Effect of isothermal heat treatment on semi-solid microstructure of AZ91D magnesium alloy containing rare earth Gd

The AZ91 D magnesium alloy containing rare earth Gd was prepared in this study, and the effect of semi-solid isothermal heat treatment on the microstructure of the alloy was investigated to obtain an optimum semi-solid structure. Results show that Gd can refine the microstructure of AZ91 D magnesium alloy, and the optimum semi-solid AZ91 D microstructure can be achieved by adding 1.5wt.% Gd. After treated at 585 °C for 30 min, the well distributed rose-shaped and near-spherical semi-solid microstructures of AZ91D+1.5wt.%Gd alloy can be obtained. The liquid phase of the semi-solid alloy consists of three components, namely, the molten pool, the "entrapped liquid" pool and the liner liquid film which separates two neighbor particles. The solid phase is composed of two phases, the primary α-Mg particles and the α-Mg phase formed in the second stage of solidification. With the increase of holding time, melting which causes the decrease of the primary α-Mg particle size is the dominant mechanism in the initial stage while coalescence and Ostwald ripening tend to be the principles later.

Microstructure and Gd-rich phase evolution of as-cast AZ31-xGd magnesium alloys during semi-solid isothermal heat treatment

The microstructure and Gd-rich phase evolution of as-cast AZ31-xGd(x=0,1.5 wt.%,2.0 wt.%and 2.5 wt.%)magnesium alloys during semi-solid isothermal heat treatment were investigated deeply in the present work.Results showed that the lamellar(Mg,Al)3Gd phases transformed into the particle-like Al2Gd phases in AZ31 magnesium alloys with Gd addition during semi-solid isothermal heat treatment,leading to yielding more sphericalα-Mg grains.When Gd content is 2.0 wt.%,the size of semi-solid spherical grains reaches the minimum.The main mechanism of grain refinement lies in the remelting of dendritic branches as well as the auxiliary effect of a small number of Al2Gd particles as grain refining inoculants.Meanwhile,Al2Gd particles enriched at the solid-liquid interfaces can remarkably retard the growth rate ofα-Mg grains.A reduction of deformation resistance has been successfully achieved in AZ31-2.0Gd magnesium alloy after semi-solid isothermal heat treatment,which shows a moderate compressive deformation resistance(230 MPa),comparing to the as-cast AZ31 magnesium alloy(280 MPa)and semi-solid AZ31 magnesium alloy(209 MPa).

Microstructural evolution of Mg9AlZnY alloy with vibration in lost foam casting during semi-solid isothermal heat treatment

The nearly equiaxed grains of Mg9AlZnY alloy were obtained by vibrating solidification in lost foam casting(LFC) and the microstructure of Mg9AlZnY alloy was analyzed.On this basis,the morphology and size of α-Mg grains fabricated by semi-solid isothermal heat treatment(SSIT) at 530 ℃ and 570 ℃ holding different time were studied.The results show that the main constituent phases of Mg9AlZnY alloy are α-Mg,β-Mg17Al12 and Al2Y,and the Y can greatly refine α-Mg grains.The distribution of α-Mg grains equivalent diameters between 20 and 100 μm is up to 87%,and the average roundness of α-Mg grains reaches 1.37 in the specimen obtained at 570 ℃ and holding time 60 min.According to the analysis of solidification kinetics and thermodynamic,binary eutectic with low melting point melts firstly on SSIT process.As the liquid fraction increases with the solute diffusibility,both of the shape and size of α-Mg grains change ceaselessly.When the liquid fraction reaches equilibrium,the α-Mg grains are gradually spheroidized under the interfacial tension,and then the α-Mg grains begin to combine and grow.Evolution of α-Mg dendritic grains on SSIT process is obviously different from that of equiaxed grains.

Evolution and distribution of Al_2Sm phase in as-extruded AZ61-xSm magnesium alloys during semi-solid isothermal heat-treatment

The evolution and distribution of Al2Sm phase in as-extruded AZ61-xSm（x=0, 1.5, 2.0 and 2.5, mass fraction, %） magnesium alloys during semi-solid isothermal heat treatment were investigated. The results showed that when as-extruded AZ61 magnesium alloys were modified with Sm, the smaller and rounder grains were obtained during semi-solid isothermal heat treatment. When the Sm content is 2.0%（mass fraction）, the average size of the globular grains reached the smallest value of 90 μm. Although a few Al2Sm particles existed in the α-Mg grains, most of Al2Sm particles solidified at the edge of the globular grains with the width of 20 μm. These phenomena are mainly attributed to the forces acting on Al2Sm particles in front of the solid-liquid interface, leading to Al2Sm particles accumulating at the solid-liquid interface and then solidifying at the edge of the globular grains in the quenching process.

