Poly(methyl methacrylate/ethyl acrylate/acrylic acid) hydrosols were prepared by employing soap-free polymerization, and (acrylic acid/butyl acrylate) oligomer was used as the polymeric surfactant. The effect of react...Poly(methyl methacrylate/ethyl acrylate/acrylic acid) hydrosols were prepared by employing soap-free polymerization, and (acrylic acid/butyl acrylate) oligomer was used as the polymeric surfactant. The effect of reaction condition on the morphology and particle size of the hydrosols was investigated. The minimum amount of acrylic acid in the hydrosols is 2%. The maximum weight average molecular weight (M-w) of polymer that assures soap-free emulsion conversion into hydrosol is about 1.2 x 10(5)-1.3 x 10(5). The particle transforming process was investigated, and an obvious change of particle diameter and morphology was observed.展开更多
Poly(styrene-co-glycidyl methacrylate) latex microspheres with uniform size and high-density epoxy groups on the surface were prepared by soap-free emulsion polymerization with batch wise operation mode in the presenc...Poly(styrene-co-glycidyl methacrylate) latex microspheres with uniform size and high-density epoxy groups on the surface were prepared by soap-free emulsion polymerization with batch wise operation mode in the presence of 2.2′- azobis(2-methylpropionamidine) dihydrochloride as an initiator.The kinetics of soap-free emulsion polymerization and the effects of polymerization factors were examined.In addition,the optimum polymerization conditions of poly(styrene-co- glycidyl methacrylate) latex microspheres for...展开更多
Monodisperse functional polymer microspheres with different particle size and with clean surface were prepared by batch soap-free emulsion polymerization of styrene, methyl methacrylate and acrylic acid in the presenc...Monodisperse functional polymer microspheres with different particle size and with clean surface were prepared by batch soap-free emulsion polymerization of styrene, methyl methacrylate and acrylic acid in the presence of salts, and the influences of type and amount of electrolytes on polymerization process and particle morphology were investigated. Results showed that there was a critical concentration for different electrolyte to make polymerization process and the resultant emulsion stable, and the particle size increased with the increase of electrolyte concentration. The effect of metal ions was Ca^2＋〉〉K^＋〉Na^＋〉Li^＋, and the effect of haloids was Br〉Cl〉F. Keywords： Electrolyte, soap-free emulsion polymerization, polystyrene, latex particle morphology.展开更多
Using methyl methacrylate （MMA）, butyl acrylate（BA） and hexafluorobutyl acrylate（HFBA） as main raw materials, we prepared self-crosslinked fluorocarbon polymer emulsion with core-shell structure via soap-free em...Using methyl methacrylate （MMA）, butyl acrylate（BA） and hexafluorobutyl acrylate（HFBA） as main raw materials, we prepared self-crosslinked fluorocarbon polymer emulsion with core-shell structure via soap-free emulsion polymerization when the conception of particle design and polymer morphology was adopted. Moreover, the influence of mole ratio of BA to MAA, pH value on the oligomer was studied. And the effects of the added amount of oligomer, self-crosslinked monomer and HFBA, mass ratio of BA to MMA, reaction temperature and the initiator on the polymerization technology and the performance of the product, were investigated and optimized. The structure and performance of the fluorocarbon polymer emulsion were characterized and tested with FTIR, TEM, MFT and contact angle and water absorption of the latex film. The experimental results show that the optimal conditions for preparing fluorocarbon polymer emulsion are as follows： for preparing the oligomer, tool ratio of BA to MAA is equal to 1.0 ： 1.60, and pH value is controlled within the range of 8.0 and 9.0; for preparing fluorocarbon polymer emulsion, the added amount of oligmer[P（BA/MANa）] is 6%; mass ratio of BA to MMA is 40 ＂ 60; the added amount of self-crosslinked monomer is 2%, the added amount of HFBA is 15 %; reaction temperature is 80 ℃; the mixture of potassium persulfate and sodium bisulfite is used as the initiator. The film-forming stability of the fluorocarbon polymer emul- sion and the performance of the latex film, which is prepared with the soap-free emulsion polymerization, are better than that prepared with the conventional emulsion polymerization.展开更多
