of ADC12 aluminum alloy

The feasibility of semi-solid die casting of ADC12 aluminum alloy was studied.The effects of plunger speed, gate thickness, and solid fraction of the slurry on the defects were determined.The defects investigated are gas and shrinkage porosity.In the experiments, semi-solid slurry was prepared by the gas-induced semi-solid (GISS) technique.Then, the slurry was transferred to the shot sleeve and injected into the die.The die and shot sleeve temperatures were kept at 180 °C and 250 °C, respectively.The results show that the samples produced by the GISS die casting give little porosity, no blister and uniform microstructure.From all the results, it can be concluded that the GISS process is feasible to apply in the ADC12 aluminum die casting process.In addition, the GISS process can give improved properties such as decreased porosity and increased microstructure uniformity.

Strengthening technology and mechanism for semi-solid die casting of aluminum alloy

Combined with theoretical evaluation, an optimized strengthening process for the semi-solid die castings of A356 aluminum alloy was obtained by studying the mechanical properties of castings solution treated and aged under different conditions in detail, then, the semi-solid die castings and liquid die castings were heat treated with the optimized process. The results show that the mechanical properties of semi-solid die castings of aluminum alloy are superior to those of the liquid die castings, especially the strengthening degree of heat treated semi-solid die castings is much greater than that of liquid die castings with the tensile strength more than 330 MPa and the elongation more than 10%, and this is mainly contributed to the non-dendritic and more compact microstructure of semi-solid die castings. The strengthening mechanism of heat treatment for the semi-solid die castings of A356 aluminum alloy is due to the dispersive precipitation of the second phase（Mg2Si） and formation of GP Zone.

Forming conditions of blisters during solution heat treatment of Al–Si alloy semi-solid die castings

In the present study,numerical simulation method was used to analyze the conditions,resulting in the formation of blisters during solution heat treatment.Blister formation is considered to occur as the height of blister reaches 5μm.The effects of process parameters on the magnitude of the forming temperatures of blister(Tb)were discussed.Two kinds of Al-Si alloys were used to analyze the effect of mechanical properties of the alloys on blister forming conditions.Simulation results show that decreasing the initial pressure in gas hole,the long-short axial ratio of gas hole and the size of gas hole,as well as increasing the depth of gas hole and the strength of alloy are helpful to increase the critical temperature of forming blister.These conclusions are helpful for casters to understand the conditions controlling blister formation during solution heat treatment and take actions to avoid the blister defects.

Compression properties of cost-efficient porous expanded clay reinforced AA7075 syntactic foams fabricated by industrial-oriented die casting technology

In today’s manufacturing industries,hard competition between rival firms makes it compulsory for researchers to design lighter and cheaper machine components due to the megatrends of cost-effectiveness and anti-pollution.At this point,aluminum syntactic foams(ASFs)are new-generation engineering composites and come into the upfront as a problem-solver.Owing to their features like low density,sufficient elongation,and perfect energy absorption ability,these advanced foams have been considerably seductive for many industrial sectors nowadays.In this study,an industrial-oriented automatic die casting technology was used for the first time to manufacture the combination of AA7075/porous expanded clay(PEC).Micro evaluations(optical and FESEM)reveal that there is a homogenous particle distribution in the foam samples,and inspections are compatible with the other ASF studies.Additionally,T6 aging heat treatment was operated on one half of the produced foams to explore the probable impact of aging on the compressive responses.Attained results show that PEC particles can be an alternative to expensive hollow spheres used in the previous works.Besides,a favorable relationship is ascertained between the aging treatment and mechanical properties such as compression strength and plateau strength.

