低约束试件断裂韧性测试对油气管道安全运营具有重要意义。本文回顾了低约束试件断裂韧性测试方法及发展过程,介绍了裂纹尖端张开位移(crack tip opening displacement,CTOD)和J积分等常用断裂韧性表征参数,并对断裂韧性测试中应力强度...低约束试件断裂韧性测试对油气管道安全运营具有重要意义。本文回顾了低约束试件断裂韧性测试方法及发展过程,介绍了裂纹尖端张开位移(crack tip opening displacement,CTOD)和J积分等常用断裂韧性表征参数,并对断裂韧性测试中应力强度因子、J积分塑性因子、J积分与CTOD转换因子、裂纹尺寸测量方法、数字图像相关方法等关键问题进行对比分析,总结需要深入研究的问题,为低约束试件断裂韧性测试发展提供一定依据。展开更多
In this context,four specimens,i.e.(i)circumferentially notched cylindrical torsion(CNCT),(ii)circum-ferentially notched cylindrical direct tension(CNCDT),(iii)edge notch disc bend(ENDB)and(iv)three-point bend beam(3P...In this context,four specimens,i.e.(i)circumferentially notched cylindrical torsion(CNCT),(ii)circum-ferentially notched cylindrical direct tension(CNCDT),(iii)edge notch disc bend(ENDB)and(iv)three-point bend beam(3PBB),were utilized to measure the modesⅠandⅢfracture toughness values of gypsum.While the CNCT specimen provides pure modeⅢloading in a direct manner,this pure mode condition is indirectly produced by the ENDB specimen.The ENDB specimen provided lower KⅢc and a non-coplanar(i.e.twisted)fracture surface compared with the CNCT specimen,which showed a planar modeⅢfracture surface.The ENDB specimen is also employed for conducting pure modeⅠ(with different crack depths)and mixed modeⅠ/Ⅲtests.KIc value was independent of the notch depth,and it was consistent with the RILEM and ASTM standard methods.But the modeⅢfracture results were highly sensitive to the notch depth.While the fracture resistance against modeⅢwas significantly lower than that of modeⅠ,the greater work of fracture under modeⅢwas noticeable.展开更多
Abstract： An effective approach was conducted for estimating fracture toughness using the crack opening displacement （COD） method for plasma enhanced chemical vapor deposition （PECVD） coating materials. For this ...Abstract： An effective approach was conducted for estimating fracture toughness using the crack opening displacement （COD） method for plasma enhanced chemical vapor deposition （PECVD） coating materials. For this evaluation, an elastoplastic analysis was used to estimate critical COD values for single edge notched bending （SENB） specimens. The relationship between fracture toughness （Kic） and critical COD for SENB specimens was obtained. Microstructure of the interface between AleO3-TiO2 composite ceramic coatings and AISI 1045 steel substrates was studied by using scanning electron microscope （SEM）. Chemical compositions were clarified by energy-dispersive X-ray spectroscopy （EDS）. The results show that the interface between of Al203-TiO2 and substrate has mechanical combining. The nanohardness of the coatings can reach 1 200 GPa examined by nanoindentation. The Klc was calculated according to this relationship from critical COD. The bending process produces a significant relationship of COD independent of the axial force applied. Fractographic analysis was conducted to determine the crack length. From the physical analysis of nanoindentation curves, the elastic modulus of 1045/AI2O3-TiO2 is 180 GPa for the 50 μm film. The highest value of fracture toughness for 1045/A1203-TiO2-250 μm is 348 MPa·mv2.展开更多
文摘低约束试件断裂韧性测试对油气管道安全运营具有重要意义。本文回顾了低约束试件断裂韧性测试方法及发展过程,介绍了裂纹尖端张开位移(crack tip opening displacement,CTOD)和J积分等常用断裂韧性表征参数,并对断裂韧性测试中应力强度因子、J积分塑性因子、J积分与CTOD转换因子、裂纹尺寸测量方法、数字图像相关方法等关键问题进行对比分析,总结需要深入研究的问题,为低约束试件断裂韧性测试发展提供一定依据。
文摘In this context,four specimens,i.e.(i)circumferentially notched cylindrical torsion(CNCT),(ii)circum-ferentially notched cylindrical direct tension(CNCDT),(iii)edge notch disc bend(ENDB)and(iv)three-point bend beam(3PBB),were utilized to measure the modesⅠandⅢfracture toughness values of gypsum.While the CNCT specimen provides pure modeⅢloading in a direct manner,this pure mode condition is indirectly produced by the ENDB specimen.The ENDB specimen provided lower KⅢc and a non-coplanar(i.e.twisted)fracture surface compared with the CNCT specimen,which showed a planar modeⅢfracture surface.The ENDB specimen is also employed for conducting pure modeⅠ(with different crack depths)and mixed modeⅠ/Ⅲtests.KIc value was independent of the notch depth,and it was consistent with the RILEM and ASTM standard methods.But the modeⅢfracture results were highly sensitive to the notch depth.While the fracture resistance against modeⅢwas significantly lower than that of modeⅠ,the greater work of fracture under modeⅢwas noticeable.
基金Project supported by the National Research Foundation of Korea(2011-0030804)the Korea Research Foundation(KRF2009-0076450)funded by the Korea Government(MEST)
文摘Abstract： An effective approach was conducted for estimating fracture toughness using the crack opening displacement （COD） method for plasma enhanced chemical vapor deposition （PECVD） coating materials. For this evaluation, an elastoplastic analysis was used to estimate critical COD values for single edge notched bending （SENB） specimens. The relationship between fracture toughness （Kic） and critical COD for SENB specimens was obtained. Microstructure of the interface between AleO3-TiO2 composite ceramic coatings and AISI 1045 steel substrates was studied by using scanning electron microscope （SEM）. Chemical compositions were clarified by energy-dispersive X-ray spectroscopy （EDS）. The results show that the interface between of Al203-TiO2 and substrate has mechanical combining. The nanohardness of the coatings can reach 1 200 GPa examined by nanoindentation. The Klc was calculated according to this relationship from critical COD. The bending process produces a significant relationship of COD independent of the axial force applied. Fractographic analysis was conducted to determine the crack length. From the physical analysis of nanoindentation curves, the elastic modulus of 1045/AI2O3-TiO2 is 180 GPa for the 50 μm film. The highest value of fracture toughness for 1045/A1203-TiO2-250 μm is 348 MPa·mv2.