High-performance yttrium oxide-phenolic resin(Y_(2)O_(3)-PF)alternating coating was prepared on epoxy resin-based composite material using supersonic plasma spraying and dual-channel powder feeding technique.Y_(2)O_(3...High-performance yttrium oxide-phenolic resin(Y_(2)O_(3)-PF)alternating coating was prepared on epoxy resin-based composite material using supersonic plasma spraying and dual-channel powder feeding technique.Y_(2)O_(3)-coated PF(Y_(2)O_(3)/PF)powder was firstly sprayed onto the substrate,forming a transition layer,and then the spherical Y_(2)O_(3) powder and Y_(2)O_(3)/PF powder were alternately deposited to form the composite alternating coating.Results show that the alternating coating is mainly composed of deposited Y_(2)O_(3)/PF powder.The bonding strength between coating and substrate is as high as 26.48 MPa with the single-test maximum bonding strength of 28.10 MPa,and shear strength reaches 24.30 MPa.Additionally,the heat transfer effect caused by external Y_(2)O_(3) particles gradually softens and even melts PF,thus effectively avoiding the damage of high temperature to molecular structure and thereby promoting the crosslinking and curing effects of resin during the deposition process.In the meantime,the unmelted Y_(2)O_(3) powder results in the shot peening effect,which washes out and eliminates the powder particles with inferior deposition effect,ultimately improving the physical and chemical properties of the alternating coating.展开更多
A series of high solid content(30 wt%)epoxy resin(EP)composite coatings reinforced with differently sized cubic boron nitride(CBN)particles were fabricated successfully on 304 L stainless steel.Polydopamine(PDA)was us...A series of high solid content(30 wt%)epoxy resin(EP)composite coatings reinforced with differently sized cubic boron nitride(CBN)particles were fabricated successfully on 304 L stainless steel.Polydopamine(PDA)was used to improve the dispersibility of CBN particles in EP.The structural and morphological features of the CBN particles and the composite coatings were characterized by Raman spectroscopy,scanning electron microscopy(SEM),and transmission electron microscopy(TEM).Moreover,a UMT-3 tribometer and surface profiler were used to investigate the tribological behaviors of the as-prepared composite coatings.Electrochemical impedance spectroscopy(EIS)and Tafel analysis were used to investigate the coatings'anti-corrosion performance.The results demonstrated that the CBN fillers could effectively enhance the tribological and anti-corrosion properties of the EP composite coatings.In addition,when the additive proportion of the microsized(5μm)and nanosized(550 nm)CBN particles was 1:1,the tribological property of the EP composite coatings was optimal for dry sliding,which was attributed to the load carrying capability of the microsized CBN particles and the toughening effect of the nanosized CBN particles.However,when the additive proportion of the microsized and nanosized CBN particles was 2:1,the tribology and corrosion resistance performance were optimal in seawater conditions.We ascribed this to the load-carrying capacity of the microparticles,which played a more important role under the seawater lubrication condition,and the more compact structure,which improved the electrolyte barrier ability for the composite coatings.展开更多
The present status and development trends of nano-composite coatings were briefly introduced. The nano-SiO2 was dispersed into crylic acid resin by ultrasonic wave and high-energy ball milling, the influence of nano-S...The present status and development trends of nano-composite coatings were briefly introduced. The nano-SiO2 was dispersed into crylic acid resin by ultrasonic wave and high-energy ball milling, the influence of nano-SiO2 on shielding property of coatings was investigated. Relation between particle size distribution of original nano-SiO2 and its dispersal in water and alcohol after treatment were analyzed, respectively. The ultraviolet permeation rate of coatings filled with nano-SiO2 was detected by ultraviolet spectral photometer. And the particle size distribution of coatings was examined by TEM. The results show that particle size distribution is comparative convergence and smaller one order of magnitude after dispersal treatment. The size of most nano-SiO2 in coatings is smaller than 100nm, which indicates that the amount of nano-SiO2 in the resin is 20% （solid content of resin）, the permeation rate of ultraviolet of composite coatings decreases to 20%. The research of its excellent ultraviolet shielding property mechanism indicates minor size and high surface energy of nano-SiO2 can produce different absorption, reflection and scatter actions to different wavelengths.展开更多
