Fabrication of silica-based ceramic cores with internal lattice structures by stereolithography

Ceramic cores are widely used in investment casting,and ideal properties of cores are essential for high-quality castings.Under the circumstances requiring thick cores,solid cores are likely to encounter deformation and cracking defects due to the accumulation of shrinkage.Therefore,with the superiority of ceramic stereolithography in producing complex ceramic parts,hollow cores with lattice structures were designed and fabricated.The dimensional accuracy and properties of the green and sintered bodies were evaluated.Results show the dimensional accuracy of sintered cores is controlled within±0.25 mm benefited from the precise green bodies.The mechanical properties are not obviously deteriorated.The bending strength reaches 11.94 MPa at room temperature and 12.87 MPa at 1,500℃ with a creep deformation of 0.345 mm.Furthermore,casting verifications prove that the hollow cores meet the requirements of investment casting.Smooth casting surfaces are obtained,at the same time,the core-removal efficiency is improved by over 3 times.

Effect of nonuniform sintering on mechanical and thermal properties of silica-based ceramic cores

During sintering of the silica-based ceramic core of turbine blades,a phenomenon called"nonuniform sintering"occurs that negatively affects the thermal and mechanical properties of the core.Standard samples of silica-based core were prepared by an injection molding method and sintered with alumina backfilling powder with different sodium contents.The effect of sodium content on the nonuniform sintering of silica-based cores and the thermal and mechanical properties was evaluated.Results show that the sintering level and the content ofα-cristobalite in the surface layer are significantly higher than that of the sample interior.A considerable number of microcracks are found in the surface layer due to theβtoα-phase transition of cristobalite.As the sodium content in the alumina powder decreases,the level of the nonuniform sintering and the amount of crystallized cristobalite in the surface layer decrease,which is beneficial to the thermal expansion and flexural strength at ambient temperature.The flexural strength and thermal deformation at high temperature are improved by reducing the surface cracks,but deteriorated with the decrease of the cristobalite crystallization when the surface cracks are macroscopically invisible.

Properties of alumina-based ceramic cores

Fused corundum is a rather promising raw material for preparing an alumina-based ceramic core due to its excellent high temperature resistance and chemical inertness.In this study,alumina-based ceramic cores were prepared using fused corundum as the matrix material,and the effect of varying silica powder contents on the properties of the alumina-based ceramic cores,including the sintering shrinkage,the flexural strength,and the high temperature deformation was investigated.The mineralization mechanisms of the silica on the alumina-based ceramic core were also analyzed.The optimum addition amount of silica in this experiment is 8% in weight.At that moment,the aluminum-based core has both a low sintering shrinkage coefficient of 0.66% and better properties:the room temperature flexural strength is 22.19 MPa,the high temperature flexural strength is 21.54 MPa,the high temperature deformation is 0.93 mm,and the residual flexural strength is 47.41 MPa.

Microstructure of Al_2O_3/SiO_2 ceramic core nano-composites

Al2O3/SiO2 ceramic core nano-composites were prepared and their microstructure was investigated by transmission electron microscope（TEM）. The results show that intergranular nano-composites are achieved. The bonding between Al2O3 and SiO2 particles is well and the interface is even. Amorphous phases and nano crystals appear in the Al2O3/SiO2 ceramic core nano-composites, which both come into being during the cooling process after sintering. Glass phase does not appear between the Al2O3 and SiO2 particles and only appears among the Al2O3 particles, which can be explained with stress model. The quantity of the glass phase is not much and its influence on the high-temperature deformation of the ceramic core nano-composites is little.

Difference in particle characteristics and coating properties between spraying metallic and ceramic powder cored wires

The sprayed particles of metallic and cermet wires were collected to analyze the atomization state of the particles in arc spraying forming, the microstructure and properties of metallic and ceramic coatings were investigated and compared. Particle size analyzer was used for quantifying particle size. The XRD, SEM and optical microscope(OM) were used to analyze the phase composition and microstructure of the particles and coatings. From the experimental results, some difference of particle characteristics was established between the spraying metallic and ceramic cored wires, and the microstructure and properties of coatings depend strongly on the particles behaviors. The result shows that Fe-TiB2/Al2O3 composite coating has a high potential for abrasive wear applications.

