PLASTIC DEFORMATION AND DENSIFICATION FOR SINTERED POWDER MATERIALS

Equivalent yield strength of sintered powder materials is determined by experiments,and the following yield condition is constructed based on it.Experiments on uniaxial compression,and plane strain,closed die upsetting have been done using sintered copper,and the relation between the deformation resistance and compactness of the prefabricated preform is analysed.A design principle for the prefabricated preform density is proposed,and the effectiveness of shear plastic deformation to densifleation is pointed out.

Preparation of Giant Mangetostrictive Sintered Compacts by Powder Metallurgy

Powder metallurgy technique was applied to prepare rare earth giant magnetostrictive materials. This preparation process consists of casted Tb0.30Dy0.70 Fe1.80 alloy, in magnetic atmosphere. which is pulverized by ball mill, aligned field, compacted and sintered in inertial The experimental results indicate that when the magnetic field is 240 kA ·m^-1, the sample with particle size less than 0. 147 mm being compacted in magnetic field exhibits 1613 × 10^-3 magnetostriction under a compressive pre-stress 8.0 MPa after being sintered at 1200 ℃ for 2 h and annealed at 950 ℃ for 24 h.

One step sintering of homogenized bauxite raw material and kinetic study

A one-step sintering process of bauxite raw material from direct mining was completed, and the kinetics of this process was analyzed thoroughly. The results show that the sintering kinetics of bauxite raw material exhibits the liquid-phase sintering behavior. A small portion of impurities existed in the raw material act as a liquid phase. After X-ray diffraction analyses, scanning electron microscopy observations, and kinetics calculations, sintering temperature and heating duration were determined as the two major factors contributing to the sintering process and densification of bauxite ore. An elevated heating temperature and longer duration favor the densification process. The major obstacle for the densification of bauxite material is attributed to the formation of the enclosed blowhole during liquid-phase sintering.

Injection molding of ultra-fine Si_3N_4 powder for gas-pressure sintering

The ceramic injection molding technique was used in the gas-pressure sintering of ultra-fine Si3N4 powder. The feedstock＇s flowability, debinding rate, defect evolution, and microstructural evolution during production were explored. The results show that the solid volume loading of less than 50vol% and the surfactant mass fraction of 6wt% result in a perfect flowability of feedstock; this feedstock is suitable for injection molding. When the debinding time is 8 h at 40°C, approximately 50% of the wax can be solvent debinded. Defects detected during the preparation are traced to improper injection parameters, mold design, debinding parameters, residual stress, or inhomogeneous composition distribution in the green body. The bulk density, Vickers hardness, and fracture toughness of the gas-pressure-sintered Si3N4 ceramic reach 3.2 g/cm^3, 16.5 GPa, and 7.2 MPa·m^1/2, respectively.

Vital role of hydroxyapatite particle shape in regulating the porosity and mechanical properties of the sintered scaffolds

The effect of particle shape on the porosity and compressive strength of porous hydroxyapatite （HA） scaffolds was investigated by sintering the mixture of rod-shaped HA （r-HA） and spherical HA （s-HA） with polyacrylamide used as the sacrificial template. It was found, for the first time, that addition of r-HA into s-HA could exponentially decrease the porosity of sintered HA scaffolds and enhance their compressive strength with the increase of r-HA content. The mechanism, according to the results from scanning electron microscopy and X-ray diffraction, lies in the restriction of s-HA to the grain formation and growth of r-HA during sintering and results in the fusion of r-HA with s-HA. These findings suggest that mixture of r-HA and s-HA might provide a new and facile way to improve the compressive strength of oorous HA scaffolds.

Fe/Cu gradient composite materials prepared by laser sintering

USLNG CO2 laser beam as a heat source to sinter whole P/M （powder metallurgy） green com-pact is a new technique. As reported in refs. [1--4], the advantages of the laser sintering ofCu-base and Fe-base green compact were characterized by rapid sintering rate, no contamina-tion, fine structure and good properties.

Design of a Digital Management System for the Sintering Material Ground

There are many kinds and a large number of raw materials in the sintering material ground to be managed,while it is difficult to obtain the precise inventory values,which often leads to high cost.Furthermore,the external factors of material ground are difficult to handle,such as weather variation,order fluctuation,measurement failure and so on.To solve such raw material management problems,a digital management system has been developed.First,the practical requirements and the raw material management processes are analyzed.Then,optimization and prediction methods are used to calculate the inventory according to the practical situation.With the help of practical technologies and production conditions,the developed system has been applied to a large-scale sintering material ground.The practical running results of the application demonstrate the validity of the proposed digital management system.

A sol-gel method to synthesize indium tin oxide nanoparticles

Transparent conductive indium tin oxide （ITO） nanoparticles were synthesized by a novel sol-gel method. Granulated indium and tin were dissolved in HNO3 and partially complexed with citric acid. A sol-gel process was induced when tertiary butyl alcohol was added dropwise to the above solution. ITO nanopartides with an average crystallite size of 18.5 nm and surface area of 32.6 m^2 ]g were obtained after the gel was heat-treated at 700 ℃, The ITO nanoparticles showed good sinterability, the starting sintering temperature decreased sharply to 900 ℃, and the 1400 ℃ sintered pellet had a density of 98.1% of theoretical density （TD）.