The molten slag in smelting reduction with iron bath has peculiar behaviour for its high FeO concentration. Slag foaming is effected by the concentration and reduction rate of FeO, basicity of slag and temperature. Ad...The molten slag in smelting reduction with iron bath has peculiar behaviour for its high FeO concentration. Slag foaming is effected by the concentration and reduction rate of FeO, basicity of slag and temperature. Addition of granulated coke can greatly decrease slag foaming extent in the process of smelting reduction with iron bath. The anti-foaming capacity of granulated coke is the best when the ratio of coke used for coke layer to total coke used in smelting reduction is controlled at about 20%.展开更多
Effects of FeO content （0, 5%, 10%, and 15% in mass, respectively ） in lab-synthesized smelting redttc- tion slag with iron bath and test temperature （1 450, 1 500, 1550, anti 1 600 ℃ ） on corrosion am,amount and...Effects of FeO content （0, 5%, 10%, and 15% in mass, respectively ） in lab-synthesized smelting redttc- tion slag with iron bath and test temperature （1 450, 1 500, 1550, anti 1 600 ℃ ） on corrosion am,amount and microstructure of fused rebonded magnesia - chrome brick with 26.02 massqc of Cr2O3 were researched by rotary cylinder method. The results show that ： （ 1 ） the corro- sion amolult of magnesia -chrome brick by slag without FeO is higher than that by the slag with 5% FeO, and the vorrosion amount increases when FeO content increa- ses from 5% to 15% ; （2） the test temperature is one of the important factors affecting the slag corrosion resist- ance of magnesia - chrome brick, and the corrosion of smelting reduction slag to brick increases with the temperature rising.展开更多
Smelting reduction is a front iron making technology for the 21st century. It can produce liquid iron by direct using common coal but not charred coal. The process has many attractive advantages such as concise flow, ...Smelting reduction is a front iron making technology for the 21st century. It can produce liquid iron by direct using common coal but not charred coal. The process has many attractive advantages such as concise flow, low investment and production cost, low environmental pollution and high quality molten iron. Combined with a reciprocal chemical technology, energy efficiency can be further improved by transforming mass coal gas, by-produced in smelting reduction,into dimethyl ether, a clean fuel. Method and characteristics of the combined technology are discussed in this paper.展开更多
A simple model for estimating the rate constant between CO2-CO gas and molten slag containing iron oxides was developed using optical basicity only. In this model, the temperature dependence of the rate constant can b...A simple model for estimating the rate constant between CO2-CO gas and molten slag containing iron oxides was developed using optical basicity only. In this model, the temperature dependence of the rate constant can be described by the Arrhenius law, and the activation energy can be expressed with a linear function of the slag＇s optical basicity. The model was applied to some molten slag systems, such as FeO, FeO-CaO, FeO-SiO2, FeO-Na2O, FeO-CaO-SiO2, FeO-SiO2-P2O5, FeO-SiOE-Na2O, and FeO-CaO-SiOE-P2O5. A comparison between the predicted results and measured data showed that the model worked well.展开更多
Red mud, an insoluble residue produced during alkali leaching of bauxite, is considered as a low-grade iron ore containing 30% to 50% iron. The present paper deals with the use of thermal plasma technology for produci...Red mud, an insoluble residue produced during alkali leaching of bauxite, is considered as a low-grade iron ore containing 30% to 50% iron. The present paper deals with the use of thermal plasma technology for producing pig iron from red mud waste fines. The smelting reduction of red mud was carried out in a 35 kW DC extended arc thermal plasma reactor. Red mud was properly mixed with fluxes and graphite （fixed carbon, 99%） as a reductant as per stoichiometric requirement. The effect of various process parameters like a reductant, fluxes and smelting time on iron recovery was studied and optimized. An optimum condition for the maximum recovery of iron was obtained. A new thermal plasma process applicable to direct iron making from red mud waste fines that would achieve significant utilization of red mud was proposed.展开更多
The processes of fine iron ore reduced in fluidized bed have been reviewed in this paper,the superiorities and limitations of the processes of direct reduction,pre-reduction in fluidized bed have also been comprehensi...The processes of fine iron ore reduced in fluidized bed have been reviewed in this paper,the superiorities and limitations of the processes of direct reduction,pre-reduction in fluidized bed have also been comprehensively analysed,which matches with bath smelting furnace or coke bed type furnace.The analysis has also been made on several controversial topics,and the gas use ratio has been point out to be the key of the competition of the reduction process in fluidized bed.The suitability with final reduction furnace is also important to the energy saving in the whole smelting reduction process.展开更多
As a new type of ironmaking raw materials,carbon composite iron ore hot briquette(CCB) is the product of fine iron ore and fine coal by hot briquetting process.On basis of experimental research on the manufacturing an...As a new type of ironmaking raw materials,carbon composite iron ore hot briquette(CCB) is the product of fine iron ore and fine coal by hot briquetting process.On basis of experimental research on the manufacturing and metallurgical properties of CCB,this study focused on the application of CCB to blast furnace ironmaking and newly-developed shaft furnace smelting reduction processes.Firstly,the metallurgical properties of CCB are experimentally tested and compared with the common iron-bearing burdens.Then,the effects of charging CCB on blast furnace operation are numerically analyzed by means of multi-fluid blast furnace model,and the flowchart and pilot test of CCB-Shaft furnace smelting reduction process are briefly introduced.展开更多
文摘The molten slag in smelting reduction with iron bath has peculiar behaviour for its high FeO concentration. Slag foaming is effected by the concentration and reduction rate of FeO, basicity of slag and temperature. Addition of granulated coke can greatly decrease slag foaming extent in the process of smelting reduction with iron bath. The anti-foaming capacity of granulated coke is the best when the ratio of coke used for coke layer to total coke used in smelting reduction is controlled at about 20%.
