利用光学显微镜、X射线衍射仪、扫描电镜、电子背散射衍射、透射电镜、硬度以及力学性能测试等对挤压态和T5处理态的Mg-6Zn-1Mn-4Sn-1.5Nd镁合金的显微组织和力学性能进行研究。研究结果表明:合金铸态的相组成为α(Mg)、Mn、Mg7Zn3、Mg...利用光学显微镜、X射线衍射仪、扫描电镜、电子背散射衍射、透射电镜、硬度以及力学性能测试等对挤压态和T5处理态的Mg-6Zn-1Mn-4Sn-1.5Nd镁合金的显微组织和力学性能进行研究。研究结果表明:合金铸态的相组成为α(Mg)、Mn、Mg7Zn3、Mg2Sn和MgS nN d相。挤压过程中完成动态再结晶,再结晶晶粒的平均尺寸为7.2μm。T5热处理显著提高挤压态合金的强度。合金的屈服强度和抗拉强度分别增加94 MPa和34 MPa。显微组织分析表明,合金强度的提高主要是由于时效过程中析出高密度的β′1杆状相。展开更多
Texture evolution of an extruded dilute Mg-1Sn-1Zn-1Al alloy was thoroughly investigated based on the twinning and dynamic recrystallization(DRX)behavior via hot compression at a strain rate of 10 s^(-1)and temperatur...Texture evolution of an extruded dilute Mg-1Sn-1Zn-1Al alloy was thoroughly investigated based on the twinning and dynamic recrystallization(DRX)behavior via hot compression at a strain rate of 10 s^(-1)and temperature of 225℃.It was found that the types and intensities of the texture are strongly dependent on the fraction of twins and DRX modes as well as regions where sub-grain boundaries(sub-GBs)are intensively accumulated.At the initial stage of deformation,the formation of compression direction(CD)-tilted basal texture was mainly determined by the occurrence of{101^(-)2}extension twins.As the strain increases,the variation in the texture intensity was greatly dominated by the DRX modes but the type of main texture remained unchanged.These findings are of great importance for texture modification of wrought Mg-Sn-based alloys during post-deformation.展开更多
The microstructures and mechanical properties of as-cast Mg-5 Sn-1 Si magnesium alloy modified with trace elements Y,Bi,Sb and Sr were investigated and compared.Results show that the microstructure of the as-cast Mg-5...The microstructures and mechanical properties of as-cast Mg-5 Sn-1 Si magnesium alloy modified with trace elements Y,Bi,Sb and Sr were investigated and compared.Results show that the microstructure of the as-cast Mg-5 Sn-1 Si alloy consists ofα-Mg,Mg_(2) Si,Mg_(2) Sn and Mg_(2)(Si_xSn_(1-x))phases.After adding 0.8 wt.%Y,0.3 wt.%Bi,0.9 wt.%Sb and 0.9 wt.%Sr,respectively into the Mg-5 Sn-1 Si magnesium alloy,Mg_(24)Y_(5),Mg_(3) Bi_(2),Mg_(3) Sb_(2) and Mg_(2) Sr phases are precipitated accordingly.Trace elements can refineα-Mg grain and Chinese scriptshaped Mg_(2) Si phase.Refinement efficiency of different trace elements onα-Mg grain and Mg_(2) Si phase is varied.Sr element has the best refinement effect,followed by Sb and Bi,while Y has the least refinement effect.Mg-5 Sn-1 Si-0.9 Sr alloy has higher tensile properties than the other three modified alloys.The refinement mechanism of Y,Bi and Sr elements on Mg-5 Sn-1 Si magnesium alloy can be explained by the growth restriction factors and the solute undercooling.For Mg-5 Sn-1 Si-0.9 Sb alloy,the heterogeneous nuclei of Mg_(3) Sb_(2) phase is the main reason for the refinement of grains and second phases.展开更多
The effect of the quenching rate after solution treatment on the residual stress and precipitation behavior of a high strength Mg-5 Zn-3.5 Sn-1 Mn-0.5 Ca-0.5 Cu plate is studied.The simulation results show decreasing ...The effect of the quenching rate after solution treatment on the residual stress and precipitation behavior of a high strength Mg-5 Zn-3.5 Sn-1 Mn-0.5 Ca-0.5 Cu plate is studied.The simulation results show decreasing temperature gradient in the plate with decreasing quenching rate,which leads to weakened inhomogeneous plastic deformation and decreased residual stress.No dynamic precipitation on the grain boundary happens after either cold water cooling or air cooling,however,air cooling leads to dynamic precipitation of Mg-Zn phase on Mn particles around which a low-density precipitate zone develops after aging