The smelting-separation process for metallized pellets of vanadium-bearing titanomagnetite concentrates was studied.The influences of smelting temperature,smelting time,and the basicity of the metallized pellet on van...The smelting-separation process for metallized pellets of vanadium-bearing titanomagnetite concentrates was studied.The influences of smelting temperature,smelting time,and the basicity of the metallized pellet on vanadium and iron recovery were investigated.The characteristics of titanium slag were analyzed using X-ray diffraction,energy dispersive spectroscopy,and mineralographic microscopic analysis.The results demonstrate that appropriate increases in smelting temperature and smelting time can improve the vanadium and iron recovery from metallized pellets and are beneficial for the slag-iron separation.Although increasing the basicity of the metallized pellet can considerably improve the vanadium and iron recovery,the TiO;grade of titanium slag was decreased.Under the optimal conditions,90.17% of vanadium and 92.98% of iron in the metallized pellet were recovered,and the TiO;grade of titanium slag was 55.01%.It was found that anosovite,augite,spinel,glassiness,and metallic iron were the main mineral phases of the titanium slag.展开更多
The pre-reduced Bayan Obo ferroniobium（FeNb）ore concentrate block was taken as raw materials for studying the physical properties of niobium-enriched slag and changes in niobium recovery rate.In addition,the dephosp...The pre-reduced Bayan Obo ferroniobium（FeNb）ore concentrate block was taken as raw materials for studying the physical properties of niobium-enriched slag and changes in niobium recovery rate.In addition,the dephosphorization rate of the slag under different melting-separation conditions was investigated using the melting-separation test.The research results demonstrate that（i）the niobium recovery rate and dephosphorization rate of the slag decrease with the increase in melting-separation temperature;（ii）the niobium recovery rate of the slag initially increases and then decreases with increase in basicity and time;and（iii）the dephosphorization rate of the slag increases with the increase in basicity and time.When the test was performed under the conditions of basicity of 0.6-0.7,time of 7-10min,and temperature of 1400-1450°C,the niobium recovery rate and dephosphorization rate are over 96%and 95%,respectively.By scanning electron microscopy,it is observed that niobium mainly exists in the form of calcium and titanium silicate within the slag phase,with uneven distribution.展开更多
基金Item Sponsored by National Natural Science Foundation of China(51174122)
文摘The smelting-separation process for metallized pellets of vanadium-bearing titanomagnetite concentrates was studied.The influences of smelting temperature,smelting time,and the basicity of the metallized pellet on vanadium and iron recovery were investigated.The characteristics of titanium slag were analyzed using X-ray diffraction,energy dispersive spectroscopy,and mineralographic microscopic analysis.The results demonstrate that appropriate increases in smelting temperature and smelting time can improve the vanadium and iron recovery from metallized pellets and are beneficial for the slag-iron separation.Although increasing the basicity of the metallized pellet can considerably improve the vanadium and iron recovery,the TiO;grade of titanium slag was decreased.Under the optimal conditions,90.17% of vanadium and 92.98% of iron in the metallized pellet were recovered,and the TiO;grade of titanium slag was 55.01%.It was found that anosovite,augite,spinel,glassiness,and metallic iron were the main mineral phases of the titanium slag.
基金financially supported by the National Science and Technology Support Program (2008BAB32087)
文摘The pre-reduced Bayan Obo ferroniobium（FeNb）ore concentrate block was taken as raw materials for studying the physical properties of niobium-enriched slag and changes in niobium recovery rate.In addition,the dephosphorization rate of the slag under different melting-separation conditions was investigated using the melting-separation test.The research results demonstrate that（i）the niobium recovery rate and dephosphorization rate of the slag decrease with the increase in melting-separation temperature;（ii）the niobium recovery rate of the slag initially increases and then decreases with increase in basicity and time;and（iii）the dephosphorization rate of the slag increases with the increase in basicity and time.When the test was performed under the conditions of basicity of 0.6-0.7,time of 7-10min,and temperature of 1400-1450°C,the niobium recovery rate and dephosphorization rate are over 96%and 95%,respectively.By scanning electron microscopy,it is observed that niobium mainly exists in the form of calcium and titanium silicate within the slag phase,with uneven distribution.