Firm joins were obtained between Ti（C,N）-based cermet and steel with Ag-Cu-Zn-Ni filler metal by vacuum brazing. The effects of technological parameters such as brazing temperature, holding time, and filler thicknes...Firm joins were obtained between Ti（C,N）-based cermet and steel with Ag-Cu-Zn-Ni filler metal by vacuum brazing. The effects of technological parameters such as brazing temperature, holding time, and filler thickness on the shear strength of the joints were investigated. The microstructure of welded area and the reaction products of the filler metal were examined by scanning electron microscopy （SEM）, metallographic microscope （OM）, energy-dispersive X-ray analysis （EDS）, and X-ray diffraction （XRD）. The brazing temperature of 870℃, holding time of 15 min, and filler thickness of 0.4 mm are a set of optimum technological parameters, under which the maximum shear strength of the joints, 176.5 MPa, is achieved. The results of microstructure show that the wettability of the filler metal on Ti（C,N）-based cermet and steel is well. A mutual solution layer and a diffusion layer exist between the welding base materials and the filler metal.展开更多
With BrazeTec BlueBraze the manufacturers in HVACR industry have an alternative filler metal with 10 weight-% less silver but same brazing temperatures. The performance of these new alloys has been evaluated in severa...With BrazeTec BlueBraze the manufacturers in HVACR industry have an alternative filler metal with 10 weight-% less silver but same brazing temperatures. The performance of these new alloys has been evaluated in several tests. The evaluation included wetting investigations, metallographic examinations, joint strength at different temperatures and pulsation and corrosion resistance. The results of these tests will be presented in this paper.展开更多
The brazing process of cubic boron nitride （CBN） grains and AISI 1045 steel with AgCuTi-TiC mixed powder as a filler material was carried out.The joining strength and the interfacial microstructure were investigated...The brazing process of cubic boron nitride （CBN） grains and AISI 1045 steel with AgCuTi-TiC mixed powder as a filler material was carried out.The joining strength and the interfacial microstructure were investigated.The experimental results indicate that the spreading of the molten filler material on AISI 1045 steel is decreased with the increase of TiC content.A good interface is formed between the TiC particulates and AgCuTi alloy through the wetting behavior.In the case of AgCuTi＋16wt% TiC,the strength of the brazed steel-to-steel joints reached the highest value of 95MPa dependent upon the reinforcement effect of TiC particles within the filler layer.Brazing resultants of TiB2,TiB,and TiN are produced at the interface of the CBN grains and the AgCuTi-TiC filler layer by virtue of the interdiffusion of B,N,and Ti atoms.展开更多
基金supported by the National Natural Science Foundation of China (No. 50074014)
文摘Firm joins were obtained between Ti（C,N）-based cermet and steel with Ag-Cu-Zn-Ni filler metal by vacuum brazing. The effects of technological parameters such as brazing temperature, holding time, and filler thickness on the shear strength of the joints were investigated. The microstructure of welded area and the reaction products of the filler metal were examined by scanning electron microscopy （SEM）, metallographic microscope （OM）, energy-dispersive X-ray analysis （EDS）, and X-ray diffraction （XRD）. The brazing temperature of 870℃, holding time of 15 min, and filler thickness of 0.4 mm are a set of optimum technological parameters, under which the maximum shear strength of the joints, 176.5 MPa, is achieved. The results of microstructure show that the wettability of the filler metal on Ti（C,N）-based cermet and steel is well. A mutual solution layer and a diffusion layer exist between the welding base materials and the filler metal.
文摘With BrazeTec BlueBraze the manufacturers in HVACR industry have an alternative filler metal with 10 weight-% less silver but same brazing temperatures. The performance of these new alloys has been evaluated in several tests. The evaluation included wetting investigations, metallographic examinations, joint strength at different temperatures and pulsation and corrosion resistance. The results of these tests will be presented in this paper.
基金supported by the National Basic Research Priorities Program of China (No.2009CB724403)the National Natural Science Foundation of China (No.51005116)+1 种基金the Natural Science Foundation of Jiangsu Province,China (No.BK2010496)the Ph.D. Program Foundation of Ministry of Education of China (No.20103218120026)
文摘The brazing process of cubic boron nitride （CBN） grains and AISI 1045 steel with AgCuTi-TiC mixed powder as a filler material was carried out.The joining strength and the interfacial microstructure were investigated.The experimental results indicate that the spreading of the molten filler material on AISI 1045 steel is decreased with the increase of TiC content.A good interface is formed between the TiC particulates and AgCuTi alloy through the wetting behavior.In the case of AgCuTi＋16wt% TiC,the strength of the brazed steel-to-steel joints reached the highest value of 95MPa dependent upon the reinforcement effect of TiC particles within the filler layer.Brazing resultants of TiB2,TiB,and TiN are produced at the interface of the CBN grains and the AgCuTi-TiC filler layer by virtue of the interdiffusion of B,N,and Ti atoms.