treatment.Moreover,the fine and densely distributed Mg-Zn precipitates observed after aging treatment of the cold water cooled alloy are replaced by coarse precipitates with low density for the air cooled alloy.Both the low-density precipitate zone near Mn particles and the coarsening of precipitates are the source of the decrease in hardness and tensile properties of the air cooled alloy.The residual stress drops faster than the hardness with decreasing quenching rate,which makes it possible to lower the residual stress without sacrificing too much age-hardening ability of the alloy.展开更多
In this study, the influence of minor titanium(Ti) addition on the microstructure and tensile properties of Mg-8Sn-1Zn based alloys were investigated by means of optical microscopy, X-ray diffraction, scanning electro...In this study, the influence of minor titanium(Ti) addition on the microstructure and tensile properties of Mg-8Sn-1Zn based alloys were investigated by means of optical microscopy, X-ray diffraction, scanning electron microscopy, energy dispersive spectrometry, and tensile tests. The results showed that Ti can decrease the secondary dendrite arm spacing(SDAS). The tensile strength of the Mg-8Sn-1Zn-Ti alloys is initially increased by increasing the Ti content up to 0.09 wt.%, but subsequently decreased for further increase of Ti content. The improved tensile properties are attributed to the decreased SDAS and refi ned Mg_2Sn phases, as well as the increased fraction of tin(Sn) segregated regions. The tensile fracture surface of the studied alloys shows mixed characteristics of cleavage and quasi-cleavage fracture. Adding Ti does not significantly change the fracture mode of the studied alloys.展开更多
基金Project(51222405) supported by the National Science Foundation of Outstanding Young Scholars of ChinaProject(51034002) supported by the National Natural Science Foundation of China+1 种基金Project(132002) supported by the Fok Ying Tong Education FoundationProject (2011CB610405) supported by the National Basic Research Program of China
基金Project(2013CB632200)supported by the National Great Theoretic Research,ChinaProject(2011BAE22B01-3)supported by the National Sci&Tech Support Program,ChinaProject(2010DFR50010)supported by the International Cooperation,Sharing Fund of Chongqing University’s Large-scale Equipment,China
文摘利用光学显微镜、X射线衍射仪、扫描电镜、电子背散射衍射、透射电镜、硬度以及力学性能测试等对挤压态和T5处理态的Mg-6Zn-1Mn-4Sn-1.5Nd镁合金的显微组织和力学性能进行研究。研究结果表明:合金铸态的相组成为α(Mg)、Mn、Mg7Zn3、Mg2Sn和MgS nN d相。挤压过程中完成动态再结晶,再结晶晶粒的平均尺寸为7.2μm。T5热处理显著提高挤压态合金的强度。合金的屈服强度和抗拉强度分别增加94 MPa和34 MPa。显微组织分析表明,合金强度的提高主要是由于时效过程中析出高密度的β′1杆状相。
基金the Natural Science Foundation of China(51404166 and 51704209)Natural Science Foundation of Shanxi(201801D121088)the Scientific and Technological Innovation Programs of Higher Education Institutions in Shanxi(2014017 and 201802034).
文摘Texture evolution of an extruded dilute Mg-1Sn-1Zn-1Al alloy was thoroughly investigated based on the twinning and dynamic recrystallization(DRX)behavior via hot compression at a strain rate of 10 s^(-1)and temperature of 225℃.It was found that the types and intensities of the texture are strongly dependent on the fraction of twins and DRX modes as well as regions where sub-grain boundaries(sub-GBs)are intensively accumulated.At the initial stage of deformation,the formation of compression direction(CD)-tilted basal texture was mainly determined by the occurrence of{101^(-)2}extension twins.As the strain increases,the variation in the texture intensity was greatly dominated by the DRX modes but the type of main texture remained unchanged.These findings are of great importance for texture modification of wrought Mg-Sn-based alloys during post-deformation.
