Zn-Cr coating was prepared on the surface of sintered NdFeB permanent magnet samples and preparation parameters were established. The anticorrosive property of Zn-Cr coating on NdFeB was studied by whole-immersion tes...Zn-Cr coating was prepared on the surface of sintered NdFeB permanent magnet samples and preparation parameters were established. The anticorrosive property of Zn-Cr coating on NdFeB was studied by whole-immersion test in NaCl solution and compared with that of zinc plating and nickel plating on NdFeB. Open-circuit potential and self-corrosion current of NdFeB samples with and without Zn-Cr coating were measured. The micro-morphology and composition of Zn-Cr coming were analyzed through SEM, XPS, EDS and XRD. The effect of Zn-Cr coating on magnetic property of NdFeB magnet was also investigated. It is exposed that Zn-Cr coating is anodic type coating for NdFeB magnet, and provided substrate electrochemical protection, barrier protection and passivation protection. The anticorrosion property of NdFeB magnet is obviously enhanced by Zn-Cr coating while the magnet property of NdFeB magnet changed little.展开更多
The Ni-P/TiO2 composite film on sintered NdFeB permanent magnet was investigated by X-ray diffraction （XRD）,environmental scanning electron microscopy （ESEM）,and energy dispersive X-ray spectrometer （EDX）. The c...The Ni-P/TiO2 composite film on sintered NdFeB permanent magnet was investigated by X-ray diffraction （XRD）,environmental scanning electron microscopy （ESEM）,and energy dispersive X-ray spectrometer （EDX）. The corrosion resistance of Ni-P/TiO2 film coated on NdFeB magnet,in 0.5 mol/L NaCl solution,was studied by potentiodynamic polarization,salt spray test and electrochemical impedance spectroscopy （EIS） techniques. The self-corrosion current density （icorr） and the polarization resistance （Rp） of Ni-P/TiO2 film are 0.22 μA/cm2 （about 14% of that of Ni-P coating）,and 120 kΩ·cm2 （about 2 times of that of Ni-P coating）,respectively. The anti-salt spray time of Ni-P/TiO2 film is about 2.5 times of that of the Ni-P coating. The results indicate that Ni-P/TiO2 film has a better corrosion resistance than Ni-P coating,and the composite film increases the corrosion resistance of NdFeB magnet markedly.展开更多
文摘Zn-Cr coating was prepared on the surface of sintered NdFeB permanent magnet samples and preparation parameters were established. The anticorrosive property of Zn-Cr coating on NdFeB was studied by whole-immersion test in NaCl solution and compared with that of zinc plating and nickel plating on NdFeB. Open-circuit potential and self-corrosion current of NdFeB samples with and without Zn-Cr coating were measured. The micro-morphology and composition of Zn-Cr coming were analyzed through SEM, XPS, EDS and XRD. The effect of Zn-Cr coating on magnetic property of NdFeB magnet was also investigated. It is exposed that Zn-Cr coating is anodic type coating for NdFeB magnet, and provided substrate electrochemical protection, barrier protection and passivation protection. The anticorrosion property of NdFeB magnet is obviously enhanced by Zn-Cr coating while the magnet property of NdFeB magnet changed little.
基金Sponsored by Hi-Tech Research and Development Program of China (2003AA305120)
文摘The Ni-P/TiO2 composite film on sintered NdFeB permanent magnet was investigated by X-ray diffraction （XRD）,environmental scanning electron microscopy （ESEM）,and energy dispersive X-ray spectrometer （EDX）. The corrosion resistance of Ni-P/TiO2 film coated on NdFeB magnet,in 0.5 mol/L NaCl solution,was studied by potentiodynamic polarization,salt spray test and electrochemical impedance spectroscopy （EIS） techniques. The self-corrosion current density （icorr） and the polarization resistance （Rp） of Ni-P/TiO2 film are 0.22 μA/cm2 （about 14% of that of Ni-P coating）,and 120 kΩ·cm2 （about 2 times of that of Ni-P coating）,respectively. The anti-salt spray time of Ni-P/TiO2 film is about 2.5 times of that of the Ni-P coating. The results indicate that Ni-P/TiO2 film has a better corrosion resistance than Ni-P coating,and the composite film increases the corrosion resistance of NdFeB magnet markedly.