A completely green pathway for the preparation of Ag nanoparticles was proposed, by using soy protein isolate （SPI） as stabilizer under UV irradiation and H2O as the environmentally benign solvent throughout the pre...A completely green pathway for the preparation of Ag nanoparticles was proposed, by using soy protein isolate （SPI） as stabilizer under UV irradiation and H2O as the environmentally benign solvent throughout the preparation. Transmission electronic microscopy （TEM） and zeta potential characterization results indicated that the Ag nanoparticles were stable and well dispersed with an average diameter about 13 nm, and X-ray diffraction （XRD） analysis of SPI/Ag composite nanoparticles confirmed the formation of metallic silver. UV-Vis spectrum showed that the Ag nanoparticles dispersion solution had the maximum absorbance at about 430 nm due to surface plasmon resonance of the Ag nanoparticles. Infrared spectroscopy confirmed that the polypeptide backbone of SPI was not cleaved during the conjugation process and that some active amino groups were oxidized. The SPI/Ag composite nanoparticles have excellent antibacterial activity against two representative bacteria, staphylococcus aureus （Gram positive） and escherichia coli （Gram negative） in the presence of SPI.展开更多
基金the National Natural Science Foundation of China(Nos.50673038 and 20374025)the Fundamental Research Funds for the Central Universities of China(No.JUSRP111A08)
文摘A completely green pathway for the preparation of Ag nanoparticles was proposed, by using soy protein isolate （SPI） as stabilizer under UV irradiation and H2O as the environmentally benign solvent throughout the preparation. Transmission electronic microscopy （TEM） and zeta potential characterization results indicated that the Ag nanoparticles were stable and well dispersed with an average diameter about 13 nm, and X-ray diffraction （XRD） analysis of SPI/Ag composite nanoparticles confirmed the formation of metallic silver. UV-Vis spectrum showed that the Ag nanoparticles dispersion solution had the maximum absorbance at about 430 nm due to surface plasmon resonance of the Ag nanoparticles. Infrared spectroscopy confirmed that the polypeptide backbone of SPI was not cleaved during the conjugation process and that some active amino groups were oxidized. The SPI/Ag composite nanoparticles have excellent antibacterial activity against two representative bacteria, staphylococcus aureus （Gram positive） and escherichia coli （Gram negative） in the presence of SPI.