Microstructure evolution of semi-solid Mg-10Gd-3Y-0.5Zr alloy during isothermal heat treatment

In this study,the microstructure evolution of semi-solid Mg-10Gd-3Y-0.5Zr alloy during isothermal heat treatment has been investigated.The results show that primary particles coarsen continuously during the holding.Coarsening rate decreases with the increase of isothermal temperature.When isothermal temperature increases from 600℃ to 620℃,the dominant mechanism for coarsening changes from particle coalescence to Ostwald ripening.Equiaxed as-cast microstructure is beneficial to the semi-solid microstructure after isothermal heat treatment,which brings about the refinement and spheroidization of primary particles,and shortening of holding time.Significant modification of second phases can also be achieved after isothermal heat treatment,due to its unique solidification process.The optimum processing parameters for Mg-10Gd-3Y-0.5Zr alloy in isothermal heat treatment are isothermal temperature of 610℃-620℃ and holding time of 20-40 min.

Structural evolution of ZA27 alloy during semi-solid isothermal heat treatment

The structural evolution of ZA27 alloy modified by element Zr was studied during semi solid isothermal heat treatment, and its transformation mechanism was also discussed. The results indicate that the primary α phase changes from equiaxed grains to spherical grains gradually at semi solid temperature of 460 ℃. With increasing isothermal time, the eutectic between boundaries of α phase diffuses toward α phase, and the primary equiaxed grain arms merge and boundaries tend to disappear to form near particle grains. Further, the eutectic left on α boundaries melts to make the near particle grains separate, and form spherical structure at last. [

Effects of trace Cr on as-cast microstructure and microstructural evolution of semi-solid isothermal heat treatment ZC61 magnesium alloy

The content and kind of trace elements in magnesium alloys have important effects on their ascast and semi-solid microstructures. In this research work, effects of trace Cr on as-cast and semi-solid microstructures of ZC61 magnesium alloy were investigated by metal mold casting and semi-solid isothermal heat treatment. The results show that the addition of Cr can refine the α-Mg phase without generating a new phase, noticeably change the eutectic phase, and decrease the average size of solid particles at the same isothermal heat treatment conditions. Non-dendritic microstructures of all alloys are constituted of α_1-Mg phases, α_2-Mg phases and eutectic phases after water quenching. With isothermal temperature increased or holding time prolonged, the eutectic microstructure(α-Mg+MgZn_2+CuMgZn) at the grain boundaries in as-cast alloy is melted preferentially and then turned into semi-solid non-dendritic microstructure by processes of initial coarsening, microstructure separation, spheroidizing and final coarsening. Especially when the ZC61-0.1 Cr alloy was treated at 585 ℃ for 30 min, the ideal non-dendritic microstructure can be obtained, and the corresponding solid particle size and shape factor were 37.5 μm and 1.33, respectively. The coarsening process of solid α-Mg phase at higher temperature or longer time, which is affected by both combining growth and Ostwald ripening mechanism, is refrained when Cr is added to the ZC61 alloy.

Microstructure evolution of semi-solid Mg-14Al-0.5Mn alloys during isothermal heat treatment

A new Mg-14Al-0.5Mn alloy that exhibits a wide solidification range and sufficient fluidity for semi-solid forming was designed. And the rnicrostructure evolution of semi-solid Mg-14Al-0.5Mn alloy during isothermal heat treatment was investigated. The mechanism of the microstructure evolution and the processing conditions for isothermal heat treatment were also discussed. The results show that the microstructures of cast alloys consist of α-Mg,β-Mg17Al12 and a small amount of Al-Mn compounds. After holding at 520 ℃ for 3 min, the phases of β-Mg17Al12 and eutectic mixtures in the Mg-14Al-0.5Mn alloy melt and the microstructures of α-Mg change from developed dendrites to irregular solid particles. With increasing the isothermal time, the amount of liquid increases, and the solid particles grow large and become spherical. When the holding time lasts for 20 min or even longer, the solid and liquid phases achieve a state of dynamic equilibrium.

