The 0.96Na_(0.5)Bi_(0.5)TiO_(3)-0.04K_(0.5)Bi_(0.5)TiO_(3)(NKBT96/4)lead-free single crystal was successfullygrown by top-seeded solution growth method.The effective segregation coefficient for K was calculated to be ...The 0.96Na_(0.5)Bi_(0.5)TiO_(3)-0.04K_(0.5)Bi_(0.5)TiO_(3)(NKBT96/4)lead-free single crystal was successfullygrown by top-seeded solution growth method.The effective segregation coefficient for K was calculated to be 0.20.X-ray powder difraction measurement showed that the as-grown crystalpossesses rhombohedral perovskite structure at room temperature.X-ray rock curve measureindicated that the as-grown single crystal owned relatively higher quality.The NKBT96/4 singlecrystal exhibits apparent diffused dielectric behavior,where the diffusiveness index aαis 1.79 forthe[001]-oriented crystal planes.A notable thermal hysteresis,△T_(h),of 25℃was disclosed for thetetragonal antiferroelectric-tetragonal paraelectric phase transition in the dielectric propertystudies between heating and cooling.The highest remnant polarization,P_(r),16.8μC/cm^(2),wasobtained at 100℃.The electromechanical coupling coefficient k_(t)of the[001]-oriented crystalplanes at room temperat ure was determined to be 38%using resonance-antiresonance technique.The room temperature piezoelectric constant d_(33)reaches 120 pC/N.展开更多
In this paper,ferroelectric tetragonal tungsten bronze type potassium lithium niobate(KLN)crystal with a size of 20mm×8mm×43mm was grown from a melt with a composition of 32mol% K 2CO 3,24mol% Li 2CO 3 and 4...In this paper,ferroelectric tetragonal tungsten bronze type potassium lithium niobate(KLN)crystal with a size of 20mm×8mm×43mm was grown from a melt with a composition of 32mol% K 2CO 3,24mol% Li 2CO 3 and 44mol% Nb 2O 5 by the top seeded solution growth (TSSG)method.The KLN crystal as grown along [110]axis has a perfect crystal melt interface dominated by {110} and {210} facets.Lattice constants were measured by X ray diffraction (XRD) analysis performed on {001}and {110}natural faces of single crystal samples.The anisotropic thermal expansion behavior of the crystal was also studied along [001] and [110] axes,respectively by using a Shimadzu TMA 50 thermomechnical analyzer.For the purpose of crystal poling,the dependence of crystal capacitance vs.temperature in both heating and cooling cycles was measured and the ferroelectric Curie temperature was determined to be 514℃.The crystal was poled at 506℃ with a dc field of about 250 V/cm along the c axis of the sample,for a time corresponding to about 1.5 h/cm.The blue second harmonic generation (SHG)characteristics of the KLN crystal were investigated by using a 3900s Ti∶sapphire CW tunable laser.Blue laser light at wavelength 432nm was obtained by the non critical phase matching (NCPM)SHG at room temperature.Based on the wavelength and temperature tuning curves for the NCPM SHG,the wavelength acceptance and temperature acceptance of this KLN crystal were measured.The crystal property homogeneity along the <110>growth axis was also studied by measuring the room temperature NCPM wavelength at different growth positions.展开更多
基金the Ministry of Science and Technology of China through 973 Program(No.2009CB623305)National Key Technology R&D Program(No.2010BAK69B26)+3 种基金the Natural Science Foundation of China(Nos.60837003,50777065,61001041 and 11090332)Science and Technology Commission of Shanghai Municipality(Nos.10520712700,10JC1415900 and 10dz0583400)the Innovation Fund of Shanghai Institute of Ceramics(Nos.O99ZC4140G andO99ZC1110G)Shanghai Rising-Star Program(No.11QA1407500).
文摘The 0.96Na_(0.5)Bi_(0.5)TiO_(3)-0.04K_(0.5)Bi_(0.5)TiO_(3)(NKBT96/4)lead-free single crystal was successfullygrown by top-seeded solution growth method.The effective segregation coefficient for K was calculated to be 0.20.X-ray powder difraction measurement showed that the as-grown crystalpossesses rhombohedral perovskite structure at room temperature.X-ray rock curve measureindicated that the as-grown single crystal owned relatively higher quality.The NKBT96/4 singlecrystal exhibits apparent diffused dielectric behavior,where the diffusiveness index aαis 1.79 forthe[001]-oriented crystal planes.A notable thermal hysteresis,△T_(h),of 25℃was disclosed for thetetragonal antiferroelectric-tetragonal paraelectric phase transition in the dielectric propertystudies between heating and cooling.The highest remnant polarization,P_(r),16.8μC/cm^(2),wasobtained at 100℃.The electromechanical coupling coefficient k_(t)of the[001]-oriented crystalplanes at room temperat ure was determined to be 38%using resonance-antiresonance technique.The room temperature piezoelectric constant d_(33)reaches 120 pC/N.
文摘In this paper,ferroelectric tetragonal tungsten bronze type potassium lithium niobate(KLN)crystal with a size of 20mm×8mm×43mm was grown from a melt with a composition of 32mol% K 2CO 3,24mol% Li 2CO 3 and 44mol% Nb 2O 5 by the top seeded solution growth (TSSG)method.The KLN crystal as grown along [110]axis has a perfect crystal melt interface dominated by {110} and {210} facets.Lattice constants were measured by X ray diffraction (XRD) analysis performed on {001}and {110}natural faces of single crystal samples.The anisotropic thermal expansion behavior of the crystal was also studied along [001] and [110] axes,respectively by using a Shimadzu TMA 50 thermomechnical analyzer.For the purpose of crystal poling,the dependence of crystal capacitance vs.temperature in both heating and cooling cycles was measured and the ferroelectric Curie temperature was determined to be 514℃.The crystal was poled at 506℃ with a dc field of about 250 V/cm along the c axis of the sample,for a time corresponding to about 1.5 h/cm.The blue second harmonic generation (SHG)characteristics of the KLN crystal were investigated by using a 3900s Ti∶sapphire CW tunable laser.Blue laser light at wavelength 432nm was obtained by the non critical phase matching (NCPM)SHG at room temperature.Based on the wavelength and temperature tuning curves for the NCPM SHG,the wavelength acceptance and temperature acceptance of this KLN crystal were measured.The crystal property homogeneity along the <110>growth axis was also studied by measuring the room temperature NCPM wavelength at different growth positions.