3D reconstruction and 2D observation were conducted to characterize the microstructure of the castings produced through high pressure die casting with different parameters.Our results indicate that shrinkage pores gen...3D reconstruction and 2D observation were conducted to characterize the microstructure of the castings produced through high pressure die casting with different parameters.Our results indicate that shrinkage pores generally co-existed with externally solidified crystals(ESCs).In specimen produced without fast slow shot speed,big net-shrinkage pores accompanied with ESCs were found in the center of the specimen.When the casting pressurization was introduced,the shrinkage pores gathered to the specimen center and became much less due to the optimization of melt feeding.Much more porosity was found near the gate rather than in the middle of the rod bar,especially gas pores.Thefilling process simulation reveals that the middle position of the bars wasfirstlyfilled and followed by the near gate position accompanied with one intense turbulentflow.展开更多
基金financially supported by the National Natural Science Foundation of China (No. 52175284)the State Key Lab of Advanced Metals and Materials (2021-ZD08)technical support of BL13W1 Beamline in Shanghai Synchrotron Radiation Facility (SSRF) and Gaomi Xiangyu company
文摘3D reconstruction and 2D observation were conducted to characterize the microstructure of the castings produced through high pressure die casting with different parameters.Our results indicate that shrinkage pores generally co-existed with externally solidified crystals(ESCs).In specimen produced without fast slow shot speed,big net-shrinkage pores accompanied with ESCs were found in the center of the specimen.When the casting pressurization was introduced,the shrinkage pores gathered to the specimen center and became much less due to the optimization of melt feeding.Much more porosity was found near the gate rather than in the middle of the rod bar,especially gas pores.Thefilling process simulation reveals that the middle position of the bars wasfirstlyfilled and followed by the near gate position accompanied with one intense turbulentflow.