Microstructural evolution of equal channel angular pressed AZ91D magnesium alloy during semi-solid isothermal heat treatment

The microstructural evolution of AZ91D magnesium alloy processed by equal channel angular pressing during isothermal heat treatment at 570℃was investigated.The results indicated that the equal channel angular pressing followed by semi-solid isothermal heat treatment was an effective method to prepare semi-solid nondendritic slurry of AZ91D magnesium alloy.During this process,its microstructure change underwent four stages,the initial coarsening stage,the structure separation stage,the spheroidization stage and the final coarsening stage.The microstructural spheroidization effect was the best after being heated for 15 min for the alloy pressed for four passes,and the grain size was the smallest.With the further increase of heating time,the grain size and shape factor increased.When the heating time was kept constant,the grain size and shape factor decreased with the increase of pressing passes.

Effects of Sm addition on microstructural evolution of Mg-6Zn-0.4Zr alloy during semi-solid isothermal heat treatment

The application of segmental semi-solid thixoforming of magnesium alloys is confined due to the dimensional distinction existing in solid particles of the alloy billet from edge to center zones. In the present study, the effects of Sm addition on the microstructural evolution of Mg-6Zn-0.4Zr and Mg-6Zn-4Sm-0.4Zr alloys by semi-solid isothermal heat treatment were investigated, to obtain optimum semi-solid microstructures for the subsequently thixoforming. The results indicate that the grains of the Sm-bearing alloy are evidently refined and gradually evolve from dendritic to globular and elliptic particles. In addition, the distinctly dimensional effect of the Mg-6Zn-0.4Zr alloy is eliminated with 4% Sm addition; the particle sizes in all zones from center to the edge of the billet are almost identical. With the increment of isothermal heat treatment temperature, the dendritic microstructures completely disappear, and meanwhile, the irregular and globular particles gradually form. The size, morphology and the distribution of solid particles mainly depend on the formation and permeation of the liquid phase in the process of isothermal heat treatment. As the isothermal temperature increases from 570 °C to 610 °C, the average size and shape factor of solid particles of both the alloys with and without Sm addition gradually decrease while the liquid fraction gradually increases.

Investigation on microstructures and properties of semi-solid Al_(80)Mg_(5)Li_(5)Zn_(5)Cu_(5)light-weight high-entropy alloy during isothermal heat treatment process

The Al_(80)Mg_(5)Li_(5)Zn_(5)Cu_(5)light-weight high-entropy alloy with globular microstructure was fabricated by isothermal heat treatment.The effects of isothermal temperatures and holding times on the semi-solid microstructure evolution were investigated.The results indicate that,with increase of the isothermal temperature,the average grain size increases and the spheroidization time shortens.With prolongation of holding time,the shape factor increases firstly and then decreases,and the average grain size decreases at first and then increases when the isothermal temperature is below 520°C,however it increases gradually at 540℃.The optimal semi-solid microstructure is obtained at 520℃ for 30 min,whose shape factor and average grain size are 0.90 and 56.4μm,respectively.Compared with as-cast Al_(80)Mg_(5)Li_(5)Zn_(5)Cu_(5) light-weight high-entropy alloy,the compressive strength and plasticity of semi-solid Al_(80)Mg_(5)Li_(5)Zn_(5)Cu_(5) light-weight high-entropy alloy are increased by 36%and 108%,respectively.The formation of semi-solid microstructures includes three stages:melting separation,spheroidization,and coarsening growth.The sluggish diffusion effect of Al_(80)Mg_(5)Li_(5)Zn_(5)Cu_(5) light-weight high-entropy alloy leads to a low coarsening rate,resulting in slow grain growth.

