To realize the comprehensive utilization of ludwigite ore,an integrated and efficient route for the boron and iron separation was proposed in this work,which via soda-ash roasting under CO–CO_(2)–N_(2) atmosphere fo...To realize the comprehensive utilization of ludwigite ore,an integrated and efficient route for the boron and iron separation was proposed in this work,which via soda-ash roasting under CO–CO_(2)–N_(2) atmosphere followed by grind-leaching,magnetic separation,and CO_(2) carbonation.The effects of roasting temperature,roasting time,CO/(CO+CO_(2))composition,and Na_(2)CO_(3) dosage on the boron and iron separation indices were primarily investigated.Under the optimized conditions of the roasting temperature of 850℃,roasting time of 60 min,soda ash dosage of 20 wt%,and CO/(CO+CO_(2)) of 10 vol%,92%of boron was leached during wet grinding,and 88.6%of iron was recovered during the magnetic separation and magnetic concentrate with a total iron content of 61.51 wt%.Raman spectra and^(11)B NMR results indicated that boron exists asB(OH)_(4)^(-) in the leachate,from which high-purity borax pentahydrate could be prepared by CO_(2) carbonation.展开更多
Low-cost thermal insulation porous ceramics with uniform pore diameter and low bulk density were prepared with soda-ash dregs and felsic tailings.We investigated the effect of temperature,foaming agent,fluxing agent,A...Low-cost thermal insulation porous ceramics with uniform pore diameter and low bulk density were prepared with soda-ash dregs and felsic tailings.We investigated the effect of temperature,foaming agent,fluxing agent,Al_(2)O_(3)and CaO content on the pore structure and crystal phase of porous ceramics.The effect of Ca^(2+)in soda-ash dregs on the preparation of quartz-feldspar based porous ceramics was studied.The results showed that the contribution of Ca^(2+)to the preparation of porous ceramics in this system was mainly to accelerate the Si-O bond fracture and reduce the sintering temperature at the initial stage of sintering,which destroyed the needle-like feldspar in the high temperature melt and reduced the melt viscosity,thus reduced the foaming resistance and promoted the porous products with uniform pore size distribution.The Ca^(2+)content on the high side can participate in the formation of crystals in sintering.The generated needle-like diopside and augite,which have small length-diameter ratio,will negligibly change in the viscosity of melt at high temperatures,and their inhibition effect on pores is not as good as that of feldspar with large length-diameter ratio,resulting in the merger and collapse of pores.But the increase of diopside and augite can improve the compressive strength of porous products to some extent.Porous ceramic products containing needle-like feldspar phase can be prepared by using two kinds of solid waste,which can improve the compressive strength of the products and reduce the raw material cost and energy consumption while comprehensively utilizing the double solid waste.The optimal product has a bulk density of 0.45 g/cm^(3),a compressive strength of 3.17 MPa,and a thermal conductivity of 0.11 W/(m·K).展开更多
基金financially supported by the National Key Research and Development Program of China(No.2020YFC1909803)the Basic Science Center Project for the National Natural Science Foundation of China(No.72088101)the Graduate Research and Innovative Project of Central South University(No.506021739)。
文摘To realize the comprehensive utilization of ludwigite ore,an integrated and efficient route for the boron and iron separation was proposed in this work,which via soda-ash roasting under CO–CO_(2)–N_(2) atmosphere followed by grind-leaching,magnetic separation,and CO_(2) carbonation.The effects of roasting temperature,roasting time,CO/(CO+CO_(2))composition,and Na_(2)CO_(3) dosage on the boron and iron separation indices were primarily investigated.Under the optimized conditions of the roasting temperature of 850℃,roasting time of 60 min,soda ash dosage of 20 wt%,and CO/(CO+CO_(2)) of 10 vol%,92%of boron was leached during wet grinding,and 88.6%of iron was recovered during the magnetic separation and magnetic concentrate with a total iron content of 61.51 wt%.Raman spectra and^(11)B NMR results indicated that boron exists asB(OH)_(4)^(-) in the leachate,from which high-purity borax pentahydrate could be prepared by CO_(2) carbonation.
基金Supported by the National Natural Science Foundation of China(No.51674161)Major Basic Research Projects of Shandong Province Natural Science Foundation(No.ZR2017ZC0735)+1 种基金Open Topic of Key Laboratory of Gold Mineralization Processes and Resource Utilization Subordinated to the Ministry of Land and Resources and Key Laboratory of Metallogenic Geological Process and Resources Utilization in Shandong Province(No.Kfkt201812)Research on Precious Metal Mineral Achievement Integration and Tailings Comprehensive Utilization in Shandong Province(Shandong Geological Exploration Document:[2018]No.10)。
文摘Low-cost thermal insulation porous ceramics with uniform pore diameter and low bulk density were prepared with soda-ash dregs and felsic tailings.We investigated the effect of temperature,foaming agent,fluxing agent,Al_(2)O_(3)and CaO content on the pore structure and crystal phase of porous ceramics.The effect of Ca^(2+)in soda-ash dregs on the preparation of quartz-feldspar based porous ceramics was studied.The results showed that the contribution of Ca^(2+)to the preparation of porous ceramics in this system was mainly to accelerate the Si-O bond fracture and reduce the sintering temperature at the initial stage of sintering,which destroyed the needle-like feldspar in the high temperature melt and reduced the melt viscosity,thus reduced the foaming resistance and promoted the porous products with uniform pore size distribution.The Ca^(2+)content on the high side can participate in the formation of crystals in sintering.The generated needle-like diopside and augite,which have small length-diameter ratio,will negligibly change in the viscosity of melt at high temperatures,and their inhibition effect on pores is not as good as that of feldspar with large length-diameter ratio,resulting in the merger and collapse of pores.But the increase of diopside and augite can improve the compressive strength of porous products to some extent.Porous ceramic products containing needle-like feldspar phase can be prepared by using two kinds of solid waste,which can improve the compressive strength of the products and reduce the raw material cost and energy consumption while comprehensively utilizing the double solid waste.The optimal product has a bulk density of 0.45 g/cm^(3),a compressive strength of 3.17 MPa,and a thermal conductivity of 0.11 W/(m·K).