To improve robustness of mechanical properties of semi-solid cast A356 alloy using taguchi design method

Mechanical properties of semi-solid casting are dependent on multiple processing parameters,and improper processing parameters will not only reduce mean data but also increase variations.The present study investigated the impact of parameters in slurry preparation and heat treatment on the yield strength and ductility of T6 heat-treated A356 Al-Si alloy using rapid slurry forming(RSF)semi-solid casting.The focus was primarily on the robustness of mechanical properties based on Taguchi design method.By analyzing signal-to-noise ratio and minimum value calculated from-3S,the optimum slurry preparation parameters and heat treatment parameters were determined to be no quench,enthalpy exchange material(EEM)temperature of 140℃,EEM-to-melt ratio of 6mass%,stirring time of 18 s,solution heat treated at 520℃ for 2 h,and ageing heat treated at 190℃ for 6 h.In a small batch validation,the-3S yield strength and-3S elongation reach 256.1 MPa and 5.03% respectively,showing a satisfactory robustness.The hardness and microstructure of heat-treated samples with the best and worst properties were characterized to gain insight into the underlying mechanisms affecting the mean value and variations of mechanical properties.

Effect of slow shot speed on externally solidified crystal,porosity and tensile property in a newly developed high-pressure die-cast Al-Si alloy

The effect of slow shot speed on externally solidified crystal(ESC),porosity and tensile property in a newly developed high-pressure die-cast Al-Si alloy was investigated by optical microscopy(OM),scanning electron microscopy(SEM)and laboratory computed tomography(CT).Results showed that the newly developed AlSi9MnMoV alloy exhibited improved mechanical properties when compared to the AlSi10MnMg alloy.The AlSi9MnMoV alloy,which was designed with trace multicomponent additions,displays a notable grain refining effect in comparison to the AlSi10MnMg alloy.Refining elements Ti,Zr,V,Nb,B promote heterogeneous nucleation and reduce the grain size of primaryα-Al.At a lower slow shot speed,the large ESCs are easier to form and gather,developing into the dendrite net and net-shrinkage.With an increase in slow shot speed,the size and number of ESCs and porosities significantly reduce.In addition,the distribution of ESCs is more dispersed and the net-shrinkage disappears.The tensile property is greatly improved by adopting a higher slow shot speed.The ultimate tensile strength is enhanced from 260.31 MPa to 290.31 MPa(increased by 11.52%),and the elongation is enhanced from 3.72%to 6.34%(increased by 70.52%).

Effects of magnesium and copper additions on tensile properties of Al-Si-Cr die casting alloy under as-cast and T5 conditions

Aluminum high pressure die casting(HPDC)technology has evolved in the past decades,enabling stronger and larger one-piece casting with significant part consolidation.It also offers a higher design freedom for more mass-efficient thin-walled body structures.For body structures that require excellent ductility and fracture toughness to be joined with steel sheet via self-piercing riveting(for instance,shock towers and hinge pillars,etc.),a costly T7 heat treatment comprising a solution heat treatment at elevated temperatures(450℃-500℃)followed by an over-ageing heat treatment is needed to optimize microstructure for meeting product requirement.To enable cost-efficient mass production of HPDC body structures,it is important to eliminate the expensive T7 heat treatment without sacrificing mechanical properties.Optimizing die cast alloy chemistry is a potential solution to improve fracture toughness and ductility of the HPDC components.The present study intends to tailor the Mg and Cu additions for a new Al-Si-Cr type die casting alloy(registered as A379 with The Aluminum Association,USA)to achieve the desired tensile properties without using T7 heat treatment.It was found that Cu addition should be avoided,as it is not effective in enhancing strength while degrades tensile ductility.Mg addition is very effective in improving strength and has minor impact on tensile ductility.The investigated Al-Si-Cr alloy with a nominal composition of Al-8.5wt.%Si-0.3wt.%Cr-0.2wt.%Fe shows comparable tensile properties with the T7 treated AlSi10MnMg alloy which is currently used for manufacturing shock towers and hinge pillars.

