In this study,a single-doped phosphors yttrium aluminum garnet(Y_(3)Al_(5)O_(12),YAG):Ce^(3+),single-doped YAG:Sc^(3+),and double-doped phosphors YAG:Ce^(3+),Sc^(3+) were prepared by spark plasma sintering(SPS)(lower ...In this study,a single-doped phosphors yttrium aluminum garnet(Y_(3)Al_(5)O_(12),YAG):Ce^(3+),single-doped YAG:Sc^(3+),and double-doped phosphors YAG:Ce^(3+),Sc^(3+) were prepared by spark plasma sintering(SPS)(lower than 1 200℃).The characteristics of synthesized phosphors were determined using scanning electron microscopy(SEM),X-ray diffraction(XRD),and fluorescence spectroscopy.During SPS,the lattice structure of YAG was maintained by the added Ce^(3+) and Sc^(3+).The emission wavelength of YAG:Ce^(3+) prepared from SPS(425-700 nm) was wider compared to that of YAG:Ce^(3+) prepared from high-temperature solid-state reaction(HSSR)(500-700 nm).The incorporation of low-dose Sc^(3+) in YAG:Ce^(3+) moved the emission peak towards the short wavelength.展开更多
High-performance solid oxide fuel cell(SOFC) is in urgent need of high-quality electrolyte powders with high reactivity and chemical uniformity.Here,8 mol% Y_(2)O_(3) doped ZrO_(2)(YSZ) nano-powders were synthesized b...High-performance solid oxide fuel cell(SOFC) is in urgent need of high-quality electrolyte powders with high reactivity and chemical uniformity.Here,8 mol% Y_(2)O_(3) doped ZrO_(2)(YSZ) nano-powders were synthesized by an improved solid-state reaction method at ambient temperature,and were applied to the fabrication of SOFC electrolytes.YSZ nano-powders show average grain sizes of ^(2)0 nm and high dispersibility,which is comparable with or even better than some other chemical methods.Benefitting from their high reactivity,dense YSZ electrolytes(relative density of 97.9%) can be obtained at a relatively low sintering temperature of 1400℃.The optimized electrical conductivity reaches up to a high value of0.034 S/cm at 800 0C in air.The anode supported single cell with the construction of Ni-YSZ/YSZ/Sm_(0.2)Ce_(0.8)O_(2-δ)(SDC)/La_(0.6)Sr_(0.4)Co_(0.2)Fe_(0.8)O_(3-δ)(LSCF) exhibits the peak power density of 0.827 W/cm^(2) at800℃ while taking wet H_(2) as fuels and ambient air as oxidants.展开更多
The effect of sintering temperature on thermoelectric properties of CdO ceramics was investigated by solid-state reaction method within the temperature range of 700-1000℃.With the increase of sintering temperature,bo...The effect of sintering temperature on thermoelectric properties of CdO ceramics was investigated by solid-state reaction method within the temperature range of 700-1000℃.With the increase of sintering temperature,both the grain size and the carrier concentration of these samples increased,while the Seebeck coefficient decreased.The highest dimensionless figure of merit ZT,0.34,was obtained at 1023 K for the sample sintered at 800℃,suggesting the potential application of CdO ceramics in thermoelectric(TE)devices.展开更多
Sr- and Mg-doped lanthanum gallate powders with the composition of La0.55Sr0.15Ga0.85Mg0.15O2.85were synthesized by a glycine-nitrate combustion method. Powders prepared under different fuel combustion conditions were...Sr- and Mg-doped lanthanum gallate powders with the composition of La0.55Sr0.15Ga0.85Mg0.15O2.85were synthesized by a glycine-nitrate combustion method. Powders prepared under different fuel combustion conditions were investigated by XRD and TEM. The results show that, under slightly rich fuel condition, the product powders contain less impurity phases, and powders prepared by the glycine-nitrate combustion contain far less impurity phases and have smaller particle sizes than those prepared by solid-state reaction method or acrylamide polymerization technique.展开更多
基金Funded by the Primary Research and Development Plan of Jiangsu Province(No.BE2016175)。
文摘In this study,a single-doped phosphors yttrium aluminum garnet(Y_(3)Al_(5)O_(12),YAG):Ce^(3+),single-doped YAG:Sc^(3+),and double-doped phosphors YAG:Ce^(3+),Sc^(3+) were prepared by spark plasma sintering(SPS)(lower than 1 200℃).The characteristics of synthesized phosphors were determined using scanning electron microscopy(SEM),X-ray diffraction(XRD),and fluorescence spectroscopy.During SPS,the lattice structure of YAG was maintained by the added Ce^(3+) and Sc^(3+).The emission wavelength of YAG:Ce^(3+) prepared from SPS(425-700 nm) was wider compared to that of YAG:Ce^(3+) prepared from high-temperature solid-state reaction(HSSR)(500-700 nm).The incorporation of low-dose Sc^(3+) in YAG:Ce^(3+) moved the emission peak towards the short wavelength.
基金supported by the Natural Science Foundation of Shandong Province (ZR2020KE033,ZR2020ME051,ZR2019BEM013,ZR2021ME253)the Shandong Science and Technology Program (2021TSGC1122)+1 种基金the Shandong Postdoctoral Innovation Foundation (201903069)the Zibo Key Research and Development Project (2021SNPT0004,2021SNCG0076)。
文摘High-performance solid oxide fuel cell(SOFC) is in urgent need of high-quality electrolyte powders with high reactivity and chemical uniformity.Here,8 mol% Y_(2)O_(3) doped ZrO_(2)(YSZ) nano-powders were synthesized by an improved solid-state reaction method at ambient temperature,and were applied to the fabrication of SOFC electrolytes.YSZ nano-powders show average grain sizes of ^(2)0 nm and high dispersibility,which is comparable with or even better than some other chemical methods.Benefitting from their high reactivity,dense YSZ electrolytes(relative density of 97.9%) can be obtained at a relatively low sintering temperature of 1400℃.The optimized electrical conductivity reaches up to a high value of0.034 S/cm at 800 0C in air.The anode supported single cell with the construction of Ni-YSZ/YSZ/Sm_(0.2)Ce_(0.8)O_(2-δ)(SDC)/La_(0.6)Sr_(0.4)Co_(0.2)Fe_(0.8)O_(3-δ)(LSCF) exhibits the peak power density of 0.827 W/cm^(2) at800℃ while taking wet H_(2) as fuels and ambient air as oxidants.
基金supported by the Natural Science Foundation of Hebei Province,China(Grant No.A2014201176)the Science and Technology Research Projects of Colleges and Universities in Hebei Province,China(Grant No.ZD2014018).
文摘The effect of sintering temperature on thermoelectric properties of CdO ceramics was investigated by solid-state reaction method within the temperature range of 700-1000℃.With the increase of sintering temperature,both the grain size and the carrier concentration of these samples increased,while the Seebeck coefficient decreased.The highest dimensionless figure of merit ZT,0.34,was obtained at 1023 K for the sample sintered at 800℃,suggesting the potential application of CdO ceramics in thermoelectric(TE)devices.
文摘Sr- and Mg-doped lanthanum gallate powders with the composition of La0.55Sr0.15Ga0.85Mg0.15O2.85were synthesized by a glycine-nitrate combustion method. Powders prepared under different fuel combustion conditions were investigated by XRD and TEM. The results show that, under slightly rich fuel condition, the product powders contain less impurity phases, and powders prepared by the glycine-nitrate combustion contain far less impurity phases and have smaller particle sizes than those prepared by solid-state reaction method or acrylamide polymerization technique.