The microwave radiation method was introduced to prepare the Fe_2O_3/SO solid superacid.Its structure and properties were investigated by means of X-ray diffraction and infrared spectrum analyses as well as measuremen...The microwave radiation method was introduced to prepare the Fe_2O_3/SO solid superacid.Its structure and properties were investigated by means of X-ray diffraction and infrared spectrum analyses as well as measurement of magnetic susceptibility and rate of esterification. The structure of the superacids prepared in microwave field can be crystalline or non-crystalline, the latter has not been reported yet in literatures. Comparing with the traditional superacid, the non-crystalline Fe2O3/SO superacid prepared in microwave field has the highest magnetic susceptibility and catalytic activity. The di-coordination of Fe2O3 and SO and the S=O bi-bond were reinforced by microwave radiation, which is favorable for increasing the acid intensity of the Fe2O3/SO catalyst展开更多
Fe3O4 catalyst supported on spherical γ-Al2O3 was prepared with and without ultrasonic treatment during the impregnation step,and the heterogeneous catalytic oxidation of dimethoate wastewater was conducted with Fent...Fe3O4 catalyst supported on spherical γ-Al2O3 was prepared with and without ultrasonic treatment during the impregnation step,and the heterogeneous catalytic oxidation of dimethoate wastewater was conducted with Fenton reagent.Then,the physical and chemical properties of the catalysts were analyzed by means of XRD,ICP-AES and SEM,especially the effect of Fe3O4 dispersity on γ-Al2O3.The results showed that the activity of the supported catalysts prepared with ultrasonic treatment for dimethoate was higher than those without ultrasonic treatment and the corresponding degradation rate doubled those of the catalyst obtained by impregnation.The probable cause was that for catalysts prepared with ultrasonic treatment,Fe3O4 was well dispersed on the catalyst surface with small particle size,or existed in non-crystalline amorphous state,and Fe content on the catalyst surface was higher than those without ultrasonic treatment.展开更多
SO4^2- / TiO2-La2O3, a novel solid superacid, was prepared and its catalytic activities at different synthetic conditions are discussed with esterification of n-butanoic acid and n-butyl alcohol as probing reaction. T...SO4^2- / TiO2-La2O3, a novel solid superacid, was prepared and its catalytic activities at different synthetic conditions are discussed with esterification of n-butanoic acid and n-butyl alcohol as probing reaction. The optimum conditions have also been found, mole ratio of n（La^3＋）：n（Ti^4＋） is 1：34, the soaked consistency of H2SO4 is 0.8 tool/L, the soaked time of HESO4 is 24 h, the calcining temperature is 480 ℃, the calcining time is 3 h. Then it was applied in the catalytic synthesis often important ketals and acetals as catalyst and revealed high catalytic activity. Under these conditions on which the molar ratio of aldehyde/ketone to glycol is l： 1.5, the mass ratio of the catalyst used in the reactants is 0.5%, and the reaction time is 1.0 h, the yields of ketals and acetals can reach 41.4%-95.8%.展开更多
文摘The microwave radiation method was introduced to prepare the Fe_2O_3/SO solid superacid.Its structure and properties were investigated by means of X-ray diffraction and infrared spectrum analyses as well as measurement of magnetic susceptibility and rate of esterification. The structure of the superacids prepared in microwave field can be crystalline or non-crystalline, the latter has not been reported yet in literatures. Comparing with the traditional superacid, the non-crystalline Fe2O3/SO superacid prepared in microwave field has the highest magnetic susceptibility and catalytic activity. The di-coordination of Fe2O3 and SO and the S=O bi-bond were reinforced by microwave radiation, which is favorable for increasing the acid intensity of the Fe2O3/SO catalyst
文摘Fe3O4 catalyst supported on spherical γ-Al2O3 was prepared with and without ultrasonic treatment during the impregnation step,and the heterogeneous catalytic oxidation of dimethoate wastewater was conducted with Fenton reagent.Then,the physical and chemical properties of the catalysts were analyzed by means of XRD,ICP-AES and SEM,especially the effect of Fe3O4 dispersity on γ-Al2O3.The results showed that the activity of the supported catalysts prepared with ultrasonic treatment for dimethoate was higher than those without ultrasonic treatment and the corresponding degradation rate doubled those of the catalyst obtained by impregnation.The probable cause was that for catalysts prepared with ultrasonic treatment,Fe3O4 was well dispersed on the catalyst surface with small particle size,or existed in non-crystalline amorphous state,and Fe content on the catalyst surface was higher than those without ultrasonic treatment.
基金Project supported by the National Natural Science Foundation of China (No. 20471044), and the Natural Science Foundation of Hubei Province (No. 2005ABA053), China
文摘SO4^2- / TiO2-La2O3, a novel solid superacid, was prepared and its catalytic activities at different synthetic conditions are discussed with esterification of n-butanoic acid and n-butyl alcohol as probing reaction. The optimum conditions have also been found, mole ratio of n（La^3＋）：n（Ti^4＋） is 1：34, the soaked consistency of H2SO4 is 0.8 tool/L, the soaked time of HESO4 is 24 h, the calcining temperature is 480 ℃, the calcining time is 3 h. Then it was applied in the catalytic synthesis often important ketals and acetals as catalyst and revealed high catalytic activity. Under these conditions on which the molar ratio of aldehyde/ketone to glycol is l： 1.5, the mass ratio of the catalyst used in the reactants is 0.5%, and the reaction time is 1.0 h, the yields of ketals and acetals can reach 41.4%-95.8%.