Direct preparation of semi-solid billets by the semi-solid isothermal heat treatment for commercial cold-rolled ZL104 aluminum alloy

Semi-solid isothermal heat treatment was proposed to directly process cold-rolled ZL104 aluminum alloys and obtain semi-solid bil-lets.The effects of two process parameters,namely,temperature and processing time,on the microstructure and hardness of the resulting bil-lets were also experimentally examined.Average grain size(AGS)increased and the shape factor(SF)of the grain improved as the process temperature increased.The SF of the grain also increased with increasing processing time,and the AGS was augmented when the processing time was prolonged from 5 to 20 min at 570℃.The hardness of the aluminum alloy decreased because of the increase in AGS with increasing temperature and processing time.The optimal temperature and time for the preparation of semi-solid ZL104 aluminum alloys were 570℃and 5 min,respectively.Under optimal process parameters,the AGS,SF,and hardness of the resulting alloy were 35.88μm,0.81,and 55.24 MPa,respectively.The Lifshitz-Slyozov-Wagner relationship was analyzed to determine the coarsening rate constant at 570℃,and a rate constant of 1357.2μm3/s was obtained.

Effect of Semi-solid Isothermal Heat Treatment on Microstructure of VW63Z Alloy

The effects of isothermal heat treatment on the semi-solid microstructure evolution of VW63Z(Mg-6Gd-3Y-0.4Zr,wt.%)alloy are studied.It shows that the microstructure of VW63Z alloy could transform from equiaxed crystal to semi-solid spherical crystal after isothermal heat treatment above 620℃.With the heating temperature elevating from 620℃ to 635℃ and the holding time prolonging from 10 min to 35 min,the liquid fraction increases gradually.The semi-solid microstructure evolution of VW63Z alloy can be divided into three stages,i.e.,particle coarsening and spheroidization;particle necking,coalescence,and Ostwald ripening;and dynamic equilibrium.The semi-solid process window of VW63Z alloy ranges from 620℃ to 635℃,where the best process parameters are holding at 635℃ for 20 min-30 min.The solid fraction,the average particle size,and the shape factor are 41.1%-53.8%,81.5μm-83.2μm,and 0.70-0.75,respectively.The maximum relative deviations of the solid fraction,the particle size,and the shape factor at different heights of the same billet are 44.6%,17.4%,and 16.6%,respectively,which means that it should pay attention to the uniformity of edge and core of VW63Z alloy during isothermal heat treatment.The driving force of microstructure is supposed to be the reduction of solid-liquid interface free energy.

Influence of Semi-Solid Isothermal Heat Treatment on Microstructure of Gray Cast Iron

Materials serve as an enabling technology contributing to solutions in problems of concern to society. In this research, the effect of semi-solid isothermal heat treatment on graphite morphologies and matrix structure for gray cast iron were studied. Microstructure observations and measurements of flaky graphite morphology are reported as a function of isothermal heating time range of 5 to 25 minutes after isothermal heating temperature at 1163℃. The effect heating time, on the semisolid microstructures during partial re-melting was investigated. Flack graphite morphology was changed significantly by isothermal heating of gray cast iron at 1163℃ for heating time above 15 min resulting fine graphite morphology in matrix structure. Hardness increases with increasing heating time due to the amount of cementite and fine pearlite matrix for air cooled gray cast iron. The optimum heating treatment condition was achieved at the temperature of 1163℃ for the range of 15 to 20 min.

Effect of holding time on microstructure of Mg-9Al-1Si alloy during semisolid isothermal heat treatment

The effects of isothermal holding time on the semisolid microstructure of Mg-9Al-1Si(mass fraction,%)alloy were investigated.The research results indicate that the Mg-9Al-1Si alloy with non-dendritic microstructure can be produced by the semi-solid isothermal heat treatment.With holding time varying from 5 to 30 min,the volume fraction of liquid is gradually enlarged from 29.3%to 38.6%,the morphology ofα-Mg grains changes from initial dendritic shape to spherical types and their average sizes increases from 41.1 to 56.1μm.In addition,during the isothermal heat treatment,the eutectic Mg2Si phase changes from the initial Chinese script shape to granule and/or polygon shape in Mg-9Al-1Si alloy.The modification of Mg2Si phase is possibly attributed to a shift of the eutectic composition of the liquid in semi-solid slurries,towards lower silicon contents with increasing Al content due to a redistribution of Al during isothermal heat treatment.