Synthesis of Ti₃SiC₂-Bicarbide Based Ceramic by Electro-Thermal Explosion

A polycrystalline dense Ti3SiC2 based ceramic material has been produced by several techniques. The effect of addition of TiC and SiC is also studied. The Ti3SiC2 material shows extraordinary electrical, thermal and mechanical properties. Furthermore, it shows a damage tolerance capability and oxidation resistance. In this work, we have synthesized Ti3SiC2 by electro-thermal explosion chemical reaction (ETE) with high current density (900 Amperes/a.u) followed by uniaxial pressure. The structural properties of the as-prepared materials are studied by x-ray diffraction (XRD), scanning electron microscope (SEM) and energy dispersive x-ray spectroscopy (EDX) techniques. The chemical cartography, imaging and electronic properties are investigated using Ultra-STEM and electron high energy loss resolution spectroscopy (EELS) techniques, respectively. The surface of Ti3SiC2 is characterized by means of X-ray photoelectron spectroscopy (XPS). High resolution C 1s, Si 2p, Ti 2p, Ti 3s core level spectra are explained in terms of crystallographic and electronic structure. Valence band spectrum is performed to confirm the validity of the theoretical calculations.

Dimension effects on the dielectric properties of fine BaTiO_3 ceramics

It is found that the core-shell structured grains are easy to produce for fine grain doped BaTiO3 ceramics in the sintering process. We study the influence of the core-shell structure on the Curie-Weiss temperature and dielectric properties of BaTiO3 ceramics by using effective medium approximation （EMA）. Considering the second approximation, the dielectric properties of fine grain doped BaTiO3 ceramics are consistent with experimental data.

Effect of sintering temperature on microstructure and properties of 3D printing polysilazane reinforced Al_(2)O_(3)core

Ceramic cores are the key intermediate components of hollow blades for aero-engine.Conventional processes,such as hot-press molding and gel film casting,face difficulties in fabricating complex-structured ceramic cores due to the complexity of moulds and long process cycles.Stereolithography 3D printing provides a new idea for the fabrication of complex-structured ceramic cores.The effect of sintering temperature on open porosity,bulk density,weight loss rate,shrinkage rate,flexural strength and microstructure of the Al_(2)O_(3)-based ceramic core doped with 10vol.%polysilazane(PSZ)was studied.The sintering mechanism of PSZ-reinforced ceramic cores was analyzed.Results show that the optimum sintering temperature of PSZ-reinforced ceramic cores is 1,450°C.At this temperature,the open porosity of the ceramic core is 36.60%,bulk density is 2.33 g·cm^(-3),weight loss rate is 22.11%,shrinkage rate along the X,Y,Z directions is 5.72%,5.01%,9.61%,respectively;the flexural strength is 28.794 MPa at 25°C and 13.649 MPa at 1,500°C.Properties of 3D printing PSZ-reinforced ceramic cores can meet the casting requirement of superalloy hollow blades,which is expected to promote the industrial application of 3D printing complex structure ceramic cores.

黏结剂喷射制备陶瓷型芯抗弯强度、尺寸精度及表面质量影响因素的研究进展

黏结剂喷射因具有低成本和可控性优势而在陶瓷型芯的制备中得到广泛的应用,但制备陶瓷型芯的抗弯强度、尺寸精度和表面质量一般较低,而这些不足可以通过改变制备工艺参数来进行改进。综述了粉末、黏结剂、成形工艺和后处理工艺这4个方面的参数对陶瓷型芯抗弯强度、尺寸精度和表面质量的影响,提出了提高黏结剂喷射制备陶瓷型芯抗弯强度、尺寸精度和表面质量的未来发展方向。

浸渗处理及真空度对喷射粘结成形氧化钙基陶瓷型芯性能影响

采用喷射粘结成形技术,以重质碳酸钙作为原料,浸渗纳米ZrO2分散液后烧结得到了氧化钙基陶瓷型芯,研究了浸渗处理以及浸渗真空度对陶瓷型芯性能的影响。研究发现,浸渗处理后的陶瓷型芯内部生成了大量CaZrO3,使内部孔隙减少,微观组织更加致密,弯曲强度最大增加幅度为277.87%。浸渗处理时增大真空度可以进一步改善陶瓷型芯的性能,当真空度从0增加至0.05 MPa时,弯曲强度由7.15 MPa提升到8.88 MPa,但当真空度进一步增加至0.08 MPa时,弯曲强度却降至6.85 MPa,陶瓷型芯性能降低。不同处理工艺烧结后得到的陶瓷型芯浸泡在热水中5 min后即开始溃散,表现出良好的可溶性。

高温合金熔模精密铸造陶瓷型芯研究进展

陶瓷型芯广泛应用于飞机发动机涡轮叶片的熔模精密铸造中,以实现涡轮叶片复杂的空心结构。本文介绍了高温合金熔模精密铸造用陶瓷型芯的应用现状,概述了陶瓷型芯的制备工艺和常用基体材料的研究进展,分别对石英玻璃、电熔刚玉、锆英石、氧化钇等基体材料制备陶瓷型芯的优缺点和研究进展进行了概述。