基金National Natural Science Foundation of China(52130509,52275211,52075542)Supported by 145 Project+1 种基金Science and Technology New Star Project of Shaanxi Innovation Capability Support Program(2021KJXX-38)China Postdoctoral Science Foundation(2021M693883)。
文摘High-performance yttrium oxide-phenolic resin(Y_(2)O_(3)-PF)alternating coating was prepared on epoxy resin-based composite material using supersonic plasma spraying and dual-channel powder feeding technique.Y_(2)O_(3)-coated PF(Y_(2)O_(3)/PF)powder was firstly sprayed onto the substrate,forming a transition layer,and then the spherical Y_(2)O_(3) powder and Y_(2)O_(3)/PF powder were alternately deposited to form the composite alternating coating.Results show that the alternating coating is mainly composed of deposited Y_(2)O_(3)/PF powder.The bonding strength between coating and substrate is as high as 26.48 MPa with the single-test maximum bonding strength of 28.10 MPa,and shear strength reaches 24.30 MPa.Additionally,the heat transfer effect caused by external Y_(2)O_(3) particles gradually softens and even melts PF,thus effectively avoiding the damage of high temperature to molecular structure and thereby promoting the crosslinking and curing effects of resin during the deposition process.In the meantime,the unmelted Y_(2)O_(3) powder results in the shot peening effect,which washes out and eliminates the powder particles with inferior deposition effect,ultimately improving the physical and chemical properties of the alternating coating.
基金the National Natural Science Foundation of China(No.51775540)Key Research Program of Frontier Sciences of the Chinese Academy of Science(No.QYZDY-SSW-JSC009)the Youth Innovation Promotion Association,CAS(No.2017338)。
文摘A series of high solid content(30 wt%)epoxy resin(EP)composite coatings reinforced with differently sized cubic boron nitride(CBN)particles were fabricated successfully on 304 L stainless steel.Polydopamine(PDA)was used to improve the dispersibility of CBN particles in EP.The structural and morphological features of the CBN particles and the composite coatings were characterized by Raman spectroscopy,scanning electron microscopy(SEM),and transmission electron microscopy(TEM).Moreover,a UMT-3 tribometer and surface profiler were used to investigate the tribological behaviors of the as-prepared composite coatings.Electrochemical impedance spectroscopy(EIS)and Tafel analysis were used to investigate the coatings'anti-corrosion performance.The results demonstrated that the CBN fillers could effectively enhance the tribological and anti-corrosion properties of the EP composite coatings.In addition,when the additive proportion of the microsized(5μm)and nanosized(550 nm)CBN particles was 1:1,the tribological property of the EP composite coatings was optimal for dry sliding,which was attributed to the load carrying capability of the microsized CBN particles and the toughening effect of the nanosized CBN particles.However,when the additive proportion of the microsized and nanosized CBN particles was 2:1,the tribology and corrosion resistance performance were optimal in seawater conditions.We ascribed this to the load-carrying capacity of the microparticles,which played a more important role under the seawater lubrication condition,and the more compact structure,which improved the electrolyte barrier ability for the composite coatings.
文摘The present status and development trends of nano-composite coatings were briefly introduced. The nano-SiO2 was dispersed into crylic acid resin by ultrasonic wave and high-energy ball milling, the influence of nano-SiO2 on shielding property of coatings was investigated. Relation between particle size distribution of original nano-SiO2 and its dispersal in water and alcohol after treatment were analyzed, respectively. The ultraviolet permeation rate of coatings filled with nano-SiO2 was detected by ultraviolet spectral photometer. And the particle size distribution of coatings was examined by TEM. The results show that particle size distribution is comparative convergence and smaller one order of magnitude after dispersal treatment. The size of most nano-SiO2 in coatings is smaller than 100nm, which indicates that the amount of nano-SiO2 in the resin is 20% （solid content of resin）, the permeation rate of ultraviolet of composite coatings decreases to 20%. The research of its excellent ultraviolet shielding property mechanism indicates minor size and high surface energy of nano-SiO2 can produce different absorption, reflection and scatter actions to different wavelengths.