基金the financial support by the Natioal Natural Science Foundation of China(Nos.:51571086 and 51271073)the financial support from the Natural Science Foundation of Henan Polytechnic University(No.:B2010-20)。
文摘The microstructures and mechanical properties of as-cast Mg-5 Sn-1 Si magnesium alloy modified with trace elements Y,Bi,Sb and Sr were investigated and compared.Results show that the microstructure of the as-cast Mg-5 Sn-1 Si alloy consists ofα-Mg,Mg_(2) Si,Mg_(2) Sn and Mg_(2)(Si_xSn_(1-x))phases.After adding 0.8 wt.%Y,0.3 wt.%Bi,0.9 wt.%Sb and 0.9 wt.%Sr,respectively into the Mg-5 Sn-1 Si magnesium alloy,Mg_(24)Y_(5),Mg_(3) Bi_(2),Mg_(3) Sb_(2) and Mg_(2) Sr phases are precipitated accordingly.Trace elements can refineα-Mg grain and Chinese scriptshaped Mg_(2) Si phase.Refinement efficiency of different trace elements onα-Mg grain and Mg_(2) Si phase is varied.Sr element has the best refinement effect,followed by Sb and Bi,while Y has the least refinement effect.Mg-5 Sn-1 Si-0.9 Sr alloy has higher tensile properties than the other three modified alloys.The refinement mechanism of Y,Bi and Sr elements on Mg-5 Sn-1 Si magnesium alloy can be explained by the growth restriction factors and the solute undercooling.For Mg-5 Sn-1 Si-0.9 Sb alloy,the heterogeneous nuclei of Mg_(3) Sb_(2) phase is the main reason for the refinement of grains and second phases.
基金supported by the National Key Research and Development Program of China[2016YFB0301105]the National Key Research and Development Plan[2017YFB0103904]
文摘The effect of the quenching rate after solution treatment on the residual stress and precipitation behavior of a high strength Mg-5 Zn-3.5 Sn-1 Mn-0.5 Ca-0.5 Cu plate is studied.The simulation results show decreasing temperature gradient in the plate with decreasing quenching rate,which leads to weakened inhomogeneous plastic deformation and decreased residual stress.No dynamic precipitation on the grain boundary happens after either cold water cooling or air cooling,however,air cooling leads to dynamic precipitation of Mg-Zn phase on Mn particles around which a low-density precipitate zone develops after aging treatment.Moreover,the fine and densely distributed Mg-Zn precipitates observed after aging treatment of the cold water cooled alloy are replaced by coarse precipitates with low density for the air cooled alloy.Both the low-density precipitate zone near Mn particles and the coarsening of precipitates are the source of the decrease in hardness and tensile properties of the air cooled alloy.The residual stress drops faster than the hardness with decreasing quenching rate,which makes it possible to lower the residual stress without sacrificing too much age-hardening ability of the alloy.
基金supported by the National Natural Science Foundation of China(Grant no.51404166)Shanxi Province Science Foundation for Youths(2013021013-4)+2 种基金Research Project Supported by Shanxi Scholarship Council of China(2014-023)Technological Innovation Programs of Higher Education Institutions Shanxi(Grant no.2014120)the Advanced Programs of Department of Human Resources and Social Security of Shanxi Province for Returned Scholars(2013101)
文摘In this study, the influence of minor titanium(Ti) addition on the microstructure and tensile properties of Mg-8Sn-1Zn based alloys were investigated by means of optical microscopy, X-ray diffraction, scanning electron microscopy, energy dispersive spectrometry, and tensile tests. The results showed that Ti can decrease the secondary dendrite arm spacing(SDAS). The tensile strength of the Mg-8Sn-1Zn-Ti alloys is initially increased by increasing the Ti content up to 0.09 wt.%, but subsequently decreased for further increase of Ti content. The improved tensile properties are attributed to the decreased SDAS and refi ned Mg_2Sn phases, as well as the increased fraction of tin(Sn) segregated regions. The tensile fracture surface of the studied alloys shows mixed characteristics of cleavage and quasi-cleavage fracture. Adding Ti does not significantly change the fracture mode of the studied alloys.