The fact that the amount of the mold flux components differs at differentlocations on the cracking surface indicates that the longitudinal surface cracks are initiallyformed in the mold and are enlarged in the seconda...The fact that the amount of the mold flux components differs at differentlocations on the cracking surface indicates that the longitudinal surface cracks are initiallyformed in the mold and are enlarged in the secondary cooling zone. Based on the hot ductilitymeasurement of two typical container used steels, it is known that the steels are in severeembrittlement state in the temperature range of 825-775 deg C. By means of increasing Cr/Ni platingthickness on the upper part of the mold, reducing mold heat flux, adopting new secondary coolingpattern, etc., the occurrence of the surface longitudinal cracks on the steel CC (continuouscasting) slabs has been significantly reduced.展开更多
The correlation between the longitudinal crack occurrence and integrated heat transfer of the mold with data mining methods was investigated.Firstly,three kinds of support vector machine models based on principal comp...The correlation between the longitudinal crack occurrence and integrated heat transfer of the mold with data mining methods was investigated.Firstly,three kinds of support vector machine models based on principal component analysis with different input features were established to explore the effect of integrated heat transfer on the accuracy of the prediction model for the longitudinal crack.The results show that the accuracy was improved while features including mean and standard deviation of integrated heat transfer were added.Then,the difference in integrated heat transfer between defect and normal samples under the same process parameters was quantitatively compared.Compared with normal samples,the temperature difference of cooling water for defect samples decreased by 0.65%,and the temperature difference fluctuation increased by 31.1%.Finally,the literature data were used to provide support for the quantitative correlation according to defect formation mechanism.A new criterion for the prediction of longitudinal crack and a discovering method for correlation between product quality and process parameters in the manufacturing industry have been provided.展开更多
The surface longitudinal cracking of peritectic steel Q345 D slab was studied by means of metallographic microscopy and scanning electron microscopy. The results show that the surface longitudinal cracking is caused b...The surface longitudinal cracking of peritectic steel Q345 D slab was studied by means of metallographic microscopy and scanning electron microscopy. The results show that the surface longitudinal cracking is caused by the shell repeatedly tearing and healing under the action of stress, which is due to disruption of the steel matrix continuity with inclusion aggregation on the shell surface. The relative precautions of reducing the cracking are raised according to the practical situation.展开更多
In order to solve the problem of the high surface longitudinal crack ratio of heavy peritectic steel slabs produced by the No. 3 continuous caster at Baosteel,the physical properties of the original mold flux and the ...In order to solve the problem of the high surface longitudinal crack ratio of heavy peritectic steel slabs produced by the No. 3 continuous caster at Baosteel,the physical properties of the original mold flux and the optimized mold flux were compared in a comprehensive way by using analytical measures, such as a slag film heat-flow simulator, a thermowire molten flux crystallization tester and an X-ray diffractometer in the laboratory. The results reveal that one of the major reasons for the cracks is the poor heat transfer ability of the original mold flux. However, the optimized mold flux with a high basicity features a high crystallizing rate,low crystallization temperature and low heat-flow density. Therefore, the optimized mold flux is more suitable for casting peritectic steel by the heavy slab continuous caster. The test results show that the slabs produced by using the optimized mold flux had no surface longitudinal crack in four test casts, while the surface longitudinal crack ratio of the slabs produced by using the original mold flux was 5%. The optimized mold flux can effectively prevent slab surface longitudinal cracks from occurring.展开更多
文摘The fact that the amount of the mold flux components differs at differentlocations on the cracking surface indicates that the longitudinal surface cracks are initiallyformed in the mold and are enlarged in the secondary cooling zone. Based on the hot ductilitymeasurement of two typical container used steels, it is known that the steels are in severeembrittlement state in the temperature range of 825-775 deg C. By means of increasing Cr/Ni platingthickness on the upper part of the mold, reducing mold heat flux, adopting new secondary coolingpattern, etc., the occurrence of the surface longitudinal cracks on the steel CC (continuouscasting) slabs has been significantly reduced.
基金the support from National Natural Science Foundation of China(52274318).
文摘The correlation between the longitudinal crack occurrence and integrated heat transfer of the mold with data mining methods was investigated.Firstly,three kinds of support vector machine models based on principal component analysis with different input features were established to explore the effect of integrated heat transfer on the accuracy of the prediction model for the longitudinal crack.The results show that the accuracy was improved while features including mean and standard deviation of integrated heat transfer were added.Then,the difference in integrated heat transfer between defect and normal samples under the same process parameters was quantitatively compared.Compared with normal samples,the temperature difference of cooling water for defect samples decreased by 0.65%,and the temperature difference fluctuation increased by 31.1%.Finally,the literature data were used to provide support for the quantitative correlation according to defect formation mechanism.A new criterion for the prediction of longitudinal crack and a discovering method for correlation between product quality and process parameters in the manufacturing industry have been provided.
文摘The surface longitudinal cracking of peritectic steel Q345 D slab was studied by means of metallographic microscopy and scanning electron microscopy. The results show that the surface longitudinal cracking is caused by the shell repeatedly tearing and healing under the action of stress, which is due to disruption of the steel matrix continuity with inclusion aggregation on the shell surface. The relative precautions of reducing the cracking are raised according to the practical situation.
文摘In order to solve the problem of the high surface longitudinal crack ratio of heavy peritectic steel slabs produced by the No. 3 continuous caster at Baosteel,the physical properties of the original mold flux and the optimized mold flux were compared in a comprehensive way by using analytical measures, such as a slag film heat-flow simulator, a thermowire molten flux crystallization tester and an X-ray diffractometer in the laboratory. The results reveal that one of the major reasons for the cracks is the poor heat transfer ability of the original mold flux. However, the optimized mold flux with a high basicity features a high crystallizing rate,low crystallization temperature and low heat-flow density. Therefore, the optimized mold flux is more suitable for casting peritectic steel by the heavy slab continuous caster. The test results show that the slabs produced by using the optimized mold flux had no surface longitudinal crack in four test casts, while the surface longitudinal crack ratio of the slabs produced by using the original mold flux was 5%. The optimized mold flux can effectively prevent slab surface longitudinal cracks from occurring.