Grain growth of Al-4Cu-Mg alloy during isothermal heat treatment

The microstructure of an Al-4Cu-Mg alloy during isothermal heat treatment in the Strain Induced Melt Activation （SIMA） process was investigated and the kinetics of grain growth was analyzed, The grain growth during isothermal heat treatment of the Al-4Cu-Mg alloy coincided with the Ostwald ripening theory. During isothermal heat treatment, both grain shape and the high volume fraction of solid phase have significant effects on grain growth. Therefore, a new grain growth model based on the Ostwald ripening theory was proposed taking into consideration the grain shape and the volume fraction of solid phase. By comparing the calculated results with the experimental results, it was confirmed that the present model could be applied to grain growth during isothermal heat treatment of the Al-4Cu-Mg alloy in the SIMA process.

Effects of isothermal process parameters on semisolid microstructure of Mg-8%Al-1%Si alloy

A Mg-8%Al-1%Si alloy with semisolid microstructure was fabricated by isothermal heat treatment process. The effects of isothermal process parameters such as holding temperature and holding time on the microstructure of Mg-8%Al-1%Si alloy were investigated. The results show that a non-dendritic microstructure could be obtained by isothermal heat treatment. With increasing holding temperature from 560 to 575 °C or holding time from 5 to 30 min, the liquid volume fraction increases, the average size of α-Mg grains grows larger and globular tendency becomes more obvious. In addition, the Mg2Si phase transforms from Chinese script shape to granule shape. The morphology modification mechanisium of Mg2Si phase in Mg-8%Al-1%Si alloy during the semisolid isothermal heat treatment was also studied.

Effects of Semi-solid Isothermal Heat Treatment on Microstructures and Damping Capacities of Fly Ash Cenosphere/AZ91D Composites

The fly ash cenosphere/AZ91D composites were successfully prepared and isothermally heat-treated at different tem- peratures for different time. The effects of semi-solid isothermal heat treatment on the microstructures and damping capacities of fly ash cenosphere/AZ91D composites were investigated. With the increase in isothermal temperature or holding time, the small liquid droplets within grains increased in size but decreased in quantity. The average size and shape factor of Mg2Si particles increased with the rise of isothermal temperature. The damping capacities of the composites were improved by isothermal heat treatment. At room temperature, the composites after heat treatment at 520 and 550 ℃ had a higher damping capacity due to interface damping when the strain amplitude was lower than about 8.8 × 10^-5, and the composite after heat treatment at 580 ℃ had a better damping capacity because of the dislocation damping under the condition of high strain amplitude. The damping capacities of the composites increased with the rise of the test temper- ature, and the damping mechanisms varied depending on different test temperatures. The interface damping played an important role when the test temperature was below about 100 ℃, and the dislocation damping and grain boundary damping took effect with the rise of test temperature.

Mg-5Al-1.5Ca-0.4Zn基镁合金的等温法半固态压铸组织和性能

研究了Mg25Al2115Ca2014Zn2012Mn2Sr2Ti合金的等温法半固态压铸组织和性能。结果表明:合金相组成为α(Mg)、(α(Mg)+Al2Ca)共晶和少量球状Mg17Al12。Sr变质合金在585℃等温法处理时,α(Mg)首先分离成核。随着等温时间加长,α(Mg)由块状向球状转变。25min时,转变为粒径40μm的均匀球状组织。此后,球晶发生长大,进而聚拢合并。合金等温法压铸实验发现,组织为均匀细小等轴晶,粒径25μm。合金室温和高温强度较砂铸大幅提高,塑性略有下降。这是由于细晶强化作用,以及晶粒细化使得晶界上半连续分布的Al2Ca相更弥散,这样Al2Ca高温下钉扎晶界的作用更加突出。等温法半固态压铸合金200℃的高温强度优于AZ91压铸合金,可达140MPa。

半固态等温热处理对AZ91D镁合金组织的影响

研究了 AZ91 D镁合金在半固态等温热处理过程中 ,等温时间、等温温度对其组织形态和初生相尺寸的影响 .研究发现 :在升温过程中 ,晶界处的共晶组织 (δ+γ)中的 γ相先发生溶解 ,之后 ,随着温度进一步升高 ,δ相又发生熔化分离 ,并在等温处理过程中逐渐变为球状 .当等温时间过长时 ,球状颗粒有长大的趋势 ,结果表明 :在 570℃时保温 60 min,可得到初生相尺寸在 50～ 80 μm的球状组织 .