Aluminum foam is a light weight material with good mechanical and energy absorption properties. In this study, aluminum foam composite was fabricated using aluminum powder 6061 and silicon carbide (SiC) powder. Titani...Aluminum foam is a light weight material with good mechanical and energy absorption properties. In this study, aluminum foam composite was fabricated using aluminum powder 6061 and silicon carbide (SiC) powder. Titanium hydride (TiH2) was used as the foaming agent. Cold compact followed by hot pressing (sintering) was used to produce the composite precursor. Foaming was carried out, following the sintering process, by heating the aluminum composite precursor to a temperature above the melting point of aluminum (Al). The linear expansion of the foam and the percent porosity were found to increase as the SiC percentage decreased from 10 to 4%, whereas the density got lower. The percent porosity and linear expansion were both found to increase as the percentage of the foaming agent was increased from 0.5 to 1.5%. Compression stress was evaluated for two different porosity values (40% and 47%), and found to be higher for the samples with lower percent porosity at the same strain value. Effect of shape memory alloy fiber, made of nickel and titanium (NiTi), on the mechanical properties was also investigated. The compression stress was higher, in the densification region, for the samples in which NiTi was used.展开更多
文摘Aluminum foam is a light weight material with good mechanical and energy absorption properties. In this study, aluminum foam composite was fabricated using aluminum powder 6061 and silicon carbide (SiC) powder. Titanium hydride (TiH2) was used as the foaming agent. Cold compact followed by hot pressing (sintering) was used to produce the composite precursor. Foaming was carried out, following the sintering process, by heating the aluminum composite precursor to a temperature above the melting point of aluminum (Al). The linear expansion of the foam and the percent porosity were found to increase as the SiC percentage decreased from 10 to 4%, whereas the density got lower. The percent porosity and linear expansion were both found to increase as the percentage of the foaming agent was increased from 0.5 to 1.5%. Compression stress was evaluated for two different porosity values (40% and 47%), and found to be higher for the samples with lower percent porosity at the same strain value. Effect of shape memory alloy fiber, made of nickel and titanium (NiTi), on the mechanical properties was also investigated. The compression stress was higher, in the densification region, for the samples in which NiTi was used.