Soap-free P(MMA-EA-MAA) particles with narrow size distribution were synthesized by seeded emulsion polymerization of methyl methacrylate (MMA), ethyl acrylate (EA) and methacrylic acid (MAA), and large voids inside t...Soap-free P(MMA-EA-MAA) particles with narrow size distribution were synthesized by seeded emulsion polymerization of methyl methacrylate (MMA), ethyl acrylate (EA) and methacrylic acid (MAA), and large voids inside the particles were generated by alkali posttreatment in the presence of 2-butanone. Results indicated that the size of void and the particle volume were related with the amount of 2-butanone. The generation mechanism of voids was proposed.展开更多
Unlike previous emulsion polymerization, we used grafting reactions in soap-free emulsion systems. In this study, we synthesized grafted PMMA/PEI core-shell nanoparticles by varying the MMA/PEI content and molecular w...Unlike previous emulsion polymerization, we used grafting reactions in soap-free emulsion systems. In this study, we synthesized grafted PMMA/PEI core-shell nanoparticles by varying the MMA/PEI content and molecular weight of PEI (M<sub>n</sub> = 600, 8000, and 10,000). The size and morphology of the core-shell nanoparticles were characterized by a particle size analyzer and scanning electron microscopy. The nanoparticles were 178 - 408 nm in diameter and swelled in water or methanol by 30 - 75 nm. The size of the nanoparticles increased with MMA contents, whereas the size distribution progressively became homogeneous with increasing molecular weight of PEI. Lastly, we measured CO<sub>2</sub> adsorption capacity of the grafted PMMA/PEI core-shell nanoparticles, and we found the capacity to be limited at a level of 0.69 mg, which occurred for nanoparticles prepared from emulsions at a pH value of 11.展开更多
Soap-free poly（methyl methacrylate-ethyl acrylate-methacrylic acid） latex particles with narrow size distribution were synthesized by seeded emulsion polymerization, and the porous particles were created by a stepwi...Soap-free poly（methyl methacrylate-ethyl acrylate-methacrylic acid） latex particles with narrow size distribution were synthesized by seeded emulsion polymerization, and the porous particles were created by a stepwise alkali/acid treatment method. Effects of acid treatment conditions on the particle morphology were investigated. Results show that one to three pores were formed inside most of particles after post-treatment. At pH 7.0, when the treatment temperature was lower than 70℃, the size of particles and the volume of pores remained almost unchanged, and these two values increased significantly when the temperature was higher than 70℃. Both the particle size and the pore volume decreased with the increase of initial pH value and treatment time in the acid treatment. As the pH was below 4.0 and the treatment time was longer than 180 min, the particles shrunk in size.展开更多
文摘Poly(methyl methacrylate/ethyl acrylate/acrylic acid) hydrosols were prepared by employing soap-free polymerization, and (acrylic acid/butyl acrylate) oligomer was used as the polymeric surfactant. The effect of reaction condition on the morphology and particle size of the hydrosols was investigated. The minimum amount of acrylic acid in the hydrosols is 2%. The maximum weight average molecular weight (M-w) of polymer that assures soap-free emulsion conversion into hydrosol is about 1.2 x 10(5)-1.3 x 10(5). The particle transforming process was investigated, and an obvious change of particle diameter and morphology was observed.
基金supported by the State Key Laboratory of Chemical Engineering of Zhejiang Universitythe financial support from the National Natural Science Foundation of China (No.20676113).
文摘Poly(styrene-co-glycidyl methacrylate) latex microspheres with uniform size and high-density epoxy groups on the surface were prepared by soap-free emulsion polymerization with batch wise operation mode in the presence of 2.2′- azobis(2-methylpropionamidine) dihydrochloride as an initiator.The kinetics of soap-free emulsion polymerization and the effects of polymerization factors were examined.In addition,the optimum polymerization conditions of poly(styrene-co- glycidyl methacrylate) latex microspheres for...