石英玻璃粉含量对氧化镁基陶瓷型芯性能的影响

利用X射线衍射、扫描电子显微镜及能谱仪等手段研究了矿化剂(石英玻璃粉)含量对氧化镁基陶瓷型芯物相组成、微观组织、烧结收缩率、显孔隙率、线热膨胀系数、室温抗弯强度、高温抗弯强度及型芯浸出率的影响。结果表明:随着石英玻璃粉含量提高,硅酸镁含量增加,陶瓷基体颗粒细化,由连通大孔隙向封闭小孔隙转变,颗粒间结合松散,脱除性能及抗弯强度大幅下降;添加30%SiO_(2)得到的氧化镁基陶瓷型芯综合性能最佳,其中烧结收缩率为2.8%,显孔隙率为32.9%,室温抗弯强度为15.1 MPa,采用体积浓度40%的CH3COOH水溶液浸泡120 h后型芯的浸出率为61.9%。

Manufacturing of ceramic cores:From hot injection to 3D printing

With the improvement of aero-engine performance,the preparation of hollow blades of single-crystal superalloys with complex inner cavity cooling structures is becoming increasingly urgent.The ceramic core is the key intermediate part of the preparation and has attracted wide attention.To meet this challenge,new technologies that can make up for the defects of long periods and high costs of fabricating complex structural cores by traditional hot injection technology are needed.Vat photopolymerization 3D printing ceramic technology has been applied to the core field to realize the rapid preparation of complex structural cores.However,the industrial application of this technology still needs further research and improvement.Herein,ceramic cores were prepared using traditional hot injection and vat photopolymerization 3D printing techniques using fused silica,nano-ZrO_(2),and Al_(2)O_(3) powders as starting materials.The 3D printed ceramic core has a typical layered structure with a small pore size and low porosity.Because of the layered structure,the pore area is larger than that of the hot injection ceramic core,the leaching performance has little effect(0.0277 g/min for 3D printing cores,0.298 g/min for hot injection cores).In the X and Y directions,the sintering shrinkage is low(2.7%),but in the Z direction,the shrinkage is large(4.7%).The fracture occurs when the inner layer crack expands and connects with the interlayer crack,forming a stepped fracture in the 3D-printed cores.The bending strength of the 3D printed core at high temperature(1500℃)is 17.3 MPa.These analyses show that the performance of vat photopolymerization 3D-printed ceramic cores can meet the casting requirements of single crystal superalloy blades,which is a potential technology for the preparation of complex structure ceramic cores.The research mode of 3D printing core technology based on the traditional hot injection process provides an effective new idea for promoting the industrial application of 3D printing core technology.

氧化铝改性硅基陶瓷型芯制备及结晶动力学

氧化铝是硅基陶瓷型芯中的常用矿化剂,但其对石英析晶的促进或抑制作用却存在两种相反的结论。为探究不同氧化铝添加剂对硅基陶瓷型芯性能与析晶行为的影响,分别采用高纯氧化铝、普通氧化铝作为矿化剂,制备氧化铝改性硅基陶瓷型芯。高纯氧化铝粉对方石英的析晶起到抑制作用,而普通氧化铝粉反而促进方石英的析晶。普通氧化铝粉比高纯氧化铝粉含有更多的碱金属、碱土金属氧化物杂质,这些氧化物作为网络修饰体降低结晶活化能,促进方石英的析晶。两种氧化铝矿化剂对型芯的线收缩率、致密化和力学性能影响表现出很大差异。由于普通氧化铝粉促进方石英析晶和烧结致密化,显著提高型芯的抗蠕变能力。当普通氧化铝粉加入量为5%(质量分数)时,陶瓷型芯表现出良好的综合性能,其收缩率为0.63%,室温弯曲强度为20.2 MPa,1540℃/0.5 h双支点挠度为0.23 mm,可满足精密铸造对型芯的要求。

浅谈预埋陶瓷型芯工艺对钛合金铸件尺寸的影响

通过分析铸件和蜡模上孔槽深度尺寸数据,研究了两种陶瓷型芯定位方式对铸件孔槽深度尺寸的影响。研究表明,采用变尺寸陶瓷型芯定位方式,可以有效保证蜡模和铸件孔槽深度尺寸精度。

碳化硼对硅基陶瓷型芯性能的影响研究

以石英玻璃粉作为基体材料,添加0~1wt.%的碳化硼为矿化剂,通过热压注法制备了硅基陶瓷型芯,探究了不同碳化硼含量对硅基陶瓷型芯综合性能影响的变化规律。试验结果表明:随着碳化硼含量的增加,样品的收缩率和体积密度逐渐增大,气孔率逐渐减小。此外,室温抗弯强度和高温抗弯强度随着碳化硼含量的增加先增大后减小,高温挠度先减小后增大;当碳化硼含量为0.3wt.%时,陶瓷型芯综合性能得到大幅度改善,收缩率为1.44%,体积密度为1.67 g/cm^(3),气孔率达到25.51%,室温抗弯强度为16.32 MPa,高温抗弯强度为33.2 MPa,高温挠度为0.19 mm。