Microstructure characteristics and thermodynamic properties of A357-SiCp/A357 layered composites prepared by semi-solid vacuum stirring suction casting

A357-SiCp/A357 layered composites were prepared using a semi-solid vacuum stirring suction casting method.The microstructures,mechanical properties,and thermal conductivities of the composites fabricated under different suction casting processes were compared.Additionally,the microstructural evolution characteristics and performance enhancement mechanism of the A357-SiCp/A357 layered composites were discussed.The results demonstrate that suction casting at 610°C with a low solid phase ratio can significantly enhance the material density and reduce the agglomeration of SiCp.The A357-SiC_(p)/A357 interface is clear and straight with good bonding.With an increase in the suction casting temperature,the bending resistance and thermal conductivity of the A357-SiC_(p)/A357 layered composites exhibit a trend of significantly increase at first and then slowly decrease owing to casting defects,interface bonding,and SiCp distribution.Compared with SiCp/A357 composites,the bending strength,deflection,and thermal conductivity of the A357-SiCp/A357 layered composites increase from 257 MPa,1.07 mm,and 155.72 W·(m·K)^(-1) to 298 MPa,2.1 mm,and 169.86 W·(m·K)^(-1),respectively.This study provides a reference for improving the rheological casting of aluminum matrix layered composites.

Performance of Semi-solid Slurry Produced by Twin-screw Stirring Mixer and Rheo-diecasting Process of AZ91D Alloy

The microstructure of semi-solid slurry of AZ91D alloy, which was produced by twin-screw stirring mixer under the different parameters, was investigated.Rheoforming by cold chamber die casting process was performed thereafter. The results indicate that with decreasing of the barrel temperature of the mixer and the pouring temperature of molten Mg alloy, the solid fraction of semi-solid slurry increases and the size of non-dendritic grains becomes smaller. While the shear rate increases, the solid fraction of semi-solid slurry decreases. The tensile strength and elongation of metal rheoformed by die casting are higher by about 37% and 44% respectively than those produced by conventional liquid die casting.

Gating system optimization of high pressure die casting thin-wall AlSi10MnMg longitudinal loadbearing beam based on numerical simulation

High pressure die casting(HPDC) is a kind of near net shape manufacturing method. However, air entrapment in HPDC parts has serious effects upon the casting quality. In order to reduce the air entrapment defects in a AlSi10 MnMg alloy thin-wall longitudinal load-bearing beam produced by HPDC, different gating systems were designed and simulated by software Flow-3D to evaluate the entrapped air. Simulation results showed that when the beam is produced by the original designed gating system with a middle ingate, there exist obvious air entrapments in the critical area; the volume of air entrapment was reduced by replacing the middle ingate to an overflow well, and the filling of molten metal became more stable. When the middle ingate was removed for further improvement, the volume of air entrapment was decreased drastically. The parts with glossy surface and good microstructure have been successfully produced by using the final optimized gating system based on simulation results.

Finite element analysis for die casting parameters in high-pressure die casting process

The gating system and the overflow system were designed according to the casting structure during high pressure die casting(HPDC) process. The simulation was carried out by ProCAST software to visualize the injection chamber pre-crystallization and the flow of molten metal. The main work is to research four die casting process parameters, i.e. injection temperature, low-pressure velocity, high-and low-pressure velocity’s switching position, and high-pressure velocity. Experimental results show that the higher injection temperature and lowpressure velocity can mitigate the pre-crystallization of the injection chamber. However, when the low-pressure velocity exceeds 0.2 m·s-1, the air entrapment in the chamber occurs. Besides, when the high-pressure velocity is greater than 2.5 m·s-1, the overflow channel at the final filling position is covered by the liquid metal too early. Finally, the injection temperature of 650 °C, the low-pressure velocity of 0.2 m·s-1, the high-and low-pressure velocity’s switching position of 320 mm and the high-pressure velocity of 2 m·s-1 are obtained as the optimal parameters by the software simulation, which has been verified by actual production.

