Effect of Grinding Techniques on Absorbing Characteristics of Short Iron Fibers

Microwave-absorbing properties of iron fibers can be adjusted by their aspect ratio. This paper presents several modification techniques for grinding long iron fibers to a suitable aspect ratio. The grinding instruments include pulsator, jet mill and muller. The aspect ratio distribution, microstructure, electromagnetic parameter and reflectivity of the samples were analyzed and discussed in detail. The results show that the fractions of 5〈aspect ratio〈40 for the three methods are 69.03%, 81.11% and 80.2% , respectively, that is, suitable short iron fibers can be obtained by the jet mill and muller. Furthermore, the short iron fibers milled by jet mill and muller have better absorbing propterties than those obtained by the pulsator under the same condition. Therefore, their microwave absorption properties can be improved by regulating the electromagnetic parameters with grinding.

合金元素铜和镍对铸铁短纤维烧结特性的影响

研究了1100℃烧结温度下合金元素铜、镍含量对铸铁短纤维烧结特性的影响规律,结果表明:与铁—铜粉末压坯相比,铸铁短纤维—铜压坯烧结后的最大膨胀率及相对应的铜含量均明显减少。产生膨胀的主要原因是铜熔化后,富铜液相向奥氏体中扩散,在原位留下空隙,而液相沿界面流动不明显。镍显著加快了铸铁短纤维烧结体的致密化。在镍含量高于4.5％时,显微组织中出现奥氏体相,在奥氏体与珠光体边界析出网状渗碳体,在奥氏体晶内析出魏氏碳化物及游离石墨,引起致密化速率下降,断裂方式由延性断裂转化为脆性断裂。

合金元素P、Cu含量对铸铁短纤维结合剂组织和性能的影响

本文研究了合金元素磷和铜对铸铁短纤维烧结体显微组织和性能的影响.结果表明,合金元素磷可显著提高铸铁短纤维烧结体的密度、致密化系数和压溃强度.磷与铜的共同加入可进一步提高烧结体的压溃强度和硬度,同时,铜的加入可抑制由磷引起的烧结体的急剧收缩.烧结机理随磷、铜含量的增加逐渐由固相烧结+瞬态液相烧结转变为液相烧结.

短纤维增韧铁硼化合物基复合材料应力研究

铁硼合金具有较好的耐锌腐蚀性能,但脆性限制了它的工业应用,短切纤维增韧可以有效改善该材料的力学性能。在断口分析基础上,采用双纤维复合材料模型,利用有限元方法计算了复合材料的残余热应力及外力作用时的应力分布。结果表明,纤维中的残余热应力为压应力,基体中为拉应力;随着纤维长径比的增加,残余应力逐渐提高;增加纤维体积分数有利于提高复合材料的抗拉强度。

铸铁短纤维结合剂金刚石圆锯片的研制

在研究成型、烧结工艺参数对铸铁短纤维烧结性能影响的基础上,研制新型金刚石锯片——铸铁短纤维结合剂金刚石圆锯片。在250 MPa,940℃条件下热压烧结10 min后,获得的金刚石锯片其刀头具有较高的密度(6.92 g/cm3)、强度和硬度,胎体对金刚石有较高的把持力,切削锋利,使用寿命偏短。制造铸铁短纤维结合剂金刚石工具,热压成形低温烧结工艺要优于冷压成形高温烧结工艺。

桥面抢修用超快硬超短钢纤维混凝土的研究

普通混凝土桥面和汽车通行频率较高的国道桥面运行中发生的一些混凝土裂缝、破碎、脱落和凹面等问题 ,严重影响了桥面往来的平稳行驶 ,往往需要及时抢修 ,研究发现超快硬超短钢纤维混凝土具有轻、强、巧。