Diamond single crystal was epitaxially grown on the surface of diamond seeds with rough planes at high pressure and high temperature(HPHT)conditions.Fe80Ni20alloy powder was used as catalyst/solvent and natural flake-...Diamond single crystal was epitaxially grown on the surface of diamond seeds with rough planes at high pressure and high temperature(HPHT)conditions.Fe80Ni20alloy powder was used as catalyst/solvent and natural flake-like graphite was used as carbon source.Diamond single crystals were grown on the diamond seeds at 4.8GPa and 1500K.The morphology of the samples was observed by SEM.The mechanism of diamond growth with smooth planes from original seed with rough planes was studied.展开更多
文摘Diamond single crystal was epitaxially grown on the surface of diamond seeds with rough planes at high pressure and high temperature(HPHT)conditions.Fe80Ni20alloy powder was used as catalyst/solvent and natural flake-like graphite was used as carbon source.Diamond single crystals were grown on the diamond seeds at 4.8GPa and 1500K.The morphology of the samples was observed by SEM.The mechanism of diamond growth with smooth planes from original seed with rough planes was studied.