The biaxially textured ion beam-assisted deposited(IBAD)-MgO templates were successfully prepared on polycrystalline Hastelloy metal substrate with reel-to-reel system for YB2Cu3O7-d(YBCO)-coated conductors.By the sol...The biaxially textured ion beam-assisted deposited(IBAD)-MgO templates were successfully prepared on polycrystalline Hastelloy metal substrate with reel-to-reel system for YB2Cu3O7-d(YBCO)-coated conductors.By the solution deposition planarization technique,amorphous Y2O3films were coated on untreated Hastelloy substrate as the bed layer to obtain smooth,dense,and crack-free surface for subsequent IBAD-MgO deposition.The 50 m long IBAD-MgO and homo-epitaxial(epi)-MgO buffer layers deposited on Y2O3films exhibit excellent crystallographic consistency along the scope with full width half maximum(FWHM)values of(110)DU and(200)Dx in the range of 5.5°–6.0°and3.0°–3.5°,respectively.To match the lattice constant of YBCO material,LaMnO3cap layer was fabricated on IBAD-MgO templates by radio frequency(rf)magnetron sputtering with the FWHM values of in-plane and out-ofplane of 6.8°and 3.7°,respectively,indicating excellent biaxial texture.展开更多
基金supported by the Sichuan Youth Science and Technology Innovation Research Team (No. 2011JTD0006)Fundamental Research Funds for the Central Universities (Nos. ZYGX2012J039 and ZYGX2011Z002)
文摘The biaxially textured ion beam-assisted deposited(IBAD)-MgO templates were successfully prepared on polycrystalline Hastelloy metal substrate with reel-to-reel system for YB2Cu3O7-d(YBCO)-coated conductors.By the solution deposition planarization technique,amorphous Y2O3films were coated on untreated Hastelloy substrate as the bed layer to obtain smooth,dense,and crack-free surface for subsequent IBAD-MgO deposition.The 50 m long IBAD-MgO and homo-epitaxial(epi)-MgO buffer layers deposited on Y2O3films exhibit excellent crystallographic consistency along the scope with full width half maximum(FWHM)values of(110)DU and(200)Dx in the range of 5.5°–6.0°and3.0°–3.5°,respectively.To match the lattice constant of YBCO material,LaMnO3cap layer was fabricated on IBAD-MgO templates by radio frequency(rf)magnetron sputtering with the FWHM values of in-plane and out-ofplane of 6.8°and 3.7°,respectively,indicating excellent biaxial texture.