This paper presents the performance and characteristics of new-type sulfur tolerant shift catalyst QDB-04 and its industrial side-line test as well as the first-time industrial application in Lunan Chemical Fertilizer...This paper presents the performance and characteristics of new-type sulfur tolerant shift catalyst QDB-04 and its industrial side-line test as well as the first-time industrial application in Lunan Chemical Fertilizer Plant of Shandong in China. The results show that the catalyst has high strength and strength stability, good low temperature activity and stability as well as low potassium bleeding ratio which well meet for the requirements of the methanol plant on catalyst performance in Lunan Chemical Fertilizer Plant.展开更多
采用水热合成法制备了CuS_(x)催化剂,通过改变前驱体铜硫比〔n(Cu)∶n(S)〕,调控催化剂形貌和反应路径。将CuS_(x)催化剂用于温和电势下CO_(2)高效电催化还原制CO反应。采用XRD、FESEM和XPS对CuS_(x)催化剂进行了表征,探究了铜硫比对CuS...采用水热合成法制备了CuS_(x)催化剂,通过改变前驱体铜硫比〔n(Cu)∶n(S)〕,调控催化剂形貌和反应路径。将CuS_(x)催化剂用于温和电势下CO_(2)高效电催化还原制CO反应。采用XRD、FESEM和XPS对CuS_(x)催化剂进行了表征,探究了铜硫比对CuS_(x)催化剂电催化CO_(2)还原“构效关系”的影响。结果表明,铜硫比影响CuS晶体成核与生长,进而影响CuS_(x)催化剂的形貌和S空位缺陷。当铜硫比在2∶1~1∶4内变化,CuS_(x)催化剂的形貌由荷花状转化为花球状,S空位含量由20.66%提高至63.37%,CO_(2)电催化还原活性和目标产物CO选择性明显提升。由铜硫比为1∶4制备的CuS_(x)催化剂(CuS-1∶4)在0.1 mol/L的KHCO3电解液中,在–0.51 V vs.RHE(可逆氢电极)的温和电势下,CO选择性达72.67%。CuS-1∶4优异的CO_(2)还原性能归因于催化剂花球状形貌、高比表面积和气体扩散通道提供的不饱和活性位点促进了气体扩散,以及S空位缺陷对电子传递和*COOH中间体在催化剂表面吸附的强化作用。展开更多
A series of sulfur tolerant Co Mo/MgO Al 2O 3 TiO 2 catalysts promoted by TiO 2 were prepared by kneading method and characterized by temperature programmed reduction, temperature programmed sulfurization and in situ ...A series of sulfur tolerant Co Mo/MgO Al 2O 3 TiO 2 catalysts promoted by TiO 2 were prepared by kneading method and characterized by temperature programmed reduction, temperature programmed sulfurization and in situ infra red spectroscopy. The catalyst activity for water gas shift reaction was tested under atmosphere in an ordinary tubular reactor. The results indicate that TiO 2 promotes the activity of Co Mo/MgO Al 2O 3 TiO 2 catalyst and decreases the reducing and sulfurizing temperature by changing interaction between active composition and carrier. In situ infra red spectra show that TiO 2 decreases the saturation level of active Mo and increases the coordinate capacity of active Mo with CO.展开更多
文摘This paper presents the performance and characteristics of new-type sulfur tolerant shift catalyst QDB-04 and its industrial side-line test as well as the first-time industrial application in Lunan Chemical Fertilizer Plant of Shandong in China. The results show that the catalyst has high strength and strength stability, good low temperature activity and stability as well as low potassium bleeding ratio which well meet for the requirements of the methanol plant on catalyst performance in Lunan Chemical Fertilizer Plant.
文摘采用水热合成法制备了CuS_(x)催化剂,通过改变前驱体铜硫比〔n(Cu)∶n(S)〕,调控催化剂形貌和反应路径。将CuS_(x)催化剂用于温和电势下CO_(2)高效电催化还原制CO反应。采用XRD、FESEM和XPS对CuS_(x)催化剂进行了表征,探究了铜硫比对CuS_(x)催化剂电催化CO_(2)还原“构效关系”的影响。结果表明,铜硫比影响CuS晶体成核与生长,进而影响CuS_(x)催化剂的形貌和S空位缺陷。当铜硫比在2∶1~1∶4内变化,CuS_(x)催化剂的形貌由荷花状转化为花球状,S空位含量由20.66%提高至63.37%,CO_(2)电催化还原活性和目标产物CO选择性明显提升。由铜硫比为1∶4制备的CuS_(x)催化剂(CuS-1∶4)在0.1 mol/L的KHCO3电解液中,在–0.51 V vs.RHE(可逆氢电极)的温和电势下,CO选择性达72.67%。CuS-1∶4优异的CO_(2)还原性能归因于催化剂花球状形貌、高比表面积和气体扩散通道提供的不饱和活性位点促进了气体扩散,以及S空位缺陷对电子传递和*COOH中间体在催化剂表面吸附的强化作用。
文摘A series of sulfur tolerant Co Mo/MgO Al 2O 3 TiO 2 catalysts promoted by TiO 2 were prepared by kneading method and characterized by temperature programmed reduction, temperature programmed sulfurization and in situ infra red spectroscopy. The catalyst activity for water gas shift reaction was tested under atmosphere in an ordinary tubular reactor. The results indicate that TiO 2 promotes the activity of Co Mo/MgO Al 2O 3 TiO 2 catalyst and decreases the reducing and sulfurizing temperature by changing interaction between active composition and carrier. In situ infra red spectra show that TiO 2 decreases the saturation level of active Mo and increases the coordinate capacity of active Mo with CO.