Hydroxyapatite/alumina nanocrystalline composite powders needed for various biomedical applications were successfully synthe- sized by sol-gel process. Structural and morphological investigations of the prepared compo...Hydroxyapatite/alumina nanocrystalline composite powders needed for various biomedical applications were successfully synthe- sized by sol-gel process. Structural and morphological investigations of the prepared composite powders were performed using X-ray dif- fractometer （XRD）, scanning electron microscopy （SEM）, X＇Pert HighScore software, and Clemex Vision image analysis software. The re- suits show that the crystallite size of the obtained composite powders is in the range of 25 to 90 nm. SEM evaluation shows that the obtained composite powders have a porous structure, which is very useful for biomedical applications. The spherical nanoparticles in the range of 60 to 800 nm are embedded in the agglomerated clusters of the prepared composite powders.展开更多
Nanocrystalline rare earth mixed oxides DyFe x Co 1- x O 3- δ were prepared by sol gel method and characterized by X ray diffraction (XRD), thermogravimetric analysis (TG DTA) and scanning elec...Nanocrystalline rare earth mixed oxides DyFe x Co 1- x O 3- δ were prepared by sol gel method and characterized by X ray diffraction (XRD), thermogravimetric analysis (TG DTA) and scanning electron microscope (SEM). The results show that DyFe x Co 1- x O 3- δ has the structure of perovskite type at 800 ℃ for 2 h calcination. The conductivity of the materials at different temperature was measured by four probe instrumentation and two pole method. The results show that the conductivity of mixed oxides DyFe x Co 1- x O 3- δ is higher than those of un mixed oxides DyFeO 3 and DyCoO 3 and the conductivity is the best at x =0.8 in the matter of DyFe x Co 1- x O 3- δ . The conductivity of these materials always increases with the temperature rising and there is an apparent change between 600 and 800 ℃. However, the spinodals are different with different ration of Fe 3+ and Co 3+ . This kind of oxide is a conductive pottery material.展开更多
The nanocrystalline TiO_2 powder were prepared by improved sol-gel method at low temperature under ambient pressure. The prepared TiO_2 powder was characterized by X-ray diffraction (XRD), transmission electron micros...The nanocrystalline TiO_2 powder were prepared by improved sol-gel method at low temperature under ambient pressure. The prepared TiO_2 powder was characterized by X-ray diffraction (XRD), transmission electron microscopy (TEM). It is found that the yield of anatase TiO_2 significantly increases with the reduction of pH by increasing the nucleation rate of anatase. There is an optimum amount of water in sol for the formation of anatase by combining two effects on the concentration of Ti(OH)_4 in gels. Increasing in reaction temperature also benefit to the nucleation of anatase of TiO_2.展开更多
YAG:Ce3+ phosphor was prepared by sol-gel low-temperature combustion method. The effects of the precursor properties and calcining temperature on the crystallization process, microscopic morphology and luminescent pro...YAG:Ce3+ phosphor was prepared by sol-gel low-temperature combustion method. The effects of the precursor properties and calcining temperature on the crystallization process, microscopic morphology and luminescent properties of phosphor were studied. The results indicate that the pure phase of YAG can be obtained at 800 ℃ by sol-gel low temperature combustion method, using citric acid as complexing agent. When the molar ratio of metal ion to citric acid is 2.0 and pH value is 2, the crystallinity increases and the phosphor particle size grows up gradually with the increase of the calcining temperature. The powders were characterized through thermal analysis, X-ray diffraction analysis and scanning electron microscope analysis. The excitation spectra of YAG:Ce3+ phosphor take on a double peak structure, and the peak value of the main excitation spectra occurs at 460 nm and that of the emission spectra is near 530 nm. With the gradual increase of the calcining temperature, the peak position of excitation and emission spectra remains basically unchanged, but its relative intensity increases gradually.展开更多
Two series of perovskite-type oxides with composition (La_(1-x))Sr_xFeO_3(x≤0.8)and La_(1-x)Sr_xFe_(1-y)Co_yO_3(x=0.2; y=0.2, 0.4)powder productions were synthesized by EDTA complexing sol-gel method. The products we...Two series of perovskite-type oxides with composition (La_(1-x))Sr_xFeO_3(x≤0.8)and La_(1-x)Sr_xFe_(1-y)Co_yO_3(x=0.2; y=0.2, 0.4)powder productions were synthesized by EDTA complexing sol-gel method. The products were characterized by XRD, TEM, SEM, BET method(N_2 adsorption)and laser granularity analysis for different synthesis conditions to obtain the optimum conditions for the preparation process. Single-phased, uniform perovskite-type oxides with small particle size were obtained by EDTA sol-gel process with high stability and repeatability, and the process temperature is much lower than that of solid state reaction method.展开更多
