Milling Research and Tool Selection Design of SiC14Cu4Mg0.5Si based on Aluminium Matrix 2A14

The selection of milling tools for Si C14Cu4Mg0.5Si based on Aluminium matrix 2A14 was analyzed, and the factors that affect the efficiency of the milling were discussed. The Si C14Cu4Mg0.5Si was designed for use on the moon landing vehicle or missile wings, but the hardness of aluminium-silicon carbide composite material was very high, much higher than the general hardness of cemented carbide, which will bring many difficulties in the aluminium-silicon carbide composite material processing. The chemical compositions of Si C14Cu4Mg0.5Si were analyzed. A new selected indexable cutter was designed to mill Si C14Cu4Mg0.5Si. The structure design of milling cutter was different from the conventional milling cutter, breaking the previous limitations to a certain extent, pioneering the idea. The tool material wear was detected by experiments. The mechanical and physical properties of Si C14Cu4Mg0.5Si were also tested. Si C14Cu4Mg0.5Si exhibited different surface quality characteristics under different milling tools.

Effect of Mg and Si on infiltration behavior of Al alloys pressureless infiltration into porous SiCp preforms

The effect of Mg and Si additon to Al matrix on infiltration kinetics and rates of Al alloys pressureless infiltration into porous SiCp preform was investigated by observing the change of infiltration distance with time as the Al alloys infiltrate into SiCp preforms at different temperatures.The results show that infiltration of SiCp preforms by Al melt is a thermal activation process and there is an incubation period before the infiltration becomes stable.With the increase of Mg content in the Al alloys from 0wt% to 8wt%,the infiltration will become much easier,the incubation period becomes shorter and the infiltration rate is faster,but these effects are not obvious when the Mg content is higher than 8wt%.As for Si addition to the Al alloys,it has no obvious effect on the incubation period,but the infiltration rate increases markedly with the increase of Si content from 0wt% to 12wt% and the rate has no obvious change when the content is bigger than 12wt%.The effect of Mg and Si on the incubation period is related to the infiltration mechanism of Al pressureless infiltration into SiCp preforms and their impact on the infiltration rate is a combined result from viscosity and surface tension of Al melt and SiC-Al wetting ability.

Long-term ceramic matrix composite for aeroengine

Three strategies were proposed to prolong the service life of continuous fiber-reinforced silicon carbide ceramic matrix composite(CMC-SiC),which served as thermal-structure components of aeroengine at thermo-mechanical-oxygenic coupling environment.As for some thermal-structure components with low working stress,improving the degree of densification was crucial to prolong the service life,and the related process approaches were recited.If the thermal-structure components worked under moderate stress,the matrix cracking stress(σ^(mc))should be improved as far as possible.The fiber preform architecture,interface shear strength,residual thermal stress,and matrix strengthening were associated withσ_(mc)in this review.Introducing self-healing components was quite significant with the appearance of matrix microcracks when CMC-SiC worked at more severe environment for hundreds of hours.The damage can be sealed by glass phase originating from the reaction between self-healing components and oxygen.The effective self-healing temperature range of different self-healing components was first summarized and distinguished.The structure,composition,and preparation process of CMC-SiC should be systematically designed and optimized to achieve long duration target.

Thermal conductivity and bending strength of SiC composites reinforced by pitch-based carbon fibers

In this work,pitch-based carbon fibers were utilized to reinforce silicon carbide(SiC)composites via reaction melting infiltration(RMI)method by controlling the reaction temperature and resin carbon content.Thermal conductivities and bending strengths of composites obtained under different preparation conditions were characterized by various analytical methods.Results showed the formation of SiC whiskers(SiC_(w))during RMI process according to vapor–solid(VS)mechanism.SiC_(w) played an important role in toughening the C_(pf)/SiC composites due to crack bridging,crack deflection,and SiC_(w) pull-out.Increase in reaction temperature during RMI process led to an initial increase in thermal conductivity along in-plane and thickness directions of composites,followed by a decline.At reaction temperature of 1600℃,thermal conductivities along the in-plane and thickness directions were estimated to be 203.00 and 39.59 W/(m×K),respectively.Under these conditions,bending strength was recorded as 186.15±3.95 MPa.Increase in resin carbon content before RMI process led to the generation of more SiC matrix.Thermal conductivities along in-plane and thickness directions remained stable with desirable values of 175.79 and 38.86 W/(m×K),respectively.By comparison,optimal bending strength improved to 244.62±3.07 MPa.In sum,these findings look promising for future application of pitch-based carbon fibers for reinforcement of SiC ceramic composites.

Rare earth monosilicates as oxidation resistant interphase for SiCf/SiC CMC:Investigation of SiC_(f)/Yb_(2)SiO_(5)model composites

Model composites consisting of SiC fiber and Yb_(2)SiO_(5)were processed by the spark plasma sintering(SPS)method.The mechanical compatibility and chemical stability between Yb_(2)SiO_(5)and SiC fiber were studied to evaluate the potential application of Yb monosilicate as the interphase of silicon carbide fiber reinforced silicon carbide ceramic matrix composite(SiC_(f)/SiC CMC).Two kinds of interfaces,namely mechanical and chemical bonding interfaces,were achieved by adjusting sintering temperature.SiC_(f)/Yb_(2)SiO_(5)interfaces prepared at 1450 and 1500℃exhibit high interface strength and debond energy,which do not satisfy the crack deflection criteria based on He-Hutchison diagram.Raman spectrum analyzation indicates that the thermal expansion mismatch between Yb_(2)SiO_(5)and SiC contributes to high compressive thermal stress at interface,and leads to high interfacial parameters.Amorphous layer at interface in model composite sintered at 1550℃is related to the diffusion promoted by high temperature and DC electric filed during SPS.It is inspired that the interfacial parameters could be adjusted by introducing Yb_(2)Si_(2)O_(7)-Yb_(2)SiO_(5)interphase with controlled composition to optimize the mechanical fuse mechanism in SiC_(f)/SiC CMC.