The shape memory behavior of [111]-oriented Ni_（51）Ti_（49） （at.%） single crystals was investigated after stressassisted aging at 500 °C for 1.5 h under a compressive stress of-150 MPa.It was found that a si...The shape memory behavior of [111]-oriented Ni_（51）Ti_（49） （at.%） single crystals was investigated after stressassisted aging at 500 °C for 1.5 h under a compressive stress of-150 MPa.It was found that a single family of Ni_4Ti_3 precipitates with two crystallographically equivalent variants was formed after aging under compressive stress.Stressassisted aging resulted in tensile two-way shape memory effect strain of 1.56% under-5 MPa.Thermal cycling under-600 MPa resulted in a transformation strain of-2.15%,while the subsequent thermal cycling under-5 MPa resulted in a tensile two-way shape memory effect strain of 2.2%.展开更多
The influence of heat treatment with different cooling rates on phase transition behaviors and magnetocaloric effect is systematically studied.Difference in atomic order is induced by changing cooling rates,where orde...The influence of heat treatment with different cooling rates on phase transition behaviors and magnetocaloric effect is systematically studied.Difference in atomic order is induced by changing cooling rates,where ordered phase is obtained in the furnace cooled（FC）sample while disordered phase is reserved in the water quenched（WQ）sample.The coupled magneto-structural transition is detected in both samples but the characteristic temperature significantly shifts to lower temperatures with increasing atomic order.Giant magnetic entropy change（ΔS_（mag））derived from magnetic field induced martensitic transformation is confirmed for both samples,and can be remarkably enhanced by the atomic ordering.The largestΔS_（mag） of 20.9J/（kg·K）is obtained at 307.5Kunder 5Tin the FC sample.展开更多
基金supported in part by the NASA Fundamental Aeronautics ProgramSupersonics Project and the NASA EPSCOR program(Grant No.NNX11AQ31A)RFBR Project(Grant No.10-03-0154-a)
文摘The shape memory behavior of [111]-oriented Ni_（51）Ti_（49） （at.%） single crystals was investigated after stressassisted aging at 500 °C for 1.5 h under a compressive stress of-150 MPa.It was found that a single family of Ni_4Ti_3 precipitates with two crystallographically equivalent variants was formed after aging under compressive stress.Stressassisted aging resulted in tensile two-way shape memory effect strain of 1.56% under-5 MPa.Thermal cycling under-600 MPa resulted in a transformation strain of-2.15%,while the subsequent thermal cycling under-5 MPa resulted in a tensile two-way shape memory effect strain of 2.2%.
基金supported by the National Natural Science Foundations of China(Grant Nos.51331001, 51520105002,51601008,and 51601007)the Fundamental Research Funds for Central Universities
文摘The influence of heat treatment with different cooling rates on phase transition behaviors and magnetocaloric effect is systematically studied.Difference in atomic order is induced by changing cooling rates,where ordered phase is obtained in the furnace cooled（FC）sample while disordered phase is reserved in the water quenched（WQ）sample.The coupled magneto-structural transition is detected in both samples but the characteristic temperature significantly shifts to lower temperatures with increasing atomic order.Giant magnetic entropy change（ΔS_（mag））derived from magnetic field induced martensitic transformation is confirmed for both samples,and can be remarkably enhanced by the atomic ordering.The largestΔS_（mag） of 20.9J/（kg·K）is obtained at 307.5Kunder 5Tin the FC sample.
