The effect of diboron trioxide(B_2O_3) on the crushing strength and smelting mechanism of high-chromium vanadium–titanium magnetite pellets was investigated in this work. The main characterization methods were X-ray ...The effect of diboron trioxide(B_2O_3) on the crushing strength and smelting mechanism of high-chromium vanadium–titanium magnetite pellets was investigated in this work. The main characterization methods were X-ray fluorescence, inductively coupled plasma–atomic emission spectroscopy, mercury injection porosimetry, X-ray diffraction, metallographic microscopy, and scanning electron microscopy–energy-dispersive X-ray spectroscopy. The results showed that the crushing strength increased greatly with increasing B_2O_3 content and that the increase in crushing strength was strongly correlated with a decrease in porosity, the formation of liquid phases, and the growth and recrystallization consolidation of hematite crystalline grains. The smelting properties were measured under simulated blast furnace conditions; the results showed that the smelting properties within a certain B_2O_3 content range were improved and optimized except in the softening stage. The valuable element B was easily transformed to the slag, and this phenomenon became increasingly evident with increasing B_2O_3 content. The formation of Ti(C,N) was mostly avoided, and the slag and melted iron were separated well during smelting with the addition of B_2O_3. The size increase of the melted iron was consistent with the gradual optimization of the dripping characteristics with increasing B_2O_3 content.展开更多
A comparative study was made of the reduction kinetics for high temperature smelting of vadium-titanium-containing magnetite,together with Hainan iron ore,using iron bath method.Three peaks were revealed on the reduct...A comparative study was made of the reduction kinetics for high temperature smelting of vadium-titanium-containing magnetite,together with Hainan iron ore,using iron bath method.Three peaks were revealed on the reduction rate curves for the magnetite,while one peak only for Hainan ore.Under the same conditions,the smelting reduction rate of the magnetite was found to be lower than that of Hainan ore.The rate increases evidently with the increase of the bath volume.The expressions of smelting reduction rate were suggested for the reduction with and without iron bath respectively.展开更多
基金financially supported by the National Key Technology Research and Development Program of the Ministry of Science and Technology of China (No. 2015BAB19B02)the National Program on Key Basic Research Project of China (No. 2013CB632603)
文摘The effect of diboron trioxide(B_2O_3) on the crushing strength and smelting mechanism of high-chromium vanadium–titanium magnetite pellets was investigated in this work. The main characterization methods were X-ray fluorescence, inductively coupled plasma–atomic emission spectroscopy, mercury injection porosimetry, X-ray diffraction, metallographic microscopy, and scanning electron microscopy–energy-dispersive X-ray spectroscopy. The results showed that the crushing strength increased greatly with increasing B_2O_3 content and that the increase in crushing strength was strongly correlated with a decrease in porosity, the formation of liquid phases, and the growth and recrystallization consolidation of hematite crystalline grains. The smelting properties were measured under simulated blast furnace conditions; the results showed that the smelting properties within a certain B_2O_3 content range were improved and optimized except in the softening stage. The valuable element B was easily transformed to the slag, and this phenomenon became increasingly evident with increasing B_2O_3 content. The formation of Ti(C,N) was mostly avoided, and the slag and melted iron were separated well during smelting with the addition of B_2O_3. The size increase of the melted iron was consistent with the gradual optimization of the dripping characteristics with increasing B_2O_3 content.
文摘A comparative study was made of the reduction kinetics for high temperature smelting of vadium-titanium-containing magnetite,together with Hainan iron ore,using iron bath method.Three peaks were revealed on the reduction rate curves for the magnetite,while one peak only for Hainan ore.Under the same conditions,the smelting reduction rate of the magnetite was found to be lower than that of Hainan ore.The rate increases evidently with the increase of the bath volume.The expressions of smelting reduction rate were suggested for the reduction with and without iron bath respectively.