This study has developed an efficient method to achieve excellent thermal dimensional stability and desired dimensions of hollow polyester fiber. Firstly,the influence of thermal treatment temperate( 140-180 ℃) on th...This study has developed an efficient method to achieve excellent thermal dimensional stability and desired dimensions of hollow polyester fiber. Firstly,the influence of thermal treatment temperate( 140-180 ℃) on the degree of shrinkage of fiber was investigated. The influence was also analyzed with a 2nd heating to simulate the application situation. It was discovered that the heat treatment at a temperature which was above the application temperature( 2nd heating) would efficiently remove the internal stress in the fiber and improve the thermal dimensional stability.Secondly,the impact of heat treatment temperature on the fiber diameter and the degree of hollowness were studied. The results implied that with a fixed fiber length, higher treatment temperature led to thinner fiber and a lower degree of hollowness.Last but not least,key parameters that could further influence the fiber dimensions were investigated. The results suggested that the fiber diameters and the degree of hollowness could be further controlled by tuning the drawing speed,the spinning meter pump output and cooling status while the spinneret parameters were fixed.展开更多
Using brighten white and modified PET chips, fine denier hollow fibres (dpf=0.5～1.5) were prepared on a Fuji Filter MSTC-400 and VC-443A drawn machine, whose structure and properties were tested by X-ray diffraction ...Using brighten white and modified PET chips, fine denier hollow fibres (dpf=0.5～1.5) were prepared on a Fuji Filter MSTC-400 and VC-443A drawn machine, whose structure and properties were tested by X-ray diffraction mater, SOM-II sonic velocity meter and Instron-1122 Tensile tester, electron and light microscopy etc,. The results show: fine denier hollow taken-up yarns prepared at low spinning velocity have radial orientation, higher strength and elongation at rupture because radial stress is higher than normal stress. Fine denier hollow drawn yarns with hollow degree up to 18～35％ and high tenacity, together with high crystalline degree and small crystal and amorphous domains, can be empolyed as products.展开更多
基金Innovation Fund Project of National Commercial Aircraft Manufacturing Engineering Research Center(No.SAM C14-JS-15-048)Natural Science Foundation of Shanghai,China(No.13ZR1400400)the Fundamental Research Funds for the Central Universities,China
文摘This study has developed an efficient method to achieve excellent thermal dimensional stability and desired dimensions of hollow polyester fiber. Firstly,the influence of thermal treatment temperate( 140-180 ℃) on the degree of shrinkage of fiber was investigated. The influence was also analyzed with a 2nd heating to simulate the application situation. It was discovered that the heat treatment at a temperature which was above the application temperature( 2nd heating) would efficiently remove the internal stress in the fiber and improve the thermal dimensional stability.Secondly,the impact of heat treatment temperature on the fiber diameter and the degree of hollowness were studied. The results implied that with a fixed fiber length, higher treatment temperature led to thinner fiber and a lower degree of hollowness.Last but not least,key parameters that could further influence the fiber dimensions were investigated. The results suggested that the fiber diameters and the degree of hollowness could be further controlled by tuning the drawing speed,the spinning meter pump output and cooling status while the spinneret parameters were fixed.
文摘Using brighten white and modified PET chips, fine denier hollow fibres (dpf=0.5～1.5) were prepared on a Fuji Filter MSTC-400 and VC-443A drawn machine, whose structure and properties were tested by X-ray diffraction mater, SOM-II sonic velocity meter and Instron-1122 Tensile tester, electron and light microscopy etc,. The results show: fine denier hollow taken-up yarns prepared at low spinning velocity have radial orientation, higher strength and elongation at rupture because radial stress is higher than normal stress. Fine denier hollow drawn yarns with hollow degree up to 18～35％ and high tenacity, together with high crystalline degree and small crystal and amorphous domains, can be empolyed as products.