Investigations were made both in laboratorial and industrial scales on formation of non-metallic inclusions with relatively lower melting temperatures to improve the fatigue property of the special steels which contai...Investigations were made both in laboratorial and industrial scales on formation of non-metallic inclusions with relatively lower melting temperatures to improve the fatigue property of the special steels which contained extra low oxygen.It was found in laboratory studies that steel/slag reaction time largely affected non-metallic inclusions in steel.With the slag/steel reaction time increasing from 30 to 90 min,inclusions of MgO-Al2O3 spinel were gradually changed into CaO-MgO-Al2O3 system inclusions which were surrounded by lower melting temperature softer CaO-Al2O3 surface layers.By using high basicity and as much as 41 mass% Al2O3 refining slag,the ratio of the lower melting temperature CaO-MgO-Al2O3 system inclusions was remarkably increased to above 80%.In the industrial experiments,it was found that the inclusions changed in the order of "Al2O3 →MgO-Al2O3 system→CaO-MgO-Al2O3 system" in the secondary refining,and the change from MgO-Al2O3 system to CaO-MgO-Al2O3 system took place from the outside to the inside.The diffusion of CaO and MgO inside the layer of CaO-MgO-Al2O3 was considered as the controlling step of the inclusion transfer.Through LF and RH refining,most inclusions could be transferred to lower melting temperature CaO-Al2O3 and CaO-MgO-Al2O3 system inclusions.展开更多
基金supported by the National Basic Research Program of China (Grant No. 2010CB630806)
文摘Investigations were made both in laboratorial and industrial scales on formation of non-metallic inclusions with relatively lower melting temperatures to improve the fatigue property of the special steels which contained extra low oxygen.It was found in laboratory studies that steel/slag reaction time largely affected non-metallic inclusions in steel.With the slag/steel reaction time increasing from 30 to 90 min,inclusions of MgO-Al2O3 spinel were gradually changed into CaO-MgO-Al2O3 system inclusions which were surrounded by lower melting temperature softer CaO-Al2O3 surface layers.By using high basicity and as much as 41 mass% Al2O3 refining slag,the ratio of the lower melting temperature CaO-MgO-Al2O3 system inclusions was remarkably increased to above 80%.In the industrial experiments,it was found that the inclusions changed in the order of "Al2O3 →MgO-Al2O3 system→CaO-MgO-Al2O3 system" in the secondary refining,and the change from MgO-Al2O3 system to CaO-MgO-Al2O3 system took place from the outside to the inside.The diffusion of CaO and MgO inside the layer of CaO-MgO-Al2O3 was considered as the controlling step of the inclusion transfer.Through LF and RH refining,most inclusions could be transferred to lower melting temperature CaO-Al2O3 and CaO-MgO-Al2O3 system inclusions.