Solubility of ion and trace metals from stabilized sewage sludge by fly ash and alkaline mine tailing

Stabilized sewage sludge （SS） by fly ash （FA） and alkaline mine tailing as artificial soil, to be applied on the ecological rehabilitation at mining junkyards, offers a potentially viable utilization of the industrial by-product, as well as solves the shortage of soil resource in the mine area. An incubation experiment with different ratios of SS and FA was conducted to evaluate the solubility of ions and trace elements from stabilized sewage sludge. Results showed that fly ash offset a decrease in pH value of sewage sludge. The pH of （C） treatment （FA：SS = 1：1） was stable and tended to neutrality. The SO4^2- and Cl^- concentrations of the solution in the mixture were significantly decreased in the stabilized sewage sludge by alkaline fly ash and mine tailing, compared to the single SS treatment. Stabilized sewage sludge by FA weakened the nitrification of total nitrogen from SS when the proportion of FA in the mixture was more than 50%. The Cr, Ni, and Cu concentrations in the solution were gradually decreased and achieved a stable level after 22 days, for all treatments over the duration of the incubation. Moreover stabilized sewage sludge by fly ash and/or mine tailing notably decreased the trace metal solubility. The final Cr, Cu, and Ni concentrations in the solution for all mixtures of treatments were lower than 2.5, 15, and 50 μg/L, respectively.

Treatment method of hazardous pickling sludge by reusing as glass–ceramics nucleation agent

Heavy metal containing pickling sludge（PS） is one of the by-products of the stainless-steel-making industry,which has been considered hazardous due to contained chromium and nickel.Traditional methods of PS disposing are landfill and cement solidification.This research is aimed at disposing PS by solidification/stabilization and reusing it as a nucleation agent of glass–ceramics.The crystallization behavior and the properties of a glass in the CaO–MgO–SiO2–Al2O3 system were studied by considering PS as the nucleation agent.Experimental results confirm that introducing 14 wt% PS as the nucleation agent of glass–ceramics can decrease crystallization temperature by 110.8 °C,refine the grain size by forming isometric crystals with size of 2 lm,enhance Vickers hardness by 2690 MPa and decrease water absorption from（1.21 ± 0.10） wt% to（0.04 ± 0.01） wt%.Therefore,it is reasonable to conclude that PS can be utilized as a nucleation agent to improve the crystallization and mechanical properties of the glass–ceramics.The testing results of US EPA toxicity characteristic leaching procedure（TCLP）confirm the safety of this reusing method.