The composition and production technology of the type of hot-rolled steel plate used in two-sided enameling were briefly described. The microstructure and mechanical properties before and after enameling were contrast...The composition and production technology of the type of hot-rolled steel plate used in two-sided enameling were briefly described. The microstructure and mechanical properties before and after enameling were contrastively investigated,and the precipitates in the samples were analyzed using transmission electron microscope and energy dispersive spectrometer. The results show the ferrite grain size of the steel plate after high-temperature enamel firing to be fine,with a large number of TiC and Ti;C;S;precipitates dispersed throughout the ferrite matrix. After two rounds of enamel firing at a temperature range of 800-890 ℃,its yield strength can still reach342 MPa. The results of a hydrogen permeation test show that the hydrogen storage properties of the steel plate are much better than those of ordinary structural carbon steel. A better bubble structure in the enamel layer can be obtained by this steel plate,with no fish-scale defects on the enameled steel-plate surface.展开更多
Reducing wear on a side dam can prolong the casting operation life of a twin-roll strip casting process,thus reducing production cost and improving casting stability.To lengthen the service life of the side dam,it is ...Reducing wear on a side dam can prolong the casting operation life of a twin-roll strip casting process,thus reducing production cost and improving casting stability.To lengthen the service life of the side dam,it is necessary to understand the wear performance of the side dam material.To investigate the wear behavior mechanism of the side dam,in this study,the UMT-2 friction and wear tester was used to determine the relationship between the wear rate of the side-dam material and various parameters.Based on the roughness of the contact area between the side dam and the end of the casting rolls as well as on the amount of deformation of the side dam,which was derived using a thermal-deformation simulation model,the reasons for the uneven wear of the side dam were obtained.展开更多
文摘The composition and production technology of the type of hot-rolled steel plate used in two-sided enameling were briefly described. The microstructure and mechanical properties before and after enameling were contrastively investigated,and the precipitates in the samples were analyzed using transmission electron microscope and energy dispersive spectrometer. The results show the ferrite grain size of the steel plate after high-temperature enamel firing to be fine,with a large number of TiC and Ti;C;S;precipitates dispersed throughout the ferrite matrix. After two rounds of enamel firing at a temperature range of 800-890 ℃,its yield strength can still reach342 MPa. The results of a hydrogen permeation test show that the hydrogen storage properties of the steel plate are much better than those of ordinary structural carbon steel. A better bubble structure in the enamel layer can be obtained by this steel plate,with no fish-scale defects on the enameled steel-plate surface.
文摘Reducing wear on a side dam can prolong the casting operation life of a twin-roll strip casting process,thus reducing production cost and improving casting stability.To lengthen the service life of the side dam,it is necessary to understand the wear performance of the side dam material.To investigate the wear behavior mechanism of the side dam,in this study,the UMT-2 friction and wear tester was used to determine the relationship between the wear rate of the side-dam material and various parameters.Based on the roughness of the contact area between the side dam and the end of the casting rolls as well as on the amount of deformation of the side dam,which was derived using a thermal-deformation simulation model,the reasons for the uneven wear of the side dam were obtained.