The preparation procedure of DD5 single crystal castings was optimized. The microstructure characteristics of DD5 single crystal superalloy were investigated by microstructure observation and segregation behavior exam...The preparation procedure of DD5 single crystal castings was optimized. The microstructure characteristics of DD5 single crystal superalloy were investigated by microstructure observation and segregation behavior examination. The results show that the grain orientation is optimized by constraining the spiral crystallizer in [001] orientation and spatial scale. Also, the γ＇ phase of inter-dendrites is larger and more irregular than that in dendrite arms. High temperature tensile tests of DD5 single crystal castings exhibit that the peak stress increases with increasing temperature, while the area reduction shows an opposite trend, when the temperature is below 800℃; meanwhile, when the temperature is between 800℃ and 1000℃, the fracture stress of the alloy is the same as the peak stress. The fracture mode changes from shear to ductile with increasing temperature from 600℃ and 1000℃.展开更多
Crystallization growth of single-crystal Cu by continuous casting has been investigated using self-designed horizontal continuous casting equipment and XRD. Experimental results showed that the crystallization plane o...Crystallization growth of single-crystal Cu by continuous casting has been investigated using self-designed horizontal continuous casting equipment and XRD. Experimental results showed that the crystallization plane of (311), (220) and (ill) were eliminated sequentially in evolutionary process. The final growth plane of crystal was (200), the direction of crystallization was [100], the growth direction of both sides of the rod inclined to axis, and the degree of deviation of direction [100] from the crystal axis was less than 10°. In order to produce high quality single crystal, the solid-liquid interface morphology must be smooth, even be planar.展开更多
基金financially supported by Jiangsu Industrial Support Project (Nos. BE2014007-2, BE2014007-3, and BE2014007-4)the financial support from Jiangsu Development and Reform Commission (No. [2013]2027)Jiangsu Postgraduates Innovating Scientific Research Project (No. KYLX15-1061)
文摘The preparation procedure of DD5 single crystal castings was optimized. The microstructure characteristics of DD5 single crystal superalloy were investigated by microstructure observation and segregation behavior examination. The results show that the grain orientation is optimized by constraining the spiral crystallizer in [001] orientation and spatial scale. Also, the γ＇ phase of inter-dendrites is larger and more irregular than that in dendrite arms. High temperature tensile tests of DD5 single crystal castings exhibit that the peak stress increases with increasing temperature, while the area reduction shows an opposite trend, when the temperature is below 800℃; meanwhile, when the temperature is between 800℃ and 1000℃, the fracture stress of the alloy is the same as the peak stress. The fracture mode changes from shear to ductile with increasing temperature from 600℃ and 1000℃.
文摘Crystallization growth of single-crystal Cu by continuous casting has been investigated using self-designed horizontal continuous casting equipment and XRD. Experimental results showed that the crystallization plane of (311), (220) and (ill) were eliminated sequentially in evolutionary process. The final growth plane of crystal was (200), the direction of crystallization was [100], the growth direction of both sides of the rod inclined to axis, and the degree of deviation of direction [100] from the crystal axis was less than 10°. In order to produce high quality single crystal, the solid-liquid interface morphology must be smooth, even be planar.