The synthesis process for La 1- x Sr x Mn 1- y Co y O 3- δ ( x = 0.2, 0.3; y = 0.2, 0.8, designated as LSMC below) perovskite oxides prepared by solid state reaction was investigated using DSC/TG, XRD, EPMA and parti...The synthesis process for La 1- x Sr x Mn 1- y Co y O 3- δ ( x = 0.2, 0.3; y = 0.2, 0.8, designated as LSMC below) perovskite oxides prepared by solid state reaction was investigated using DSC/TG, XRD, EPMA and particle size analysis methods. It was found that LSMCs were all of single phase and the synthesis process might be divided into three stages: the decomposition of reactants, the formation of LaMn(Co)O 3 based oxides, and the formation of LSMC solid solution. Typical average and the peak value of particle size, and the specific surface area are 14.65?μm, 16.4?μm and 1.38?m 2/mL, respectively, for mixed reactants and are 23.81?μm, 32.11?μm and 0.5?m 2/mL, respectively, for powder synthesized at 1?200?℃ for 8?h in air.展开更多
文摘The synthesis process for La 1- x Sr x Mn 1- y Co y O 3- δ ( x = 0.2, 0.3; y = 0.2, 0.8, designated as LSMC below) perovskite oxides prepared by solid state reaction was investigated using DSC/TG, XRD, EPMA and particle size analysis methods. It was found that LSMCs were all of single phase and the synthesis process might be divided into three stages: the decomposition of reactants, the formation of LaMn(Co)O 3 based oxides, and the formation of LSMC solid solution. Typical average and the peak value of particle size, and the specific surface area are 14.65?μm, 16.4?μm and 1.38?m 2/mL, respectively, for mixed reactants and are 23.81?μm, 32.11?μm and 0.5?m 2/mL, respectively, for powder synthesized at 1?200?℃ for 8?h in air.