This paper reviewed the effect of powder characteristics and additives including metals,rare earth oxides,and ZrO2 on nitridation of Si powder.The decrease of particle size of Si powder increased nitridation.Most of m...This paper reviewed the effect of powder characteristics and additives including metals,rare earth oxides,and ZrO2 on nitridation of Si powder.The decrease of particle size of Si powder increased nitridation.Most of metal additives inhibited nitridation,while some metal additives such as Fe,Cu,Cr,and Ca increased nitrida—tion.Otherwise,the addition of metals might lead to the degradation of physical and mechanical properties of Si3N4.All the rare earth oxides,especially CeO2 and Eu2O3,showed nitridation enhancing effect.In addition,ZrO2 with small particle size showed a stronger enhancing effect.展开更多
Si3N4 powder was synthesized by carbothermal re- duction nitridation reaction using sawdust as carbon source and introducing SiO2 by silica sol immersion. Effects of SiO2 content of silica sol, molding pressure, react...Si3N4 powder was synthesized by carbothermal re- duction nitridation reaction using sawdust as carbon source and introducing SiO2 by silica sol immersion. Effects of SiO2 content of silica sol, molding pressure, reaction temperature, reaction duration, and N2 flow rate on phase compositions and microstructure of result- ants were studied. The results show that using 7. 5 mass% SiO2 containing silica sol immersed sawdust as raw materials, the prepared Si3N4 powder is featured with high α-Si3N4 content, few impurities, etc. in the conditions of 1 450 ℃ of reaction temperature, 9 h of reaction duration, 400 mL ·min- 1 of N2 flow rate and 10 MPa of molding pressure.展开更多
基金financially supported by Guangdong Innovative and Entrepreneurial Research Team Program ( No. 2013G061)the National Natural Science Foundation of China ( No. 51402055)
文摘This paper reviewed the effect of powder characteristics and additives including metals,rare earth oxides,and ZrO2 on nitridation of Si powder.The decrease of particle size of Si powder increased nitridation.Most of metal additives inhibited nitridation,while some metal additives such as Fe,Cu,Cr,and Ca increased nitrida—tion.Otherwise,the addition of metals might lead to the degradation of physical and mechanical properties of Si3N4.All the rare earth oxides,especially CeO2 and Eu2O3,showed nitridation enhancing effect.In addition,ZrO2 with small particle size showed a stronger enhancing effect.
文摘Si3N4 powder was synthesized by carbothermal re- duction nitridation reaction using sawdust as carbon source and introducing SiO2 by silica sol immersion. Effects of SiO2 content of silica sol, molding pressure, reaction temperature, reaction duration, and N2 flow rate on phase compositions and microstructure of result- ants were studied. The results show that using 7. 5 mass% SiO2 containing silica sol immersed sawdust as raw materials, the prepared Si3N4 powder is featured with high α-Si3N4 content, few impurities, etc. in the conditions of 1 450 ℃ of reaction temperature, 9 h of reaction duration, 400 mL ·min- 1 of N2 flow rate and 10 MPa of molding pressure.