Semi-solid rheocasting of grain refined aluminum alloy 7075

Near-net shape rheocasting with the Council for Scientific and Industrial Research Rheo casting system(CSIR-RCS) and a high pressure die casting machine was successfully performed on Al-5Ti-1B grain refined aluminum alloy 7075.Grain refinement levels used were 0.03% Ti,0.13% Ti and 0.29% Ti(mass fraction).Tensile tests reveal that the ultimate tensile strengths,at all levels of grain refinement,are at least 97% of the specified minimum.Elongation at fracture increases with the increase of level of grain refinement although a maximum elongation is only 76% of the required minimum elongation in the case of 0.29% Ti.Incipient melting,during solution treatment,of the low melting point multinary eutectic causes porosity in the material and accounts for poor elongation results.0.03% Ti has a coarse eutectic structure forming larger pores while 0.29% Ti has a fine structure forming fine pores in the multinary eutectic.The 0.2% offset yield strengths of all the grain refinement levels are at least equal to or above the specified minimum and a decrease is observed with the increase of grain refinement level.There is a clear reduction in grain size from 0.03% Ti to 0.29% Ti in the as-cast condition.An underlying grain structure develops in the T6 condition material which has an inverse size to the as-cast structure;coarse grained as-cast material results in fine grained T6 condition material after solution heat treatment.The decrease in the offset yield strength as grain refinement increases correlates very strongly with the T6 grain sizes according to a Hall-Petch type relationship.

Determination of interfacial heat transfer coefficient and its application in high pressure die casting process

In this paper,the research progress of the interfacial heat transfer in high pressure die casting(HPDC)is reviewed.Results including determination of the interfacial heat transfer coefficient(IHTC),influence of casting thickness,process parameters and casting alloys on the IHTC are summarized and discussed.A thermal boundary condition model was developed based on the two correlations:(a)IHTC and casting solid fraction and(b)IHTC peak value and initial die surface temperature.The boundary model was then applied during the determination of the temperature field in HPDC and excellent agreement was found.

Interfacial heat transfer behavior at metal/die in finger-plated casting during high pressure die casting process

Heat transfer at the metal-die interface has a great influence on the solidification process and casting structure. As thin-wall components are extensively produced by high pressure die casting process(HPDC), the B390 alloy finger-plate casting was cast against an H13 steel die on a cold-chamber HPDC machine. The interfacial heat transfer behavior at different positions of the die was carefully studied using an inverse approach based on the temperature measurements inside the die. Furthermore, the filling process and the solidification rate in different finger-plates were also given to explain the distribution of interfacial heat flux(q) and interfacial heat transfer coefficient(h). Measurement results at the side of sprue indicates that qmax and hmax could reach 9.2 MW·m^(-2) and 64.3 kW ·m^(-2)·K^(-1), respectively. The simulation of melt flow in the die reveals that the thinnest(T_1) finger plate could accelerate the melt flow from 50 m·s^(-1) to 110 m·s^(-1). Due to this high velocity, the interfacial heat flux at the end of T_1 could firstly reach a highest value 7.92 MW·m^(-2) among the ends of T_n(n=2,3,4,5). In addition, the q_(max) and h_(max) values of T_2, T_4 and T_5 finger-plates increase with the increasing thickness of the finger plate. Finally, at the rapid decreasing stage of interfacial heat transfer coefficient(h), the decreasing rate of h has an exponential relationship with the increasing rate of solid fraction(f).

Die Casting Mold Design of the Thin-walled Aluminum Case by Computational Solidification Simulation

Recently, demand for the lightweight alloy in electric/electronic housings has been greatly increased. However, among the lightweight alloys, aluminum alloy thin-walled die casting is problematic because it is quite difficult to achieve sufficient fluidity and feedability to fill the thin cavity as the wall thickness becomes less than 1mm. Therefore, in this study, thin-walled die casting of aluminum （Al-Si-Cu alloy： ALDC 12） in size of notebook computer housing and thickness of 0.8 mm was investigated by solidification simulation （MAGMA soft） and actual casting experiment （Buhler Evolution B 53D）. Three different types of gating design, finger, tangential and split type with 6 vertical runners, were simulated and the results showed that sound thin-walled die casting was possible with tangential and split type gating design because those gates allowed aluminum melt to flow into the thin cavity uniformly and split type gating system was preferable gating design comparing to tangential type gating system at the point of view of soundness of casting and distortion generated after solidification. Also, the solidification simulation agreed well with the actual die-casting and the casting showed no casting defects and distortion.