文摘Effects of FeO content （0, 5%, 10%, and 15% in mass, respectively ） in lab-synthesized smelting redttc- tion slag with iron bath and test temperature （1 450, 1 500, 1550, anti 1 600 ℃ ） on corrosion am,amount and microstructure of fused rebonded magnesia - chrome brick with 26.02 massqc of Cr2O3 were researched by rotary cylinder method. The results show that ： （ 1 ） the corro- sion amolult of magnesia -chrome brick by slag without FeO is higher than that by the slag with 5% FeO, and the vorrosion amount increases when FeO content increa- ses from 5% to 15% ; （2） the test temperature is one of the important factors affecting the slag corrosion resist- ance of magnesia - chrome brick, and the corrosion of smelting reduction slag to brick increases with the temperature rising.
文摘Smelting reduction is a front iron making technology for the 21st century. It can produce liquid iron by direct using common coal but not charred coal. The process has many attractive advantages such as concise flow, low investment and production cost, low environmental pollution and high quality molten iron. Combined with a reciprocal chemical technology, energy efficiency can be further improved by transforming mass coal gas, by-produced in smelting reduction,into dimethyl ether, a clean fuel. Method and characteristics of the combined technology are discussed in this paper.
基金supported by the National Natural Science Foundation of China (Nos. 50834007, 50874128, and 50674012)
文摘A simple model for estimating the rate constant between CO2-CO gas and molten slag containing iron oxides was developed using optical basicity only. In this model, the temperature dependence of the rate constant can be described by the Arrhenius law, and the activation energy can be expressed with a linear function of the slag＇s optical basicity. The model was applied to some molten slag systems, such as FeO, FeO-CaO, FeO-SiO2, FeO-Na2O, FeO-CaO-SiO2, FeO-SiO2-P2O5, FeO-SiOE-Na2O, and FeO-CaO-SiOE-P2O5. A comparison between the predicted results and measured data showed that the model worked well.
文摘Red mud, an insoluble residue produced during alkali leaching of bauxite, is considered as a low-grade iron ore containing 30% to 50% iron. The present paper deals with the use of thermal plasma technology for producing pig iron from red mud waste fines. The smelting reduction of red mud was carried out in a 35 kW DC extended arc thermal plasma reactor. Red mud was properly mixed with fluxes and graphite （fixed carbon, 99%） as a reductant as per stoichiometric requirement. The effect of various process parameters like a reductant, fluxes and smelting time on iron recovery was studied and optimized. An optimum condition for the maximum recovery of iron was obtained. A new thermal plasma process applicable to direct iron making from red mud waste fines that would achieve significant utilization of red mud was proposed.
文摘The processes of fine iron ore reduced in fluidized bed have been reviewed in this paper,the superiorities and limitations of the processes of direct reduction,pre-reduction in fluidized bed have also been comprehensively analysed,which matches with bath smelting furnace or coke bed type furnace.The analysis has also been made on several controversial topics,and the gas use ratio has been point out to be the key of the competition of the reduction process in fluidized bed.The suitability with final reduction furnace is also important to the energy saving in the whole smelting reduction process.
文摘As a new type of ironmaking raw materials,carbon composite iron ore hot briquette(CCB) is the product of fine iron ore and fine coal by hot briquetting process.On basis of experimental research on the manufacturing and metallurgical properties of CCB,this study focused on the application of CCB to blast furnace ironmaking and newly-developed shaft furnace smelting reduction processes.Firstly,the metallurgical properties of CCB are experimentally tested and compared with the common iron-bearing burdens.Then,the effects of charging CCB on blast furnace operation are numerically analyzed by means of multi-fluid blast furnace model,and the flowchart and pilot test of CCB-Shaft furnace smelting reduction process are briefly introduced.