Ni–MgO核–壳纳米粉体的制备

采用包覆热分解烧结法,制备了多层陶瓷电容器内部电极用MgO包覆Ni纳米粉体,讨论了反应物浓度和分散剂含量对包覆纳米镍盐前驱体颗粒大小和均匀性的影响,分析了还原烧结温度对包覆纳米Ni粉球形度和分散性的影响,并利用X射线衍射仪、扫描电镜、透射电镜、热机械分析仪对MgO包覆纳米Ni粉进行了表征分析。结果表明:反应物浓度达到足以引起反应爆炸成核时,能够获得纳米镍盐颗粒;添加适量的分散剂,可以得到分散良好的纳米镍盐前驱体颗粒;还原烧结温度700℃时,可以获得球形度和分散性良好的MgO包覆纳米Ni粉;MgO包覆在纳米Ni粉表面,形成了核壳结构,该纳米Ni粉具有良好的收缩延迟效果。

数字化辅助一体化纤维桩核及树脂基陶瓷冠修复冠折年轻恒牙1例

桩核修复是临床常见的牙体缺损修复方式,临床常用桩核主要有玻璃纤维预成桩树脂核和个性化一体式桩核。在个性化桩核的材料选择上,由于金属的美观缺陷及氧化锆的弹性模量限制,兼具个性化、机械性能及美学优势的一体化玻璃纤维桩核作为一种新型桩核形式被临床所应用。本文报告1例CAD/CAM一体化纤维树脂桩核及树脂基陶瓷冠修复年轻恒牙冠折的临床病例。

10种有机酸对电子烟中陶瓷雾化芯的重金属迁移影响

为研究10种有机酸对电子烟中陶瓷雾化芯的重金属迁移影响,配制不同含量有机酸的电子烟烟液,采用电感耦合等离子体质谱法(ICP-MS)对陶瓷雾化芯在加速老化条件下迁移至烟液及气溶胶中的金属元素进行测定,评估重金属在该陶瓷芯中的雾化效率及有机酸的影响。结果表明:烟液、气溶胶方法中各元素的检出限分别均<10µg/kg、≤0.055µg/100口;不同类型和含量的有机酸对重金属的迁移影响不一,柠檬酸、乳酸、苹果酸、乙酸对金属元素的迁移影响相对较大。各元素在气溶胶中的雾化效率为21.2%~45.9%。与未添加有机酸的空白对照组相比,柠檬酸、乳酸、乙酸、苯甲酸、苹果酸对气溶胶中Ni含量提升有显著影响(P<0.05),柠檬酸对气溶胶中Cu含量提升有显著影响,5种酸对其他元素无显著性差异(P>0.05)。该方法准确可靠,适用于评估电子烟烟液及气溶胶中有机酸对陶瓷芯的重金属迁移影响。

Slurry flow characteristics control of 3D printed ceramic core layered structure:Experiment and simulation

Vat photopolymerization 3D printing ceramic technology provides a feasible process for the preparation of complex internal cooling channels for aeroengine single crystal superalloy hollow blades.However,the typical layered structure characteristics of 3D printing ceramic technology led to the anisotropy of ceramic core strength and sintering shrinkage,which greatly affects the performance and accuracy of the complex structure core and requires further research and improvement.Herein,the influence of the thickness of the slurry layer on the flow characteristics of the slurry in the process of the vat photopolymerization 3D printing slurry spreading was systematically studied by the method of simulation and experiment.The simulation results show that the positions of the turbulent zone and maximum velocity zone in the scraper front affect the redistribution of powder particles with different sizes.The layered structure was caused by the redistribution of ceramic particles of different sizes in the slurry layer.By controlling the turbulent flow zone and the maximum velocity zone of the scraper leading edge,the phenomenon of laminar flow can be weakened and the particle redistribution can be improved.With the increase of the thickness of the printing layer,the layered structure appears gradually,and the pores at the interface of the layered structure gradually concentrated into the interfacial pore lines from the uniform distribution,and the crack propagation changes from intergranular micro-crack to interlayer macro-crack.The combination of finite element simulation and experiment,through the slurry flow characteristics to control the layered structure of reductive vat photopolymerization ceramic core 3D printing,the control of crack propagation mode,element distribution and pore evolution of the core was accomplished,which lays a foundation for the performance control of ceramic 3D printing technology.