Design and Verification of an Auxiliary System for High Vacuum Die Casting

Vacuum die casting is the optimal method to produce high quality aluminum alloy components.At present,there are still very few systematic studies on vacuum die casting theory and equipment design.On the basis of the existing theories of the vacuum die casting pumping and venting systems,a simplified model is established in this research.The model has an aggregate unit consisted of ＂vacuum pump ＋ buffer tank＂ and a cylindrical container（including the shot sleeve,cavity and exhaust channel）.The theoretical analysis is carried out between the cavity pressure and the pumping time under different volume models.An auxiliary system for high vacuum die casting is designed based on the above analysis.This system is composed of a vacuum control machine and a new vacuum stop valve.The machine has a human-computer control mode with ＂programmable logic controller（PLC） ＋ touch screen＂ and a real-time monitoring function of vacuum degree for buffer tank and die cavity.The vacuum stop valve with the ＂compressed gas ＋ piston rod ＋ labyrinth groove＂ structure can realize the function of whole-process vacuum venting.The new system shows great advantages on vacuuming the cavity with a much faster speed by making tests on an existing die casting mold and a 250 t die casting machine.A die cavity pressure less than 10 kPa can be reached within 0.8 s in the experiment and the porosity of castings can be greatly decreased.The systematic studies on vacuum die casting theory and equipment have a great guiding significance for high vacuum die casting,and can also be applied to other high vacuum forming in related theoretical and practical research.

LOW CYCLE FATIGUE BEHAVIOR OF AZ91HP ALLOY IN AS HIGHP RESSURE DIE CASTING

Fully reversed total strain-controlled low-cycle fatigue tests were conducted at room temperature in air to study the fatigue behavior of AZ91HP magnesium alloy in as high pressure die casting and subsequently heat treatment. All the specimens in different heat histories exhibit cyclic strain hardening in different degrees. It is difficult to distinguish the fatigue behavior of the die casting specimens from that of the solution aging specimens. The solution treated specimens show longer fatigue life at high strain amplitude and shorter fatigue life at low strain amplitude than the die casting and solution aging specimens though they have the lowest yield strength with higher strain hardening. Fatigue fracture surfaces for strain amplitude larger than 0.005 show very similar to those found by monotonic tensile tests. The SEM examination reveals that the regions of fatigue crack growth and final fracture can be characterized by quasi-cleavage mechanisms, but some shallow dimples, slip bands and secondary cracks are found on the fracture surface in the fracture crack growth areas.

Effect of heat treatment on microstructure and properties of semi-solid squeeze casting AZ91D

Semi-solid AZ91D magnesium alloy billets were prepared by near-liquidus heat holding.Semi-solid squeeze casting was conducted at 575,585 and 595℃,respectively,with 1 mm·s^-1 squeeze speed.The semisolid squeeze casting AZ91D samples were heat treated by T4(solution at 415℃for 24 h)and T6(solution at 415℃for 24 h+220℃for 8 h)processes,respectively.The microstructure and mechanical properties of the alloy in different states were investigated by means of OM,SEM and tensile testing machine.The results show that compared to as-cast alloy,the grain size of the semi-solid squeezed AZ91D decreased significantly,and with the increase of semi-solid squeeze temperature,the grain size of AZ91D increased.The grains of the alloy were refined by T4 treatment,and further refined by T6 treatment.T6 treatment greatly improved the tensile strength,elongation,and hardness,but did not significantly improve yield strength.After 575℃squeeze casting and T6 treatment,the ultimate tensile strength(UTS)reached 285 MPa,the elongation reached 13.36%,and the hardness also reached the maximum(106.8 HV),but the yield strength(YS)was only 180 MPa.During the process of semi-solid squeeze casting and heat treatment,the matrix grain was refined and a large number of precipitated and secondary precipitated phases of Mg17Al12 appeared.Both the average size of matrix grain and secondary precipitated phase decreased,while the volume fraction of secondary precipitated phase increased.All these resulted in high tensile strength,elongation and hardness.