Ni0.4Cu0.2Zn0.4Fe2O4 thin films were fabricated on Si substrates by using the sol-gel method and rapid thermal annealing （RTA）, and their magnetic properties and crystalline structures were investigated. The samples...Ni0.4Cu0.2Zn0.4Fe2O4 thin films were fabricated on Si substrates by using the sol-gel method and rapid thermal annealing （RTA）, and their magnetic properties and crystalline structures were investigated. The samples calcined at and above 600 ℃ have a single-phase spinel structure and the average grain size of the sample calcined at 600 ℃ is about 20 nm. The initial permeability μi, saturation magnetization M and coercivity H of the samples increase with the increasing calcination temperature. The sample calcined at 600 ℃ exhibits an excellent soft magnetic performance, which has μi=33.97 （10 MHz）, Hc=15.62 Oe and Ms=228.877 emu/cm^3. Low-temperature annealing can enhance the magnetic properties of the samples. The work shows that using the sol-gel method in conjunction with RTA is a promising way to fabricate integrated thin-film devices.展开更多
An aqueous sol-gel method for the synthesis of γ-Al2O3 supports has been developed for the use in tar reforming applications. It was determined the influences of two different aluminum precursors (aluminum sec-butoxi...An aqueous sol-gel method for the synthesis of γ-Al2O3 supports has been developed for the use in tar reforming applications. It was determined the influences of two different aluminum precursors (aluminum sec-butoxide (Al[OCH(CH3)CH2CH3]3) and aluminum nitrate (Al(NO3)3)) on the textural and crystallographic properties of Al2O3 supports. Only the formation of γ-Al2O3 is aimed in order to use these alumina materials as catalytic supports, because it presents high specific surface area and pore volume values. Additionally, the synthesis of γ-Al2O3 was realized with the use of a functionalized silicon precursor, [3-(2-aminoethylamino)propyl]trimethoxysilane, called EDAS. By the presence of an ethylenediamine group in this molecule, it is possible to chelate metallic ions and to highly increase their dispersion at a molecular level during the synthesis of metallic catalysts supported on alumina, which is an asset for catalytic applications. So it was developed a synthesis sol-gel procedure for the cogelation between the functionalized silicon alkoxide EDAS and alumina precursor. The alumina supports synthesized with Al(NO3)3 as precursor presented higher porous values than the ones obtained with aluminium sec-butoxide precursor. Since nitrate salts are much easier to handle than alkoxides, these observations allowed validating Al(NO3)3 as aluminum source for the future synthesis procedures for metallic catalysts supported on alumina.展开更多
文摘Hydroxyapatite/alumina nanocrystalline composite powders needed for various biomedical applications were successfully synthe- sized by sol-gel process. Structural and morphological investigations of the prepared composite powders were performed using X-ray dif- fractometer （XRD）, scanning electron microscopy （SEM）, X＇Pert HighScore software, and Clemex Vision image analysis software. The re- suits show that the crystallite size of the obtained composite powders is in the range of 25 to 90 nm. SEM evaluation shows that the obtained composite powders have a porous structure, which is very useful for biomedical applications. The spherical nanoparticles in the range of 60 to 800 nm are embedded in the agglomerated clusters of the prepared composite powders.
文摘Nanocrystalline rare earth mixed oxides DyFe x Co 1- x O 3- δ were prepared by sol gel method and characterized by X ray diffraction (XRD), thermogravimetric analysis (TG DTA) and scanning electron microscope (SEM). The results show that DyFe x Co 1- x O 3- δ has the structure of perovskite type at 800 ℃ for 2 h calcination. The conductivity of the materials at different temperature was measured by four probe instrumentation and two pole method. The results show that the conductivity of mixed oxides DyFe x Co 1- x O 3- δ is higher than those of un mixed oxides DyFeO 3 and DyCoO 3 and the conductivity is the best at x =0.8 in the matter of DyFe x Co 1- x O 3- δ . The conductivity of these materials always increases with the temperature rising and there is an apparent change between 600 and 800 ℃. However, the spinodals are different with different ration of Fe 3+ and Co 3+ . This kind of oxide is a conductive pottery material.
