This paper reports that a series of NiCuZn ferrite powders and films are prepared by using sol-gel method. The effects of raw material composition and the calcinate temperature on magnetic properties of them are inves...This paper reports that a series of NiCuZn ferrite powders and films are prepared by using sol-gel method. The effects of raw material composition and the calcinate temperature on magnetic properties of them are investigated. The NiCuZn ferrite powders are prepared by the self-propagating high-temperature synthesis method and subsequently heated at 700 ℃-1000 ℃. The results show that NiCuZn ferrite powders with single spinel phase can be formed after heat-treating at 750 ℃. Powders obtained from Ni0.4Cu0.2Zn0.4Fel.904 gel have better magnetic properties than those from gels with other composition. After heat-treating at 900 ℃for 3 h, coercivity Hc and saturation magnetization Ms are 9.70e （i Oe = 80 A/m） and 72.4 emu/g, respectively. Different from the powders, NiCuZn films produced on Si （100） from the Ni0.4Cuo.2Zno.4Fe204 gel formed at room temperature possess high properties. When heat-treating condition is around 600 ℃for 6 rain, samples with low Hc and high Ms will be obtained. The minimal Hc is 16.70e and Ms is about 300 emu/cm3. In comparison with the films prepared through long-time heat treating, the films prepared through short heat-treating time exhibits better soft magnetic properties.展开更多
基金supported by the National Natural Science Foundation of China (Grant No. 61003041)the Fundamental Research Funds for the Central Universities (Grant No. lzujbky-2010-81)
文摘This paper reports that a series of NiCuZn ferrite powders and films are prepared by using sol-gel method. The effects of raw material composition and the calcinate temperature on magnetic properties of them are investigated. The NiCuZn ferrite powders are prepared by the self-propagating high-temperature synthesis method and subsequently heated at 700 ℃-1000 ℃. The results show that NiCuZn ferrite powders with single spinel phase can be formed after heat-treating at 750 ℃. Powders obtained from Ni0.4Cu0.2Zn0.4Fel.904 gel have better magnetic properties than those from gels with other composition. After heat-treating at 900 ℃for 3 h, coercivity Hc and saturation magnetization Ms are 9.70e （i Oe = 80 A/m） and 72.4 emu/g, respectively. Different from the powders, NiCuZn films produced on Si （100） from the Ni0.4Cuo.2Zno.4Fe204 gel formed at room temperature possess high properties. When heat-treating condition is around 600 ℃for 6 rain, samples with low Hc and high Ms will be obtained. The minimal Hc is 16.70e and Ms is about 300 emu/cm3. In comparison with the films prepared through long-time heat treating, the films prepared through short heat-treating time exhibits better soft magnetic properties.