文摘Monodisperse functional polymer microspheres with different particle size and with clean surface were prepared by batch soap-free emulsion polymerization of styrene, methyl methacrylate and acrylic acid in the presence of salts, and the influences of type and amount of electrolytes on polymerization process and particle morphology were investigated. Results showed that there was a critical concentration for different electrolyte to make polymerization process and the resultant emulsion stable, and the particle size increased with the increase of electrolyte concentration. The effect of metal ions was Ca^2＋〉〉K^＋〉Na^＋〉Li^＋, and the effect of haloids was Br〉Cl〉F. Keywords： Electrolyte, soap-free emulsion polymerization, polystyrene, latex particle morphology.
基金Funded by the Jiangsu Provincial Creative Fund for Scientific and Tech-nical Small and Medium-size Enterprise
文摘Using methyl methacrylate （MMA）, butyl acrylate（BA） and hexafluorobutyl acrylate（HFBA） as main raw materials, we prepared self-crosslinked fluorocarbon polymer emulsion with core-shell structure via soap-free emulsion polymerization when the conception of particle design and polymer morphology was adopted. Moreover, the influence of mole ratio of BA to MAA, pH value on the oligomer was studied. And the effects of the added amount of oligomer, self-crosslinked monomer and HFBA, mass ratio of BA to MMA, reaction temperature and the initiator on the polymerization technology and the performance of the product, were investigated and optimized. The structure and performance of the fluorocarbon polymer emulsion were characterized and tested with FTIR, TEM, MFT and contact angle and water absorption of the latex film. The experimental results show that the optimal conditions for preparing fluorocarbon polymer emulsion are as follows： for preparing the oligomer, tool ratio of BA to MAA is equal to 1.0 ： 1.60, and pH value is controlled within the range of 8.0 and 9.0; for preparing fluorocarbon polymer emulsion, the added amount of oligmer[P（BA/MANa）] is 6%; mass ratio of BA to MMA is 40 ＂ 60; the added amount of self-crosslinked monomer is 2%, the added amount of HFBA is 15 %; reaction temperature is 80 ℃; the mixture of potassium persulfate and sodium bisulfite is used as the initiator. The film-forming stability of the fluorocarbon polymer emul- sion and the performance of the latex film, which is prepared with the soap-free emulsion polymerization, are better than that prepared with the conventional emulsion polymerization.
基金the National 863 Project of China(grant No.2001AA242041)for financial support
文摘Soap-free P(MMA-EA-MAA) particles with narrow size distribution were synthesized by seeded emulsion polymerization of methyl methacrylate (MMA), ethyl acrylate (EA) and methacrylic acid (MAA), and large voids inside the particles were generated by alkali posttreatment in the presence of 2-butanone. Results indicated that the size of void and the particle volume were related with the amount of 2-butanone. The generation mechanism of voids was proposed.
文摘Unlike previous emulsion polymerization, we used grafting reactions in soap-free emulsion systems. In this study, we synthesized grafted PMMA/PEI core-shell nanoparticles by varying the MMA/PEI content and molecular weight of PEI (M<sub>n</sub> = 600, 8000, and 10,000). The size and morphology of the core-shell nanoparticles were characterized by a particle size analyzer and scanning electron microscopy. The nanoparticles were 178 - 408 nm in diameter and swelled in water or methanol by 30 - 75 nm. The size of the nanoparticles increased with MMA contents, whereas the size distribution progressively became homogeneous with increasing molecular weight of PEI. Lastly, we measured CO<sub>2</sub> adsorption capacity of the grafted PMMA/PEI core-shell nanoparticles, and we found the capacity to be limited at a level of 0.69 mg, which occurred for nanoparticles prepared from emulsions at a pH value of 11.
基金The research was supported by the National 863 Project of China(No.2001AA242041).
文摘Soap-free poly（methyl methacrylate-ethyl acrylate-methacrylic acid） latex particles with narrow size distribution were synthesized by seeded emulsion polymerization, and the porous particles were created by a stepwise alkali/acid treatment method. Effects of acid treatment conditions on the particle morphology were investigated. Results show that one to three pores were formed inside most of particles after post-treatment. At pH 7.0, when the treatment temperature was lower than 70℃, the size of particles and the volume of pores remained almost unchanged, and these two values increased significantly when the temperature was higher than 70℃. Both the particle size and the pore volume decreased with the increase of initial pH value and treatment time in the acid treatment. As the pH was below 4.0 and the treatment time was longer than 180 min, the particles shrunk in size.