文摘The nanocrystalline TiO_2 powder were prepared by improved sol-gel method at low temperature under ambient pressure. The prepared TiO_2 powder was characterized by X-ray diffraction (XRD), transmission electron microscopy (TEM). It is found that the yield of anatase TiO_2 significantly increases with the reduction of pH by increasing the nucleation rate of anatase. There is an optimum amount of water in sol for the formation of anatase by combining two effects on the concentration of Ti(OH)_4 in gels. Increasing in reaction temperature also benefit to the nucleation of anatase of TiO_2.
文摘YAG:Ce3+ phosphor was prepared by sol-gel low-temperature combustion method. The effects of the precursor properties and calcining temperature on the crystallization process, microscopic morphology and luminescent properties of phosphor were studied. The results indicate that the pure phase of YAG can be obtained at 800 ℃ by sol-gel low temperature combustion method, using citric acid as complexing agent. When the molar ratio of metal ion to citric acid is 2.0 and pH value is 2, the crystallinity increases and the phosphor particle size grows up gradually with the increase of the calcining temperature. The powders were characterized through thermal analysis, X-ray diffraction analysis and scanning electron microscope analysis. The excitation spectra of YAG:Ce3+ phosphor take on a double peak structure, and the peak value of the main excitation spectra occurs at 460 nm and that of the emission spectra is near 530 nm. With the gradual increase of the calcining temperature, the peak position of excitation and emission spectra remains basically unchanged, but its relative intensity increases gradually.
文摘Two series of perovskite-type oxides with composition (La_(1-x))Sr_xFeO_3(x≤0.8)and La_(1-x)Sr_xFe_(1-y)Co_yO_3(x=0.2; y=0.2, 0.4)powder productions were synthesized by EDTA complexing sol-gel method. The products were characterized by XRD, TEM, SEM, BET method(N_2 adsorption)and laser granularity analysis for different synthesis conditions to obtain the optimum conditions for the preparation process. Single-phased, uniform perovskite-type oxides with small particle size were obtained by EDTA sol-gel process with high stability and repeatability, and the process temperature is much lower than that of solid state reaction method.
基金the National Natural Science Foundation of China (No. 90607021).
文摘Ni0.4Cu0.2Zn0.4Fe2O4 thin films were fabricated on Si substrates by using the sol-gel method and rapid thermal annealing （RTA）, and their magnetic properties and crystalline structures were investigated. The samples calcined at and above 600 ℃ have a single-phase spinel structure and the average grain size of the sample calcined at 600 ℃ is about 20 nm. The initial permeability μi, saturation magnetization M and coercivity H of the samples increase with the increasing calcination temperature. The sample calcined at 600 ℃ exhibits an excellent soft magnetic performance, which has μi=33.97 （10 MHz）, Hc=15.62 Oe and Ms=228.877 emu/cm^3. Low-temperature annealing can enhance the magnetic properties of the samples. The work shows that using the sol-gel method in conjunction with RTA is a promising way to fabricate integrated thin-film devices.
文摘An aqueous sol-gel method for the synthesis of γ-Al2O3 supports has been developed for the use in tar reforming applications. It was determined the influences of two different aluminum precursors (aluminum sec-butoxide (Al[OCH(CH3)CH2CH3]3) and aluminum nitrate (Al(NO3)3)) on the textural and crystallographic properties of Al2O3 supports. Only the formation of γ-Al2O3 is aimed in order to use these alumina materials as catalytic supports, because it presents high specific surface area and pore volume values. Additionally, the synthesis of γ-Al2O3 was realized with the use of a functionalized silicon precursor, [3-(2-aminoethylamino)propyl]trimethoxysilane, called EDAS. By the presence of an ethylenediamine group in this molecule, it is possible to chelate metallic ions and to highly increase their dispersion at a molecular level during the synthesis of metallic catalysts supported on alumina, which is an asset for catalytic applications. So it was developed a synthesis sol-gel procedure for the cogelation between the functionalized silicon alkoxide EDAS and alumina precursor. The alumina supports synthesized with Al(NO3)3 as precursor presented higher porous values than the ones obtained with aluminium sec-butoxide precursor. Since nitrate salts are much easier to handle than alkoxides, these observations allowed validating Al(NO3)3 as aluminum source for the future synthesis procedures for metallic catalysts supported on alumina.